Polypropylene fiber environment-friendly oil agent and preparation method thereof

A green and environmentally friendly polypropylene fiber technology, applied in fiber types, fiber treatment, textiles and papermaking, etc., can solve problems such as unstable oil quality, achieve low end-breakage rate, not easy to peel off, and less fuzzing during spinning

Inactive Publication Date: 2020-01-17
如皋市雨润纤维科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a polypropylene fiber green and environment-friendly oil and its preparation method in order to solve the problem that the existing polypropylene oil agent relies on imports and the quality of the domestically produced oil agent is unstable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1, a polypropylene fiber green and environment-friendly oil agent, comprising the following raw materials in parts by weight: glyceryl trioleate 10, polyoxyethylene ether 20, polyoxypropylene fat 25, phosphate ester 10, potassium phosphate salt 2, poly Isobutylene 5, mineral oil 50;

[0024] The polyoxyethylene ether is an alkyl polyoxyethylene ether, specifically trimethylolaminopropane polyoxyethylene ether, and the polyoxypropylene fat is fatty acid polyoxypropylene fat, specifically polyoxypropylene stearate, The potassium phosphate is potassium orthophosphate;

[0025] The preparation method of described a kind of polypropylene fiber green environment-friendly oil agent, comprises the following steps,

[0026] Step 1: Weigh the raw materials in the above parts by weight, pour mineral oil, potassium phosphate, polyoxyethylene ether and glyceryl trioleate into a reaction kettle, stir and heat to 90°C;

[0027] Step 2: Spray polyoxypropylene resin into th...

Embodiment 2

[0029] Embodiment 2, a polypropylene fiber green and environment-friendly oil agent, comprising the following raw materials in parts by weight: glyceryl trioleate 25, polyoxyethylene ether 30, polyoxypropylene fat 10, phosphate ester 3, potassium phosphate salt 5, poly Isobutene 2, mineral oil 30;

[0030] The polyoxyethylene ether is an alkyl polyoxyethylene ether, specifically trimethylolaminopropane polyoxyethylene ether, and the polyoxypropylene fat is fatty acid polyoxypropylene fat, specifically polyoxypropylene stearate, The potassium phosphate is potassium orthophosphate;

[0031] The preparation method of described a kind of polypropylene fiber green environment-friendly oil agent, comprises the following steps,

[0032] Step 1: Weigh the raw materials in the above parts by weight, pour mineral oil, potassium phosphate, polyoxyethylene ether and triolein into a reaction kettle, stir and heat to 92°C;

[0033] Step 2: Spray polyoxypropylene resin into the reaction ke...

Embodiment 3

[0035] Embodiment 3, a kind of polypropylene fiber green environment-friendly oil agent, comprising the following raw materials by weight: glyceryl trioleate 12, polyoxyethylene ether 24, polyoxypropylene fat 20, phosphate ester 7, potassium phosphate salt 4, poly Isobutene 1, mineral oil 32;

[0036] The polyoxyethylene ether is an alkyl polyoxyethylene ether, specifically trimethylolaminopropane polyoxyethylene ether, and the polyoxypropylene fat is fatty acid polyoxypropylene fat, specifically polyoxypropylene stearate, The potassium phosphate is potassium orthophosphate;

[0037] The preparation method of described a kind of polypropylene fiber green environment-friendly oil agent, comprises the following steps,

[0038] Step 1: Weigh the raw materials in the above parts by weight, pour mineral oil, potassium phosphate, polyoxyethylene ether and glyceryl trioleate into a reaction kettle, stir and heat to 95°C;

[0039] Step 2: transport the product of step 1 to the coole...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polypropylene fiber environment-friendly oil agent. The polypropylene fiber environment-friendly oil agent comprises the following raw materials in parts by weight: 10-25 parts of triolein, 20-30 parts of polyoxyethylene ether, 10-25 parts of polyoxypropylene ester, 1-10 parts of phosphate, 2-5 parts of potassium phosphate, 1-5 parts of polyisobutylene and 30-50 parts ofmineral oil, wherein the polyoxyethylene ether is alkyl polyoxyethylene ether, specifically trimethylol aminopropane polyoxyethylene ether, the polyoxypropylene ester is fatty acid polyoxypropylene ester, specifically polyoxypropylene stearate, and the potassium phosphate salt is orthophosphate potassium salt. According to the polypropylene fiber environment-friendly oil agent disclosed by the invention, spun yarns oiled by using the oil agent has good spinnability in both spinning processing and processing after spinning, the broken end rate is low, spun yarn fuzziness is less, and the plasticity and the flexibility of the oiled spun yarns are improved by adding polyisobutylene, so that spinning of polypropylene is facilitated.

Description

technical field [0001] The invention belongs to the technical field of oil preparation, in particular to a polypropylene fiber green and environment-friendly oil and a preparation method thereof. Background technique [0002] In the production process of polypropylene fiber, oiling the filaments is an important means to ensure the smooth progress of the whole spinning process and the preparation of polypropylene fibers with high quality and good performance. At the same time, it also has a great influence on the post-spinning processing of fibers. The adhesion of the polypropylene oil used in this process to the surface of the polypropylene is only 0.4% to 0.6% of the fiber mass, but it plays an important role in the process from fiber production to spinning to final fabric processing. The polypropylene oil agent should be able to endow the fiber with excellent antistatic properties, a certain oil film strength, and good smoothness; make the fiber production and post-process...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/224D06M15/53D06M13/292D06M11/71D06M13/02D06M15/227D06M101/20
CPCD06M11/71D06M13/02D06M13/2246D06M13/292D06M15/227D06M15/53D06M2101/20
Inventor 张诗涵
Owner 如皋市雨润纤维科技有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com