Anti-radiation fabric and preparation method thereof

A radiation protection and fabric technology, applied in protective clothing, apparel, clothing, etc., can solve the problems of non-degradable radiation protection fabrics, low radiation protection performance, poor hand feel, etc., and achieve good degradability, good bacteriostatic performance, softness and so on. Comfort-enhancing effect

Active Publication Date: 2019-08-02
SUZHOU BAIYUAN GENT CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems of non-degradable, hard material, poor hand feeling and low radiation protection performance in the prior art, and further provide a radiation protection fabric and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-radiation fabric and preparation method thereof
  • Anti-radiation fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment provides a radiation-proof fabric, including the following raw materials: 40 kg of recombinant spidroin fiber, 30 kg of chitin fiber, 12 kg of nano-silver fiber, and 15 kg of pullulan fiber.

[0047] The preparation method of described anti-radiation fabric, comprises the steps:

[0048] 1) Weaving recombined spidroin fibers, chitin fibers, nano-silver fibers and pullulan fibers into blended fabrics;

[0049] 2) Dip-dye the blended fabric prepared in step 1) in the radiation-proof liquid, the dip-dyeing temperature is 25°C, the dip-dye time is 150min, and the mass ratio of the blended fabric to the radiation-proof liquid is 1:4;

[0050] 3) Rinse the dyed fabric with water, dry it, and shape it to obtain a radiation-proof fabric.

[0051] The anti-radiation liquid is composed of the following materials in parts by weight: 10 kg of Folium Isatidis extract, 16 kg of Acanthopanax acanthopanax extract, 3 kg of malic acid, 8 kg of ethylene glycol stearate, a...

Embodiment 2

[0054] This embodiment provides a radiation-proof fabric, including the following raw materials: 50 kg of recombinant spidroin fiber, 20 kg of chitin fiber, 20 kg of nano-silver fiber, and 8 kg of pullulan fiber.

[0055] The preparation method of described anti-radiation fabric, comprises the steps:

[0056] 1) Weaving recombined spidroin fibers, chitin fibers, nano-silver fibers and pullulan fibers into blended fabrics;

[0057] 2) Dip-dye the blended fabric prepared in step 1) in the radiation-proof liquid, the dip-dyeing temperature is 40°C, the dip-dye time is 100min, and the mass ratio of the blended fabric to the radiation-proof liquid is 1:6;

[0058] 3) Rinse the dyed fabric with water, dry it, and shape it to obtain a radiation-proof fabric.

[0059] The anti-radiation liquid is composed of the following materials in parts by weight: 18 kg of Folium Isatidis extract, 10 kg of Acanthopanax acanthopanax extract, 8 kg of malic acid, 3 kg of ethylene glycol stearate, an...

Embodiment 3

[0062] This embodiment provides a radiation-proof fabric, including the following raw materials: 42 kg of recombinant spidroin fiber, 25 kg of chitin fiber, 12 kg of nano-silver fiber, and 10 kg of pullulan fiber.

[0063] The preparation method of described anti-radiation fabric, comprises the steps:

[0064] 1) Weaving recombined spidroin fibers, chitin fibers, nano-silver fibers and pullulan fibers into blended fabrics;

[0065] 2) Dip-dye the blended fabric prepared in step 1) in the radiation-proof liquid, the dip-dyeing temperature is 30°C, the dip-dye time is 120min, and the mass ratio of the blended fabric to the radiation-proof liquid is 1:5;

[0066] 3) Rinse the dyed fabric with water, dry it, and shape it to obtain a radiation-proof fabric.

[0067] The anti-radiation liquid is composed of the following materials in parts by weight: 12kg of Folium Isatidis extract, 14kg of Acanthopanax acanthopanax extract, 3kg of citric acid, 6kg of ethylene glycol stearate, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of textile material preparation, in particular to an anti-radiation fabric and a preparation method thereof. The invention provides an anti-radiation fabric, which is prepared from the following raw materials in parts by weight: 40 to 50 parts of recombinant spider silk protein fiber, 20-30 parts of chitosan fiber, 12-20 parts of nano-silver fibers, and 8-15 parts of aureobasidium pullulans polysaccharide fiber. The anti-radiation fabric provided by the invention has good anti-radiation performance, and meanwhile, the prepared fabric is good in air permeability, is washable, soft and comfortable, and has certain antibacterial performance.

Description

technical field [0001] The invention relates to the field of textile material preparation, in particular to a radiation-proof fabric and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, people are paying more and more attention to textiles with green environmental protection and health care functions. Modern clothing and household textiles are beginning to develop in the direction of health, environmental protection, fashion, and functionality. People's requirements for textiles are no longer limited to the original basic characteristics such as warmth and comfort, but instead focus on special functions such as health care and safety. For functional fabrics, anti-radiation fabrics are one of them. [0003] TVs, refrigerators, air conditioners, microwave ovens, computers, mobile phones, electronic instruments, medical equipment, etc. all around us can release a certain amount of electromagnetic radiatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41D31/04
Inventor 李春李琳车锐
Owner SUZHOU BAIYUAN GENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com