Method and device for preparing carbon-coated copper nanoparticles by wire electric explosion method

A technology of copper nanoparticles and nanoparticles, applied in metal processing equipment, nanotechnology for materials and surface science, nanotechnology, etc., can solve the problems of complex production equipment, high energy, and many impurities in the product, and achieve production The effect of simple process, less by-products, and easy collection

Active Publication Date: 2020-07-28
XI AN JIAOTONG UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of these methods require complex production equipment, require high energy, and the products have many impurities or are dangerous, so they are greatly limited in practical application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for preparing carbon-coated copper nanoparticles by wire electric explosion method
  • Method and device for preparing carbon-coated copper nanoparticles by wire electric explosion method
  • Method and device for preparing carbon-coated copper nanoparticles by wire electric explosion method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] In order to enable those skilled in the art to better understand the solutions of the present invention, the following will clearly and completely describe the technical solutions in the embodiments of the present invention in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments are only The embodiments are a part of the present invention, not all embodiments, and are not intended to limit the scope of the present invention. Also, in the following description, descriptions of well-known structures and techniques are omitted to avoid unnecessarily obscuring the concepts disclosed in the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts shall fall within the protection scope of the present invention.

[0027] Various structural schematic diagrams according to the disclosed embodiments of the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method and a device for preparing carbon-coated copper nanoparticles by using a metal wire electric explosion method. A copper wire with a certain length and diameter is evenly wound on a carbon rod, and the metal wire is passed through in an argon atmosphere. High voltage and high current make the wire explode electrically, and the carbon-coated copper nanoparticles can be collected. The copper wire undergoes phase transformation during heating during the electric explosion, and undergoes melting, gasification, plasma and other processes successively, and produces copper atoms under the high temperature heating of the plasma, and a part of carbon atoms will also be formed after the carbon rod is passed through a high current. , and then the two spontaneously and uniformly nucleate and condense into atomic clusters from the gas phase, forming an initial small droplet, which grows continuously, and then forms a carbon coating layer through two mechanisms of internal carbon atom precipitation and external carbon atom deposition, and finally passes through Cooling forms carbon-coated copper nanoparticles. This method proposes a new method for preparing carbon-coated copper nanoparticles, which has great application value for industrial production and scientific research.

Description

【Technical field】 [0001] The invention belongs to the technical field of preparation of carbon-coated copper nanoparticles, and relates to a method and a device for preparing carbon-coated copper nanoparticles by using a wire electric explosion method. 【Background technique】 [0002] Metal nanoparticles have many advantages. However, due to their high energy content, they can easily react with gases and liquids in the environment or form clusters, which loses the advantages of nanoparticles. Therefore, after the carbon coating is introduced, the multi-layer graphite will be tightly coated on the periphery of the nano-metal particles, and the nano-metal is at the core position, that is, a new type of nano-carbon / metal composite material is formed through this shell / core structure, which can protect the metal nanoparticles. In addition to the original characteristics, endowed with unique electrical, optical, and magnetic properties, it has great application value in high-densi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/14B22F1/02B82Y30/00B82Y40/00
CPCB22F9/14B82Y30/00B82Y40/00B22F1/16
Inventor 吴坚李旭东石桓通刘超鹏陈立李兴文
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products