Steel fastener material double-layer protection method using surface blackening and organic coating
An organic coating, surface blackening technology, applied in metal material coating process, device for coating liquid on the surface, coating, etc. Excellent performance, the effect of solving poor corrosion resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1:
[0024] First, prepare the sample, degrease the fasteners made of steel in an alkaline degreasing solution, then wash them with a lot of water, then derust them in an acid derusting solution, wash and dry them with a lot of water.
[0025] The degreasing liquid is a mixture of sodium hydroxide, sodium carbonate, trisodium phosphate, sodium silicate, and OP-10 emulsifier. The content of each component is as follows:
[0026] Sodium hydroxide 10g / L; sodium carbonate 20g / L; trisodium phosphate 50g / L; sodium silicate 5g / L; OP-10 emulsifier 0.2g / L; the rest is water.
[0027] The rust remover is made by mixing hydrochloric acid and nitric acid, and the content of each component is as follows:
[0028] Hydrochloric acid 5g / L; nitric acid 15g / L.
[0029] Then, soak the fastener in the blackening liquid for 2 hours, the composition of the blackening liquid is as follows:
[0030] Copper sulfate 10g / L; nickel sulfate 5g / L; zinc dihydrogen phosphate 4g / L; phosphoric acid 3g / L; co...
Example Embodiment
[0036] Example 2:
[0037] First, prepare the sample, degrease the fasteners made of steel in an alkaline degreasing solution, then wash them with a lot of water, then derust them in an acid derusting solution, wash and dry them with a lot of water.
[0038] The degreasing liquid is a mixture of sodium hydroxide, sodium carbonate, trisodium phosphate, sodium silicate, and OP-10 emulsifier. The content of each component is as follows: sodium hydroxide 10g / L; sodium carbonate 50g / L; triphosphate Sodium 60g / L; sodium silicate 7g / L; OP-10 emulsifier 3g / L; the rest is water.
[0039] The rust removal solution is made by mixing hydrochloric acid and nitric acid, and the content of each component is as follows: hydrochloric acid 10g / L; nitric acid 10g / L.
[0040] Then, the fastener was immersed in the blackening liquid for 1.5 hours. The composition of the blackening liquid was as follows: copper sulfate 15g / L; nickel sulfate 4g / L; zinc dihydrogen phosphate 3g / L; phosphoric acid 2g / L; comple...
Example Embodiment
[0046] Example 3:
[0047] First, prepare the sample, degrease the fasteners made of steel in an alkaline degreasing solution, then wash them with a lot of water, then derust them in an acid derusting solution, wash and dry them with a lot of water.
[0048] The degreasing liquid is a mixture of sodium hydroxide, sodium carbonate, trisodium phosphate, sodium silicate, and OP-10 emulsifier. The content of each component is as follows: sodium hydroxide 10g / L; sodium carbonate 50g / L; triphosphate Sodium 60g / L; sodium silicate 7g / L; OP-10 emulsifier 3g / L; the rest is water.
[0049] The rust removal solution is made by mixing hydrochloric acid and nitric acid, and the content of each component is as follows: hydrochloric acid 10g / L; nitric acid 10g / L.
[0050] Then, the fastener was immersed in the blackening liquid for 3 hours. The composition of the blackening liquid was as follows: copper sulfate 14g / L; nickel sulfate 4g / L; zinc dihydrogen phosphate 4g / L; phosphoric acid 3g / L; complexi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap