High-temperature-resistant flame-retardant powder paint and production method thereof

A flame-retardant powder and powder coating technology, applied in powder coatings, fire-resistant coatings, epoxy resin coatings, etc., can solve the problems of easy ignition and combustion, no flame retardancy, personal safety threats, etc., to achieve excellent thermal oxidation Stability and electrical insulation, excellent heat resistance and UV resistance, effect of improving heat resistance

Inactive Publication Date: 2020-01-03
广西南宁维一防腐科技有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, high molecular polymers such as the main raw material resin of powder coatings generally have poor flame retardancy, and their applications in many fields are limited.
At present, most powder coatings on the market do not have flame retardant properties or have poor flame retardant effects. In case of fire, they are easy to be ignited and support combustion, which poses a threat to personal safety.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant flame-retardant powder paint and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A high-temperature-resistant flame-retardant powder coating, prepared from the following raw materials in parts by weight: 30 parts of silicone resin, 30 parts of epoxy resin, 3.4 parts of modified dicyandiamide, 0.2 parts of dimethylimidazole, and 10 parts of silicon micropowder 10 parts, 10 parts of mica powder, 0.3 parts of sanding agent, 30 parts of flame retardant, 1.2 parts of carbon black.

[0037] The silicone resin was purchased from Guangzhou Rongda Chemical Co., Ltd.

[0038] The epoxy resin is bisphenol A type epoxy resin.

[0039] The modified dicyandiamide is furfural modified dicyandiamide.

[0040] The dimethylimidazole was purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0041] The microsilica powder was purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0042] The mica powder is superfine muscovite powder, purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0043] The sand texture a...

Embodiment 2

[0054] A high-temperature-resistant flame-retardant powder coating prepared from the following raw materials in parts by weight: 45 parts of silicone resin, 45 parts of epoxy resin, 5.1 parts of modified dicyandiamide, 0.3 parts of dimethylimidazole, and 15 parts of silicon micropowder parts, 15 parts of mica powder, 0.4 parts of sanding agent, 45 parts of flame retardant, and 1.8 parts of carbon black.

[0055] The silicone resin was purchased from Guangzhou Rongda Chemical Co., Ltd.

[0056] The epoxy resin is a mixture of bisphenol A type epoxy resin and novolak epoxy resin.

[0057] The modified dicyandiamide is furfural modified dicyandiamide.

[0058] The dimethylimidazole was purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0059] The microsilica powder was purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0060] The mica powder is superfine muscovite powder, purchased from Guangzhou Shengqi Polymer Material Technology C...

Embodiment 3

[0072] A high-temperature-resistant flame-retardant powder coating prepared from the following raw materials in parts by weight: 60 parts of silicone resin, 60 parts of epoxy resin, 6.8 parts of modified dicyandiamide, 0.4 part of dimethylimidazole, and 20 parts of silicon micropowder 20 parts, 20 parts of mica powder, 0.6 parts of sanding agent, 60 parts of flame retardant, 2.4 parts of carbon black.

[0073] The silicone resin was purchased from Guangzhou Rongda Chemical Co., Ltd.

[0074] The epoxy resin is novolac epoxy resin.

[0075] The modified dicyandiamide is furfural modified dicyandiamide.

[0076] The dimethylimidazole was purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0077] The microsilica powder was purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0078] The mica powder is superfine muscovite powder, purchased from Guangzhou Shengqi Polymer Material Technology Co., Ltd.

[0079] The sand texture agent was pu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-temperature-resistant flame-retardant powder paint and a production method thereof. The powder paint is produced from the following raw materials in parts by weight: 30-60parts of organic silicon resin, 30-60 parts of epoxy resin, 3.4-6.8 parts of modified dicyandiamide, 0.2-0.4 part of dimethylimidazole, 10-20 parts of silica powder, 10-20 parts of mica powder, 0.3-0.6 part of a sand textured agent, 30-60 parts of a flame retardant and 1.2-2.4 parts of carbon black. A film, which is formed after the produced powder paint is subjected to spraying and curing, has excellent high-temperature-resistant performance, fireproof performance and flame-retardant performance in the premise that the mechanical performance, including the levelling performance and the anti-impact performance, of the film is not affected; and according to the powder paint, the production method is simple, and industrial production can be conducted.

Description

technical field [0001] The invention relates to the technical field of powder coatings, in particular to a high-temperature-resistant flame-retardant powder coating and a preparation method thereof. Background technique [0002] Powder coating refers to a new type of solvent-free 100% solid powder coating, which is made by mixing, crushing and sieving film-forming resins, additives, pigments, fillers, etc. The coating construction requires electrostatic spraying and baking film forming. It is completely different from ordinary solvent-based paints and water-based paints. It exists in the state of fine powder, and its dispersion medium is not solvent and water, but air. It has the characteristics of no solvent, no pollution, recyclable, environmental protection, saving energy and resources, reducing labor intensity and high mechanical strength of the coating film. [0003] Flame retardant powder coatings have the functions of flame retardant, flame retardant, and heat insul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D163/00C09D5/03C09D5/18C09D5/25C09D7/61
CPCC08K2003/323C08L2201/02C08L2201/08C09D5/00C09D5/033C09D5/18C09D163/00C09D183/04C08L63/00C08K3/36C08K3/34C08K5/02C08K5/521C08K3/32C08K13/02C08L83/04
Inventor 李金庆
Owner 广西南宁维一防腐科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap