A kind of preparation method of mussel shell powder/carboxymethyl cellulose composite gel adsorbent

A technology of carboxymethyl cellulose and mussel shell powder, applied in separation methods, chemical instruments and methods, alkali metal compounds, etc., can solve problems such as secondary pollution, inconvenience in use, etc., achieve good adsorption, reduce preparation components, Realize the effect of waste utilization

Active Publication Date: 2021-12-17
ZHEJIANG OCEAN UNIV
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the existing calcium hydroxide system CO 2 The adsorbents are all powdery, which is inconvenient to use, especially when used for the absorption of carbon dioxide in the flue, it is easy to cause secondary pollution and other problems. The invention provides a mussel shell powder / carboxymethyl cellulose composite gel adsorption The preparation method of the agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A preparation method of mussel shell powder / carboxymethyl cellulose composite gel adsorbent, said method comprising the following steps:

[0040] 1) Calcining mussel shells at 500°C for 4 hours at 500°C for 4 hours to form mussel shell powder;

[0041] 2) Mix carboxymethyl cellulose and water at a dosage ratio of 5g: 50mL and stir until carboxymethyl cellulose is completely dissolved to obtain a thick liquid, and the obtained mussel shell powder and thick liquid are mixed at a dosage ratio of 10g : 50mL ratio is mixed and stirred so that the mussel shell powder is evenly dispersed to obtain a dispersion;

[0042] 3) Add 60g of cross-linking agent to every liter of dispersion to make it form a gel, freeze-dry to obtain the mussel shell powder / carboxymethyl cellulose composite gel adsorbent, the obtained mussel shell powder / carboxymethyl cellulose composite The gel adsorbent is in the form of a hard sheet.

Embodiment 2

[0044] A preparation method of mussel shell powder / carboxymethyl cellulose composite gel adsorbent, said method comprising the following steps:

[0045] 1) Calcining mussel shells at 600°C for 3 hours at 600°C for 3 hours to form mussel shell powder;

[0046] 2) Mix carboxymethyl cellulose and water at a dosage ratio of 20g: 50mL and stir until the carboxymethyl cellulose is completely dissolved to obtain a thick liquid. The obtained mussel shell powder and thick liquid are mixed at a dosage ratio of 30g : 50mL ratio is mixed and stirred so that the mussel shell powder is evenly dispersed to obtain a dispersion;

[0047] 3) Add 100g of cross-linking agent to every liter of dispersion to make it form a gel, freeze-dry to obtain the mussel shell powder / carboxymethyl cellulose composite gel adsorbent, the obtained mussel shell powder / carboxymethyl cellulose composite The gel adsorbent is in the form of a hard sheet.

Embodiment 3

[0049] A preparation method of mussel shell powder / carboxymethyl cellulose composite gel adsorbent, said method comprising the following steps:

[0050]1) Calcining mussel shells at 500°C for 4 hours at 500°C for 4 hours to form mussel shell powder;

[0051] 2) Mix carboxymethyl cellulose and water at a dosage ratio of 5g: 50mL and stir until carboxymethyl cellulose is completely dissolved to obtain a thick liquid, and the obtained mussel shell powder and thick liquid are mixed at a dosage ratio of 10g : 50mL ratio is mixed and stirred so that the mussel shell powder is evenly dispersed to obtain a dispersion;

[0052] 3) Add 60g of cross-linking agent to every liter of dispersion to make it form a gel, dry at 90°C under 0.2atm to obtain the mussel shell powder / carboxymethylcellulose composite gel adsorbent, the obtained mussel shell powder / Carboxymethylcellulose composite gel adsorbent is fluffy and elastic block.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
carbon dioxide adsorption capacityaaaaaaaaaa
carbon dioxide adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of preparation of adsorption materials, in particular to a preparation method of mussel shell powder / carboxymethyl cellulose composite gel adsorbent. It includes: calcining mussel shells as raw materials until mussel shell powder is formed; dissolving carboxymethyl cellulose in water to prepare a thick liquid, and adding the obtained mussel shell powder into the thick liquid to disperse evenly , to obtain a dispersion; adding a crosslinking agent to the dispersion to form a gel, and drying to obtain a mussel shell powder / carboxymethyl cellulose composite gel adsorbent. The present invention can simply and efficiently prepare the fluffy mussel shell powder / carboxymethyl cellulose composite gel adsorbent with good adsorption properties; effectively utilize the mussel shells which are wastes from seafood processing, reduce the preparation components, and simultaneously Waste utilization is realized; the prepared mussel shell powder / carboxymethyl cellulose composite gel adsorbent can be reused.

Description

technical field [0001] The invention relates to the field of preparation of adsorption materials, in particular to a preparation method of mussel shell powder / carboxymethyl cellulose composite gel adsorbent. Background technique [0002] At present, the smog problem has attracted the attention of most countries. Due to the rapid development of industry and the destruction of furniture to the environment, my country's air pollution CO 2 The impact is very serious, SO 2 and many other industrial pollutants. The world is experiencing various disasters caused by global warming, CO 2 Filtration and emission reduction has become an important topic in the scientific community in the near future, especially for CO 2 Absorption technology development. CO in the flue gas of coal-fired power plants 2 accounted for global CO 2 more than 60% of the total emissions, apparently, the CO in the flue gas 2 Absorption is the realization of CO 2 The most effective way to reduce emission...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/28B01J20/24B01J20/30B01D53/02
CPCB01J20/28047B01J20/24B01J20/041B01D53/02B01D2253/1124B01D2253/20B01D2257/504Y02C20/40
Inventor 王阳光欧阳小琨王南杨立业
Owner ZHEJIANG OCEAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com