Aluminum-based self-cooling material and process for high-voltage power supply at 180-250 degrees

A high-voltage power supply and self-cooling technology, applied in the field of alloys, can solve problems such as the inability to meet the heat dissipation requirements of the power supply, achieve obvious economic and social benefits, increase heat transfer performance, and simplify the smelting and processing process.

Inactive Publication Date: 2019-07-23
杭州辰卓科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing alloy materials for heat dissipation can no longer meet the heat dissipation requirements of the power supply after packaging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An aluminum-based self-cooling material and process for a high-voltage power supply at 180-250 degrees Celsius. In terms of weight percentage, the composition of the alloy is: Sc: 0.1wt.%, Ag: 2.0wt.%, Ni: 1.0wt.%, Ga: 0.2wt.%, Sb: 5.0wt.%, Cd: 2.0wt. %, In: 18.0wt.%, Sn: 30.0wt.%, the balance is Al.

[0019] The above-mentioned method for preparing and using an aluminum-based self-cooling material for a high-voltage power supply of 180-250 degrees includes the following steps: (a) batching: weighing raw materials according to the above ingredients; (b) smelting: using argon protection The non-vacuum induction melting furnace is used for smelting, and the crucible is graphite crucible; the alloy melt is fully stirred at 720 degrees for 10 minutes with electromagnetic stirring, and then iron molds are used for casting, and water cooling is used for rapid cooling (c) Extrusion at room temperature Compression: Carry out extrusion molding at room temperature, and the extru...

Embodiment 2

[0022] An aluminum-based self-cooling material and process for a high-voltage power supply at 180-250 degrees Celsius. In terms of weight percentage, the composition of the alloy is: Sc: 0.3wt.%, Ag: 4.0wt.%, Ni: 1.5wt.%, Ga: 0.5wt.%, Sb: 8.0wt.%, Cd: 3.0wt. %, In: 20.0wt.%, Sn: 32.0wt.%, the balance is Al.

[0023] The above-mentioned method for preparing and using an aluminum-based self-cooling material for a high-voltage power supply of 180-250 degrees includes the following steps: (a) batching: weighing raw materials according to the above ingredients; (b) smelting: using argon protection The non-vacuum induction melting furnace is used for melting, and the crucible is graphite crucible; heat preservation at 740 degrees for 10 minutes and use electromagnetic stirring to fully stir the alloy melt, then cast iron molds, and use water cooling for rapid cooling (c) Extrusion at room temperature Compression: Carry out extrusion molding at room temperature, and the extrusion st...

Embodiment 3

[0026] An aluminum-based self-cooling material and process for a high-voltage power supply at 180-250 degrees Celsius. In terms of weight percentage, the composition of the alloy is: Sc: 0.2wt.%, Ag: 2.5wt.%, Ni: 1.4wt.%, Ga: 0.3wt.%, Sb: 5.8wt.%, Cd: 2.5wt. %, In: 19.0wt.%, Sn: 30.0wt.%, the balance is Al.

[0027] The above-mentioned method for preparing and using an aluminum-based self-cooling material for a high-voltage power supply of 180-250 degrees includes the following steps: (a) batching: weighing raw materials according to the above ingredients; (b) smelting: using argon protection The non-vacuum induction melting furnace is used for melting, and the crucible is graphite crucible; heat preservation at 730 degrees for 10 minutes and use electromagnetic stirring to fully stir the alloy melt, then cast iron molds, and use water cooling for rapid cooling (c) Extrusion at room temperature Compression: Carry out extrusion molding at room temperature, and the extrusion st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum-based self-cooling material and process for a high-voltage power supply at 180-250 degrees. An alloy comprises the following components of, by weight percentage, 0.1-0.3 wt.% of Sc, 2.0-4.0 wt.% of Ag, 1.0-1.5 wt.% of Ni, 0.2-0.5 wt.% of Ga, 5.0-8.0 wt.% of Sb, 2.0-3.0 wt.% of Cd, 18.0-20.0 wt.% of In, 30.0-32.0 wt.% of Sn and the balance of Al. The aluminum-based self-cooling material and process is a novel heat dissipation solution for generating large heat flow in a high-voltage power supply in a short time, and can meet high-end heat dissipation needs inthe electronic industry field. It can be predicted that after industrialization, great economic value will be obtained, and technological development in related fields will also be promoted.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to an aluminum-indium alloy. Background technique [0002] When the power supply with an output voltage above 5,000 volts becomes a high-voltage power supply, and this type of power supply is generally a DC power supply. The output voltage of a general high-voltage power supply can reach tens of thousands of volts, or even hundreds of thousands of volts or higher. High-voltage power supplies have many uses, mainly including high-voltage power supplies for X-ray machines, high-voltage power supplies for lasers, high-voltage power supplies for spectral analysis, and high-voltage power supplies for non-destructive testing. [0003] High-voltage power supplies are generally in harsh working environments for many years, such as high temperature, high humidity, and high salt spray corrosive environments. Not only does it lead to corrosion damage to the circuit board, but also maintenance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C30/04C22F1/04C22F1/02
CPCC22C21/003C22C30/04C22F1/02C22F1/04
Inventor 刘亚军
Owner 杭州辰卓科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com