High-strength composite plastic and preparation method thereof

A composite plastic and high-strength technology, applied in the field of plastics, can solve problems such as low strength and limitations, and achieve the effects of long service life, high strength, and cheap raw materials

Inactive Publication Date: 2019-09-24
TIANJIN CHUANHAO PLASTICS
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength of plastic products includes impact resistance and tensile capacity, but the application of unmodified plastic products is limited due to their low strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high-strength composite plastic, the components are composed of 120 parts by mass of polyethylene, 20 parts of glass fiber, 12 parts of carbon fiber, 18 parts of silicon dioxide, 1 part of toughening agent, 3 parts of stearic acid, polyethylene 22 parts of glycol, 4 parts of polyvinyl alcohol fiber, 5 parts of styrene-butadiene rubber, 10 parts of pigment and filler, 4 parts of coupling agent, 2 parts of dispersant, 3 parts of stabilizer, 1 part of plasticizer, and 5 parts of antioxidant.

[0022] The pigment and filler is light calcium carbonate.

[0023] The coupling agent is a silane coupling agent.

[0024] The dispersant is monoglyceride stearate.

[0025] The stabilizer is epoxy resin.

[0026] The plasticizer is dioctyl phthalate.

[0027] The antioxidant is naphthylamine.

[0028] A preparation method of high-strength composite plastics is carried out according to the following steps:

[0029] (1) Polyethylene, glass fiber, carbon fiber, silica, toughener...

Embodiment 2

[0033] A high-strength composite plastic, the components are as follows: 140 parts of polyethylene, 15 parts of glass fiber, 15 parts of carbon fiber, 15 parts of silicon dioxide, 5 parts of toughening agent, 2 parts of stearic acid, polyethylene 25 parts of glycol, 3 parts of polyvinyl alcohol fiber, 7 parts of styrene-butadiene rubber, 7 parts of pigment and filler, 3 parts of coupling agent, 3 parts of dispersant, 3 parts of stabilizer, 3 parts of plasticizer, and 3 parts of antioxidant.

[0034] The pigment and filler is light calcium carbonate.

[0035] The coupling agent is a silane coupling agent.

[0036] The dispersant is monoglyceride stearate.

[0037] The stabilizer is epoxy resin.

[0038] The plasticizer is dioctyl phthalate.

[0039] The antioxidant is naphthylamine.

[0040] A preparation method of high-strength composite plastics is carried out according to the following steps:

[0041] (1) Polyethylene, glass fiber, carbon fiber, silica, toughener, stear...

Embodiment 3

[0045] A high-strength composite plastic, the components are as follows: 160 parts of polyethylene, 10 parts of glass fiber, 20 parts of carbon fiber, 10 parts of silicon dioxide, 10 parts of toughening agent, 1 part of stearic acid, polyethylene 30 parts of glycol, 5 parts of polyvinyl alcohol fiber, 10 parts of styrene-butadiene rubber, 5 parts of pigment and filler, 5 parts of coupling agent, 1 part of dispersant, 5 parts of stabilizer, 5 parts of plasticizer, and 1 part of antioxidant.

[0046] The pigment and filler is light calcium carbonate.

[0047] The coupling agent is a silane coupling agent.

[0048] The dispersant is monoglyceride stearate.

[0049] The stabilizer is epoxy resin.

[0050] The plasticizer is dioctyl phthalate.

[0051] The antioxidant is naphthylamine.

[0052] A preparation method of high-strength composite plastics is carried out according to the following steps:

[0053] (1) Polyethylene, glass fiber, carbon fiber, silica, toughener, steari...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of plastics, and especially relates to a high-strength composite plastic. The composite plastic comprises, by mass, 120-160 parts of polyethylene, 10-20 parts of glass fibers, 10-20 parts of carbon fibers, 10-20 parts of silica, 1-10 parts of a toughening agent, 1-3 parts of stearic acid, 20-30 parts of polyethylene glycol, 1-5 parts of polyvinyl alcohol fibers, 5-10 parts of styrene-butadiene rubber, 5-10 parts of a pigment and filler, 1-5 parts of a coupling agent, 1-5 parts of a dispersant, 1-5 parts of a stabilizer, 1-5 parts of a plasticizer and 1-5 parts of an antioxidant. A preparation method of the composite plastic is characterized in that all above materials are mixed, and then are granulated by a granulator. The plastic prepared by the above formula of the invention has a very high strength, greatly improved impact resistance and greatly improved tensile strength, and can be widely applied to plastic products in various fields.

Description

technical field [0001] The invention belongs to the field of plastics, in particular to a high-strength composite plastic and a preparation method thereof. Background technique [0002] As plastic products are more and more widely used in daily production and life, people have higher and higher performance requirements for plastic products. Compared with other materials, plastic products have the advantages of lightness, good corrosion resistance, and low price. In some special environments, plastic products are required to have higher strength. The strength of plastic products includes impact resistance and tensile capacity, but the application of unmodified plastic products is limited due to their low strength. Therefore, it is necessary to improve the existing technology and develop a new type of high-strength plastic. Contents of the invention [0003] Aiming at the above technical problems, the present invention provides a high-strength composite plastic and a prepa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L71/02C08L9/06C08L29/04C08K13/04C08K7/14C08K7/06C08K3/36C08K5/09
CPCC08L23/06C08L2205/035C08L2205/16C08L71/02C08L9/06C08L29/04C08K13/04C08K7/14C08K7/06C08K3/36C08K5/09
Inventor 侯增海
Owner TIANJIN CHUANHAO PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com