High-gloss colorful pearlescent PET master batch and preparation method thereof

A technology of magic color and master batch, applied in the field of master batch and its preparation, can solve the problems of complicated processing technology, large addition amount of pearl powder and high cost, and achieve the effects of simple production process, environmental protection function and wide application.

Inactive Publication Date: 2019-08-23
广东一龙新材料科技有限公司
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the problems of large amount of pearlescent powder added, high cost, cumbersome manufacturing process and subsequent use in masterbatch, which limit the application of pearlescent effect in more matrix materials, the present invention provides a high-gloss illusion Pearlescent PET masterbatch and preparation method thereof, under the premise of completely not adding pearlescent powder, polyethylene terephthalate PET is used as base material, and polyethylene terephthalate PET and polymethyl methacrylate are used The characteristics of incompatibility and different fluidity of PMMA create a "mirror surface" at the interface between crystalline PET and amorphous PMMA, forming a planar pearl-like luster

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-gloss colorful pearlescent PET master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The high-gloss and magic pearlescent PET masterbatch of this embodiment has the following components by weight: 84 parts of PET, 9 parts of PMMA, 6 parts of Pigment Blue 60, 0.6 part of SR-100, and 0.4 part of stearic acid.

[0029] The preparation method of the soft non-woven masterbatch of this embodiment is as follows: firstly weigh the raw materials with the above-mentioned weight ratio; Mix uniformly; then put the uniformly mixed raw materials into a co-rotating twin-screw extruder for blending, extrusion, traction, and pelletize to obtain the primary product of the masterbatch. The screw diameter of the co-rotating twin-screw extruder is D=62mm, Length-to-diameter ratio L / D=48, main engine speed is 490Hz, screw barrel temperature control settings are as follows: Zone 1 200°C, Zone 2 220°C, Zone 3-11 240°C, die head temperature 250°C, pelletizing method is water cooling Cut into pellets; finally, dry the primary masterbatch for 12 hours at a relative humidity of 45...

Embodiment 2

[0032] The high-gloss and illusion pearlescent PET masterbatch of this embodiment has the following components by weight: 85 parts of PET, 9 parts of PMMA, 3 parts of Pigment Yellow 128, 1.8 parts of FSX803, and 0.2 parts of oleic acid amide.

[0033] The preparation method of the soft non-woven masterbatch of this embodiment is as follows: firstly weigh the raw materials with the above-mentioned weight ratio; Mix uniformly; then put the uniformly mixed raw materials into a co-rotating twin-screw extruder for blending, extrusion, traction, and pelletize to obtain the primary product of the masterbatch. The screw diameter of the co-rotating twin-screw extruder is D=62mm, Length-to-diameter ratio L / D=48, main engine speed is 490Hz, screw barrel temperature control settings are as follows: Zone 1 200°C, Zone 2 220°C, Zone 3-11 240°C, die head temperature 250°C, pelletizing method is water cooling Cut into pellets; finally, dry the primary masterbatch for 12 hours at a relative hu...

Embodiment 3

[0036] The high-gloss and magic pearlescent PET master batch of this embodiment has the following components by weight: 83 parts of PET, 8 parts of PMMA, 6 parts of pigment red 10, 2.5 parts of AST-50, and 0.5 part of oleic acid amide.

[0037] The preparation method of the soft non-woven masterbatch of this embodiment is as follows: firstly weigh the raw materials with the above-mentioned weight ratio; Mix uniformly; then put the uniformly mixed raw materials into a co-rotating twin-screw extruder for blending, extrusion, traction, and pelletize to obtain the primary product of the masterbatch. The screw diameter of the co-rotating twin-screw extruder is D=62mm, Length-to-diameter ratio L / D=48, main engine speed is 490Hz, screw barrel temperature control settings are as follows: Zone 1 200°C, Zone 2 220°C, Zone 3-11 240°C, die head temperature 250°C, pelletizing method is water cooling Cut into pellets; finally, dry the primary masterbatch for 12 hours at a relative humidity ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
aspect ratioaaaaaaaaaa
glossaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-gloss colorful pearlescent PET master batch. The high-gloss colorful pearlescent PET master batch comprises, by weight, 75-85 parts of PET, 8-15 parts of PMMA, 3-8 partsof a toner, 0.2-3 parts of a scraping resistant agent and 0.1-0.5 part of a lubricant. A preparation method of the high-gloss colorful pearlescent PET master batch comprises the following steps: rawmaterials are weighed according to above weight part proportions, are added into a high-speed mixer, and are uniformly stirred, the obtained mixture is added into a homodromous double screw extruder,and is blended, extruded and drawn, the obtained mixture is pelletized to obtain a preliminary master batch, and the preliminary master batch is dried to obtain the finished master batch. Compared with the prior art, the preparation method prepares the high-gloss colorful pearlescent PET master batch with a face pearl-like gloss without adding pearl powder; and he pearlescent master batch has theadvantages of good dispersibility and tinting strength, dust-free and environmentally-friendly processing and using process, simple manufacturing technology, low production cost and wide uses.

Description

technical field [0001] The invention relates to a masterbatch and a preparation method thereof, in particular to a high-gloss illusion pearlescent PET masterbatch and a preparation method thereof. Background technique [0002] Pearlescent powder is a kind of toner. In the production process of toner, the final process is generally made into finished products through filtration, drying, and crushing. However, when the toner is exposed to high temperature during the drying process, it is easy to reunite the pigment molecules. Thereby causing problems such as not easy to disperse, quality decline and complicated processing technology in subsequent use. [0003] Pearlescent effect is due to TiO 2 Or other metal oxides are coated on the substrate, and the light is reflected by multiple parallels to form a pearly luster. In order to achieve a good pearlescent effect, the amount of pearlescent powder added is large, about 20-40%, and the surface of the pearlescent powder is a met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L33/12C08J3/22B29B9/06B29C48/40B29C48/92B29C48/625
CPCB29B9/06B29C48/40B29C48/625B29C48/92C08J3/226C08J2433/12C08J2467/02
Inventor 王瑞明王瑞芳吴飞鹏
Owner 广东一龙新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com