Preparation method of antibacterial polyester fiber
A technology of polyester fiber and polyester, which is applied in the field of chemical fiber processing, can solve the problems of reduced antibacterial performance and easy shedding of nano-silver, and achieve the effects of reducing agglomeration, reliable design principles, and good product quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1:
[0029] The preparation method of the antibacterial polyester fiber involved in this embodiment includes the following steps:
[0030] (1) mix and stir 1-5 minutes with sodium dodecylbenzenesulfonate powder and silver powder, reduce the electrostatic force between silver powder, prevent the occurrence of silver powder agglomeration phenomenon, the silver powder particle size used is 1-10 microns, The weight ratio of sodium dodecylbenzene sulfonate powder and silver powder is 0.5:100;
[0031] (2) adding the mixed silver powder to the ethanolic solution of 5% ethyl orthosilicate and stirring rapidly, dripping the NaOH aqueous solution with a molar concentration of 1.0 mol / L to make the solution pH value greater than 7, The reaction time is 0.5 hour, and the reaction product is filtered and dried to obtain the silver powder coated with silica;
[0032] (3) place the silica-coated silver powder in the reactor, add N-methylpyrrolidone, disperse under ultrasoni...
Example Embodiment
[0038] Example 2:
[0039] The preparation method of the antibacterial polyester fiber involved in this embodiment includes the following steps:
[0040] (1) mix and stir 1-5 minutes with sodium dodecylbenzene sulfonate powder and silver powder, reduce the electrostatic force between silver powder, prevent the occurrence of silver powder agglomeration phenomenon, the silver powder particle size used is 10-15 microns, The weight ratio of sodium dodecylbenzenesulfonate powder and silver powder is 2:100;
[0041] (2) adding the mixed silver powder to the ethanolic solution of 5% ethyl orthosilicate and stirring rapidly, dripping the NaOH aqueous solution with a molar concentration of 1.0 mol / L to make the solution pH value greater than 7, The reaction time is 0.5 hour, and the reaction product is filtered and dried to obtain the silver powder coated with silica;
[0042] (3) place the silica-coated silver powder in the reactor, add N-methylpyrrolidone, disperse under ultrasonic...
Example Embodiment
[0048] Example 3:
[0049] The preparation method of the antibacterial polyester fiber involved in this embodiment includes the following steps:
[0050] (1) mix and stir 1-5 minutes with sodium dodecylbenzene sulfonate powder and silver powder, reduce the electrostatic force between silver powder, prevent the occurrence of silver powder agglomeration phenomenon, the silver powder particle size used is 10-15 microns, The weight ratio of sodium dodecylbenzenesulfonate powder and silver powder is 1:100;
[0051] (2) adding the mixed silver powder to the ethanolic solution of 5% ethyl orthosilicate and stirring rapidly, dripping the NaOH aqueous solution with a molar concentration of 1.0 mol / L to make the solution pH value greater than 7, The reaction time was 2 hours, and the reaction product was filtered and dried to obtain silica-coated silver powder;
[0052] (3) place the silver powder coated with silica in the reactor, add N-methylpyrrolidone, disperse under ultrasonic co...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Intrinsic viscosity | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap