Novel antibacterial ceramic tea set and manufacturing method thereof

A technology of antibacterial ceramics and manufacturing methods, which is applied in the field of ceramic processing and can solve problems such as easy breeding of bacteria

Inactive Publication Date: 2019-08-02
福建省德化县盛鼎瓷艺有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Ceramic tea sets are mainly special utensils for brewing and drinking tea made of kaolin, purple sand mud and other raw materials, including ceramic teapots, ceramic covered bowls, ceramic teacups, ceramic tea trays, ceramic saucers, ceramic tea washers, etc., used in daily life The ceramic tea set has residual moisture after use, which is easy to breed bacteria. Therefore, we propose a new type of antibacterial ceramic tea set and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] S1. Grind diatomite to 200-300 mesh, clay to 400-500 mesh, calcium oxide to 200-300 mesh, aluminum oxide to 200-300 mesh, mix the components in proportion, then crush and ball mill The mud is pressed into porcelain mud by a mud press, and the mass ratio of the raw material formula is: 50% diatomite, 18% clay, 20% calcium oxide, and 12% aluminum oxide;

[0026] S2. Put the porcelain clay into the tea set mould, and use one of the methods of high pressure, rolling and grouting to make the porcelain clay into ceramic pots;

[0027] S3. Put the prepared ceramics into a kiln for firing for 5-8 hours at a firing temperature of 1100-1200° C., and trim and polish the fired samples;

[0028] S4. Attach a sterilizing material to the surface of the ceramic tea set, then enter the kiln, bake at a temperature of 200-300° C. for 30-50 minutes to obtain a finished ceramic tea set.

Embodiment 2

[0030] S1. Grind diatomite to 200-300 mesh, clay to 400-500 mesh, calcium oxide to 200-300 mesh, aluminum oxide to 200-300 mesh, mix the components in proportion, then crush and ball mill The mud is pressed into porcelain mud by a mud press, and the mass ratio of the raw material formula is: diatomite 44%, clay 20%, calcium oxide 22%, aluminum oxide 14%;

[0031] S2. Put the porcelain clay into the tea set mould, and use one of the methods of high pressure, rolling and grouting to make the porcelain clay into ceramic pots;

[0032] S3. Put the prepared ceramics into a kiln for firing for 5-8 hours at a firing temperature of 1100-1200° C., and trim and polish the fired samples;

[0033] S4. Attach a sterilizing material to the surface of the ceramic tea set, then enter the kiln, and bake at 200-300°C for 30-50 minutes to obtain a finished ceramic tea set. The sterilizing material is a nano-titanium dioxide silver ion solution.

Embodiment 3

[0035] S1. Grind diatomite to 200-300 mesh, clay to 400-500 mesh, calcium oxide to 200-300 mesh, aluminum oxide to 200-300 mesh, mix the components in proportion, then crush and ball mill The mud is pressed into porcelain mud by a mud press, and the mass ratio of the raw material formula is: diatomite 45%, clay 20%, calcium oxide 22%, aluminum oxide 13%;

[0036] S2. Put the porcelain clay into the tea set mould, and use one of the methods of high pressure, rolling and grouting to make the porcelain clay into ceramic pots;

[0037] S3. Put the prepared ceramics into a kiln for firing for 5-8 hours at a firing temperature of 1100-1200° C., and trim and polish the fired samples;

[0038] S4. Attach a sterilizing material to the surface of the ceramic tea set, then enter the kiln, and bake at 200-300°C for 30-50 minutes to obtain a finished ceramic tea set. The sterilizing material is a nano-titanium dioxide silver ion solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel antibacterial ceramic tea set and a manufacturing method thereof. The manufacturing method comprises the following steps: S1, grinding diatomaceous earth into 200-300 meshes, grinding clay into 400-500 meshes, grinding calcium oxide in 200-300 meshes, grinding alumina into 200-300 meshes, proportioning the components at a ratio, then crushing and ball-milling into mud, and pressing the mud into a ceramic mud by a mud pressing machine; S2, putting the porcelain mud in a tea mold for forming, and preparing the ceramic mud into ceramic green bodies by adopting oneof the methods such as high pressure, rolling depression and grouting; S3, putting the manufactured ceramic green bodies into a kiln and firing for 5-8 hours with the firing temperature being 1100-1200 DEG C, and trimming and polishing the fired samples; S4, attaching a sterilizing material to the surface of the ceramic tea set, then putting in the kiln, and firing at 200-300 DEG C for 30-50 minutes to obtain a finished ceramic tea set. The novel antibacterial ceramic tea set is simple in principle and convenient to produce, and solves the problems of bacterial breeding, off-odor, moldiness and other potential safety hazards caused by water accumulation, decay, dampness and excess residual moisture of the ceramic tea set with high-efficiency antibacterial capacity and super water absorption function.

Description

technical field [0001] The invention relates to the technical field of ceramic processing, in particular to a novel antibacterial ceramic tea set and a production method. Background technique [0002] Ceramics are various products made of natural clay and various natural minerals as the main raw materials through crushing, kneading, molding and calcination. In the past, people called ceramics made of clay and fired at high temperature in special kilns. Ceramics is the general term for pottery and porcelain. The traditional concept of ceramics refers to all artificial industrial products that use inorganic non-metallic minerals such as clay as raw materials. [0003] Ceramic tea sets are mainly special utensils for brewing and drinking tea made of raw materials such as kaolin and purple sand mud, including ceramic teapots, ceramic covered bowls, ceramic teacups, ceramic tea trays, ceramic saucers, ceramic tea washers, etc., used in daily life The ceramic tea set has residua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/622C04B41/87A47G19/14A47G19/22
CPCA47G19/14A47G19/2205C04B35/14C04B35/622C04B41/5041C04B41/87C04B2235/3208C04B2235/3217C04B2235/349C04B2235/656C04B2235/96C04B41/4535C04B41/0072
Inventor 苏伟盛
Owner 福建省德化县盛鼎瓷艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More