Ultra-wide economical duplex stainless steel medium plate and manufacturing method thereof

A duplex stainless steel, energy-saving technology, applied in the direction of improving process efficiency, can solve the problems of not considering the influence of stainless steel surface, not considering the continuous casting process and on-line heat treatment process and the quality of the steel plate, so as to reduce surface scratches and pressure Pit, reduced manufacturing cost, beneficial to the effect of coordinated deformation

Active Publication Date: 2019-11-15
ANGANG STEEL CO LTD
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method does not consider optimizing the steelmaking, continuous casting process and on-line heat treatment process to improve the quality of the continuous steel plate, and does not consider the impact of grinding and spraying on the surface of the stainless steel on the surface quality of the plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-wide economical duplex stainless steel medium plate and manufacturing method thereof
  • Ultra-wide economical duplex stainless steel medium plate and manufacturing method thereof
  • Ultra-wide economical duplex stainless steel medium plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The following examples are used to specifically illustrate the contents of the present invention, and these examples are only general descriptions of the contents of the present invention, and do not limit the contents of the present invention.

[0025] Wherein Table 1 is the chemical composition of embodiment steel, and Table 2 is the smelting process system of embodiment steel, and Table 3 is the processing method of embodiment steel slab; Table 4 is the rolling method of embodiment steel; Table 5 is embodiment The reduction rate of each pass of the steel; Table 6 is the pre-correction and laminar cooling process of the steel of the embodiment; Table 7 is the performance of the stainless steel of the embodiment.

[0026] The chemical composition (wt, %) of the embodiment of the present invention of table 1

[0027] Example C Si Mo mn Cr Ni N B Ca V als 1 0.026 0.57 0.51 4.3 19.2 1.27 0.23 0.0026 0.0011 0.041 0.023 2 0.023 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ultra-wide economical duplex stainless steel medium plate and a manufacturing method thereof. The medium axial crystal proportion of a continuous casting billet is not lowerthan 80%; the surface roughness Ra of the casting billet is smaller than or equal to 50 [mu]m, and high-temperature antioxidant coating is sprayed; the preheating section temperature of the casting billet is 960-1100 DEG C, the heating section temperature is 1150-1230 DEG C, and the soaking section temperature is 1220-1250 DEG C; the rough rolling starting temperature is larger than or equal to 1150 DEG C, the first pass reduction amount is larger than or equal to 25%, the subsequent pass reduction amount is smaller than or equal to 20%, the roller speed is 40-70 r / min, and the thickness of an intermediate blank is 60-120 mm; the finish rolling start temperature is larger than or equal to 1050 DEG C, the finish rolling temperature is larger than or equal to 950 DEG C, the rolling reduction rate is smaller than or equal to 20%, product specifications are 2800-4000 mm wide and 20-60 mm thick, and the surface crack rejection rate is decreased from above 10% to below 1.5%. The product iswidely applied to the engineering fields of nuclear power, oil and gas, shipbuilding, papermaking, seawater desalination and the like.

Description

technical field [0001] The invention relates to the technical field of duplex stainless steel plate rolling, in particular to an ultra-wide and economical duplex stainless steel plate and a manufacturing method thereof. Background technique [0002] With the rapid development of domestic shipbuilding, chemical industry, nuclear power, shipbuilding industry and other industries in recent years, the demand for low-cost duplex stainless steel plates with high strength and excellent corrosion resistance is increasing day by day. , Higher toughness, no room temperature brittleness, good intergranular corrosion resistance and welding performance, so it is widely used in the fields of petroleum, chemical industry and nuclear power. Due to the poor thermoplasticity of economical duplex stainless steel, hot forming is restricting its ability A key factor for successful production. At present, there is an increasing demand for wide and large-size economical stainless steel hot-rolled...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/06C22C38/44C22C38/46C22C38/54C22C38/58B22D11/115C21D8/02C22C33/04
CPCB22D11/115C21D8/0205C21D8/0226C21D8/0263C21D8/0278C21D8/0284C21D2211/001C21D2211/005C22C33/04C22C38/001C22C38/02C22C38/06C22C38/44C22C38/46C22C38/54C22C38/58Y02P10/20
Inventor 徐海健沙孝春韩楚菲隋松言刘文华王文仲石锋涛
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com