A kind of flame-retardant antifouling synthetic leather and preparation method thereof

A synthetic leather and anti-fouling technology, applied in the field of synthetic leather, can solve the problems of anti-fouling agent complex composition, long time, poor wear resistance, scratch resistance, etc., achieve high promotion and application value, improve production efficiency, and reduce production cost effect

Active Publication Date: 2022-01-18
TIANMING DRESS WUHAN CITY
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the popular synthetic leather on the market is polyurethane synthetic leather. This kind of material has very good properties such as wear resistance and scratch resistance. However, its weather resistance, flame resistance and antifouling properties are very poor, which limits its application in some industries. widely used
Synthetic leather made of silica gel is another common type of synthetic leather. This material has the characteristics of environmental protection, non-hydrolysis, non-yellowing, and excellent weather resistance, but its wear resistance and scratch resistance are poor.
[0004] Chinese patent CN201610726984.0 proposes the method of modifying silicone polyurethane resin to produce synthetic leather. The synthetic leather has good biocompatibility of silicone, and also overcomes the problems of poor water resistance, antifouling and flame retardancy of polyurethane , but the transfer film and the impregnated cloth-based lamination in this invention need to be cured for 24-36 hours, and the time is too long, which affects production efficiency
The composition of the antifouling agent is complex, the price is high, and the performance stability needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A preparation method of flame-retardant antifouling synthetic leather, comprising the steps of:

[0035] Step S1, configuring slurry: fluorine-containing phenyltriazine-based silicone-modified polyurethane, butanone, natural capsaicin, 1-trifluoromethylvinylboronic acid, azobisisobutyronitrile, and surface-modified attapulgite clay Stir evenly according to the proportion to form a slurry; the proportion is as follows: 90 parts of fluorine-containing phenyltriazine-based organosilicon-modified polyurethane, 30 parts of butanone, 10 parts of natural capsaicin, and 8 parts of 1-trifluoromethylvinylboronic acid , 0.5 parts of azobisisobutyronitrile, 6 parts of surface-modified attapulgite clay;

[0036] Step S2, finishing: coating the slurry prepared in step S1 on the surface of polyurethane synthetic leather; the coating amount of the slurry is 60g / m 2 ;

[0037] Step S3, curing, drying and molding: drying the synthetic leather after finishing in step S2 at 115° C. for 4...

Embodiment 2

[0044] A preparation method of flame-retardant antifouling synthetic leather, comprising the steps of:

[0045] Step S1, configuring slurry: fluorine-containing phenyltriazine-based silicone-modified polyurethane, butanone, natural capsaicin, 1-trifluoromethylvinylboronic acid, azobisisoheptanonitrile, and surface-modified attapulgite clay Stir evenly according to the proportion to form a slurry; the proportions are as follows: 93 parts of fluorine-containing phenyltriazine-based organosilicon-modified polyurethane, 35 parts of butanone, 12 parts of natural capsaicin, and 9 parts of 1-trifluoromethylvinylboronic acid , 0.6 parts of azobisisoheptanonitrile, 7 parts of surface-modified attapulgite clay;

[0046] Step S2, finishing: coating the slurry prepared in step S1 on the surface of the silica gel synthetic leather; the coating amount of the slurry is 70g / m 2 ;

[0047] Step S3, curing, drying and molding: drying the synthetic leather after finishing in step S2 at 120° C....

Embodiment 3

[0054] A preparation method of flame-retardant antifouling synthetic leather, comprising the steps of:

[0055] Step S1, configuring slurry: fluorine-containing phenyltriazine-based silicone-modified polyurethane, butanone, natural capsaicin, 1-trifluoromethylvinylboronic acid, azobisisobutyronitrile, and surface-modified attapulgite clay Stir evenly according to the proportion to form a slurry; the proportion is as follows: 95 parts of fluorine-containing phenyltriazine-based organosilicon-modified polyurethane, 40 parts of butanone, 13 parts of natural capsaicin, and 10 parts of 1-trifluoromethylvinylboronic acid , 0.65 parts of azobisisobutyronitrile, 8 parts of surface-modified attapulgite clay;

[0056] Step S2, finishing: coating the slurry prepared in step S1 on the surface of polyurethane synthetic leather; the coating amount of the slurry is 90g / m 2 ;

[0057] Step S3, curing, drying and molding: drying the synthetic leather after finishing in step S2 at 125° C. for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing flame-retardant and antifouling synthetic leather, comprising the following steps: step S1, configuring slurry, step S2, finishing, step S3, curing, drying and molding; the slurry includes the following parts by weight: Raw materials: 90-100 parts of fluorine-containing phenyltriazine-based silicone-modified polyurethane, 30-50 parts of methyl ethyl ketone, 10-15 parts of natural capsaicin, 8-12 parts of 1-trifluoromethylvinyl boronic acid, trigger 0.5-0.8 parts of agent, 6-10 parts of surface modified attapulgite clay. The invention also discloses the flame retardant and antifouling synthetic leather prepared according to the preparation method of the flame retardant and antifouling synthetic leather. The flame-retardant and anti-fouling synthetic leather disclosed by the invention has excellent flame-retardant, anti-fouling, wear-resistant and scratch-resistant properties, and has good safety in use.

Description

technical field [0001] The invention relates to the technical field of synthetic leather, in particular to a flame-retardant antifouling synthetic leather and a preparation method thereof. Background technique [0002] In recent years, with the development of the economy and the improvement of living standards, people's demand for improving the quality of life is becoming more and more urgent, and the demand for high-quality daily products is also increasing. As a common daily product, leather products naturally have great market potential. However, with the enhancement of animal protection awareness, animal leather can no longer meet people's needs. As a substitute material for leather, synthetic leather products have entered the market. People's lives are widely used in the production of clothing, bags and footwear. [0003] Synthetic leather is a plastic product that simulates the composition and structure of natural leather and can be used as its substitute material. It...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/00D06N3/14
CPCD06N3/0061D06N3/0063D06N3/147D06N3/0059D06N2209/067D06N2209/146D06N2209/1685D06N2211/28
Inventor 朱建余李良全
Owner TIANMING DRESS WUHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products