Easy-to-clean ceramic product for daily use and preparation method thereof

An easy-to-clean technology for ceramic products, applied in the field of ceramic products, can solve the problems of rough surface of daily-use ceramic products, easy entry of fluorine into the human body, and low hardness of daily-use ceramics, so as to benefit human health, improve quality stability, The effect of good wear resistance

Inactive Publication Date: 2019-11-22
福建省德化县紫嘉工艺有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. The surface of daily-use ceramic products is rough, not smooth and flat enough, which makes it easy to stain and difficult to clean;
[0006] 2. Daily-use ceramic products have low hardness and are not wear-resistant. They are

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-to-clean ceramic product for daily use and preparation method thereof
  • Easy-to-clean ceramic product for daily use and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] An easy-to-clean ceramic product for daily use, comprising a body and a surface glaze layer; the surface glaze layer covers the surface of the body with a thickness of about 1-2 mm;

[0035] The surface glaze layer is made of the following raw materials in parts by weight: 300-370 parts of anorthite, 45-58 parts of diatomite, 30-35 parts of purple gold clay, 34-40 parts of kaolin, 42-52 parts of bentonite, quartz 27-36 parts of sand, 15-18 parts of nano-zinc oxide, 55-68 parts of nano-silicon carbide, 32-38 parts of nano-silicon, 11-14 parts of partial graphene oxide, and 4-6 parts of rare earth.

[0036] Preferably, the green body is made of the following raw materials in parts by weight: 200-250 parts of albite, 100-140 parts of anorthite, 24-32 parts of marble, 17-24 parts of talcum powder, and 27-33 parts of barium oxide. 90-105 parts of kaolin, 45-55 parts of diatomite, and 9-12 parts of quartz sand.

[0037] Preferably, the surface glaze layer is made of the foll...

Embodiment 2

[0049] An easy-to-clean ceramic product for daily use, comprising a body and a surface glaze layer; the surface glaze layer covers the surface of the body with a thickness of about 1mm;

[0050] The surface glaze layer is made of the following raw materials in parts by weight: 300 parts of anorthite, 45 parts of diatomite, 30 parts of purple gold clay, 34 parts of kaolin, 42 parts of bentonite, 27 parts of quartz sand, 15 parts of nano zinc oxide, 55 parts of nano-silicon carbide, 32 parts of nano-silicon, 11 parts of partially oxidized graphene, and 4 parts of rare earth.

[0051] In this embodiment, the green body is made of the following raw materials in parts by weight: 200 parts of albite, 100 parts of anorthite, 24 parts of marble, 17 parts of talcum powder, 27 parts of barium oxide, 90 parts of kaolin, silicon 45 parts of algae earth, 9 parts of quartz sand.

[0052] In this embodiment, the rare earth is lanthanum cerium rare earth.

[0053] In this embodiment, the ka...

Embodiment 3

[0062] An easy-to-clean ceramic product for daily use, comprising a body and a surface glaze layer; the surface glaze layer covers the surface of the body with a thickness of about 2 mm;

[0063] The surface glaze layer is made of the following raw materials in parts by weight: 370 parts of anorthite, 58 parts of diatomite, 35 parts of purple gold clay, 40 parts of kaolin, 52 parts of bentonite, 36 parts of quartz sand, 18 parts of nano zinc oxide, 68 parts of nano-silicon carbide, 38 parts of nano-silicon, 14 parts of partially oxidized graphene, and 6 parts of rare earth.

[0064] In this embodiment, the green body is made of the following raw materials in parts by weight: 250 parts of albite, 140 parts of anorthite, 32 parts of marble, 24 parts of talcum powder, 33 parts of barium oxide, 105 parts of kaolin, silicon 55 parts of algae, 12 parts of quartz sand.

[0065] In this embodiment, the rare earth is lanthanum cerium rare earth.

[0066] In this embodiment, the kaoli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface roughness valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses an easy-to-clean ceramic product for daily use. The ceramic product comprises a green body and a surface glaze layer, the surface glaze layer covers the surface of the green body, and the thickness of the surface glaze layer is about 1-2 mm; the surface glaze layer is prepared from the following raw materials in parts by weight; 300 to 370 parts of anorthite, 45 to 58 partsof diatomite, 30 to 35 parts of purple gold soil, 34 to 40 parts of kaolin, 42 to 52 parts of bentonite, 27 to 36 parts of quartz sand, 15 to 18 parts of nano zinc oxide, 55 to 68 parts of nano silicon carbide, 32 to 38 parts of nano silicon, 11 to 14 parts of partial graphene oxide and 4 to 6 parts of rare earth. The surface roughness value of the easy-to-clean domestic ceramic product reaches 4.31 nm (rm s), and the easy-to-clean domestic ceramic product is very smooth and flat in surface, not prone to contamination and easy to clean; wear resistance is excellent, scratching is not prone tohappening in the using process, contamination is not prone to happening, and cleaning is easy; fluorine-containing compounds or components are not added, so that no fluorine element enters the humanbody in the use process, and the health of the human body is facilitated.

Description

technical field [0001] The invention relates to the field of ceramic products, in particular to an easy-to-clean daily-use ceramic product and a preparation method thereof. Background technique [0002] Ceramic products are one of the most common utensils in people's daily life. The development history of ceramics is an important part of the history of Chinese civilization. Among them, the invention and development of ceramics have unique significance. With the development of modern science and technology, modern In the past century, many new ceramic varieties have appeared. They no longer use or rarely use traditional ceramic materials such as clay, feldspar, and quartz, but use other special materials, and even expand to the range of non-silicate and non-oxide. , and many new processes have appeared, making ceramics have various special functions. [0003] The production of daily-use ceramics can be said to be due to people's needs for daily life. In daily life, people ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B35/19C04B41/86
CPCC03C8/00C04B35/19C04B41/009C04B41/5022C04B41/86C04B2235/3481C04B2235/3208C04B2235/349C04B2235/3215C04B2235/3418
Inventor 苏银珽
Owner 福建省德化县紫嘉工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap