Single-component polyurethane adhesive and preparation method thereof

A polyurethane adhesive, one-component technology, applied in the direction of polyurea/polyurethane adhesives, adhesives, adhesive types, etc., can solve the problems of yellowing resistance, no toughness, poor UV resistance, etc., and prolong the service life. , to meet the water resistance, improve the effect of bond strength

Inactive Publication Date: 2019-11-22
无锡庄周新材料科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a single-component polyurethane glue and its preparation method, which solves the problem that the adhesive stone co

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component polyurethane adhesive and preparation method thereof
  • Single-component polyurethane adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] S1. Put 13 parts of hydroxy silicone oil, 15 parts of polycarbonate diol and 35 parts of trifunctional polyether polyol into the reaction stick, stir and heat up to 105°C, keep it warm and vacuum for 55 minutes, and then reduce the temperature to 57 after the moisture is less than 0.025% ℃, then add 7 parts of chain extender and stir evenly;

[0032] S2. After stirring uniformly, add 0.0225 parts of catalyst. The above catalyst is added in 3 times with an interval of 4 minutes each time. At the same time, the reaction temperature is controlled and the temperature is controlled at 55°C;

[0033] S3. Slowly add 45 parts of HDI monomer dropwise to the reaction kettle, control the temperature at 65℃ and react for 45 minutes, then increase the temperature to 75℃ and react for 45 minutes, and finally increase the temperature to between 85℃ After reacting for 45 minutes, after all the HDI monomer is added dropwise, control the temperature at 83°C and keep it warm ...

Example Embodiment

[0036] Example 2

[0037] S1. Put 10 parts of hydroxy silicone oil, 10 parts of polycarbonate diol and 30 parts of trifunctional polyether polyol into the reaction stick, stir and raise the temperature to 100°C, keep it warm and vacuum for 50 minutes, and then lower the temperature to 55 after the moisture is less than 0.02% ℃, then add 5 parts of chain extender and stir evenly;

[0038] S2. After stirring evenly, add 0.015 parts of catalyst. The above catalyst is added in 3 times with an interval of 3 minutes each time. At the same time, the reaction temperature is controlled and the temperature is controlled at 50°C;

[0039] S3. Slowly add 40 parts of HDI monomer dropwise to the reaction kettle, and control the temperature at 60°C for 45 minutes. After all the HDI monomer is added dropwise, the temperature is raised to 70°C for 45 minutes. Finally, the temperature is raised to 80°C and reacted for 45 minutes, the temperature is controlled between 80°C, and the temperature is kept...

Example Embodiment

[0042] Example 3

[0043] S1. Put 15 parts of hydroxy silicone oil, 20 parts of polycarbonate diol and 40 parts of trifunctional polyether polyol into the reaction stick, stir and heat up to 110°C, keep it warm and vacuum for 60 minutes, and then cool down to 60 minutes after the moisture is less than 0.03% ℃, then add 10 parts of chain extender and stir evenly;

[0044] S2. After stirring evenly, add 0.03 parts of the catalyst. The above catalyst is added in 3 times with an interval of 5 minutes each time. At the same time, the reaction temperature is controlled and the temperature is controlled at 60°C;

[0045] S3. Add 50 parts of HDI monomer slowly and dropwise into the reaction kettle, control the temperature at 70℃ for 45 minutes, then increase the temperature to 80℃ for 45 minutes, and finally increase the temperature to between 90℃ After reacting for 45 minutes, after all the HDI monomers are added dropwise, the temperature is controlled between 83-85°C and kept for three ho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a single-component polyurethane adhesive and a preparation method thereof. The raw materials comprise the following components in parts by weight: 40 to 50 parts of HDI monomers, 10 to 15 parts of hydroxyl-terminated silicone oil, 10 to 20 parts of polycarbonate diol, 30 to 40 parts of trifunctional polyether polyol, 5 to 10 parts of chain extender and 0.015 to 0.03 part ofcatalyst. The trifunctional polyether polyol is a reaction product of polyol and polyisocyanate, the polyol contains trifunctional polyether polyol with more than one ethyleneoxy group in one molecule and the number average molecular weight of more than 3000, and the invention relates to the technical field of preparation of polyurethane adhesives. According to the invention, in specific practical application, the adhesive strength between glue and stones can be improved, outdoor water resistance, weather resistance, ultraviolet resistance, yellowing resistance and aging resistance are met, the service life of the water-permeable adhesive stone is prolonged, and by means of low viscosity of hydroxyl silicone oil, the polyurethane adhesive is solvent-free, more environmentally friendly inuse and capable of meeting the requirements of time development.

Description

technical field [0001] The invention relates to the technical field of preparing polyurethane adhesives, in particular to a single-component polyurethane adhesive and a preparation method. Background technique [0002] Polyurethane glue is a glue containing urethane and isocyanate groups in the molecular chain. Due to the strong polar isocyanate and urethane groups, it has high reactivity and can be cured at room temperature, so it is suitable for metal, rubber, glass, ceramics, etc. , plastic, wood, fabric, leather and other materials have excellent adhesive properties. The main chain of polyurethane is very flexible. Its biggest feature is that it can withstand shock, vibration and bending fatigue, and has high peel strength, especially low temperature resistance. It is extremely excellent and ranks first among the existing glues. The polyurethane glue has a simple process and can be cured at room temperature and heating. When different materials are glued, the effect of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/66C08G18/61C08G18/44C08G18/48C08G18/32C09J175/08
CPCC08G18/3206C08G18/4018C08G18/44C08G18/4829C08G18/61C08G18/6607C09J175/08
Inventor 张志平
Owner 无锡庄周新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap