Preparation method for reducing down feather loss rate
A technology of loss rate and down, applied in the field of down, can solve the problems of high loss rate of down and unsatisfactory bulkiness, and achieve the effect of good adsorption effect, good deodorization function, and avoidance of sticking.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] A preparation method for reducing down loss rate, comprising the steps of:
[0020] S1. Remove impurities from 100 kg of raw cashmere, wash with water, dry, add 0.1 kg of nano-silver and mix evenly, microwave treatment for 50 s, microwave treatment power is 120 W, microwave treatment temperature is 48 ° C, and prefabricated material a is obtained;
[0021] S2, mix 3kg ferric chloride hexahydrate, 4kg ferrous chloride tetrahydrate and 50kg water, heat up to 97°C and stir for 30min, add 5kg of ammonia water with a concentration of 18wt% and stir evenly, then add 2kg of humic acid, adjust the temperature to Stir at 65°C for 40 minutes, add 0.4kg meteorite powder and stir for 60 minutes at a stirring speed of 2200r / min, centrifuge to remove the upper layer solution, dry the lower layer solids, and pulverize to obtain prefabricated material b;
[0022] S3. Mix 100kg of prefabricated material a, 4kg of prefabricated material b, 0.1kg of compound biological enzyme, 2kg of rose...
Embodiment 2
[0025] A preparation method for reducing down loss rate, comprising the steps of:
[0026] S1. Remove impurities from 100 kg of raw cashmere, wash with water, dry, add 0.8 kg of nano-silver and mix evenly, microwave treatment for 20 s, microwave treatment power is 150 W, and microwave treatment temperature is 40 ° C to obtain prefabricated material a;
[0027] S2, mix 8kg ferric chloride hexahydrate, 1kg ferrous chloride tetrahydrate and 80kg water, heat up to 92°C and stir for 80min, add 2kg of ammonia water with a concentration of 22wt% and stir evenly, then add 1kg humic acid, adjust the temperature to Stir at 75°C for 20 minutes, add 0.9kg meteorite powder and stir for 30 minutes at a stirring speed of 2400r / min, centrifuge to remove the upper layer solution, dry the lower layer solids, and crush to obtain prefabricated material b;
[0028] S3. Mix 100kg of prefabricated material a, 1kg of prefabricated material b, 0.4kg of compound biological enzyme, 1kg of rose essential...
Embodiment 3
[0031] A preparation method for reducing down loss rate, comprising the steps of:
[0032] S1. Remove impurities from 100 kg of raw cashmere, wash with water, dry, add 0.2 kg of nano-silver and mix evenly, microwave treatment for 40 seconds, microwave treatment power is 130W, and microwave treatment temperature is 46°C to obtain prefabricated material a;
[0033] S2. Mix 4kg of ferric chloride hexahydrate, 3kg of ferrous chloride tetrahydrate and 60kg of water, heat up to 96°C and stir for 50min, add 4kg of ammonia water with a concentration of 19wt% and stir evenly, then add 1.8kg of humic acid to adjust the temperature Stir at 68°C for 35 minutes, add 0.5kg meteorite powder and stir for 50 minutes at a stirring speed of 2250r / min, centrifuge to remove the upper layer solution, dry the lower layer solids, and crush to obtain prefabricated material b;
[0034] S3. Mix 100kg of prefabricated material a, 3kg of prefabricated material b, 0.2kg of compound biological enzyme, 1.8kg...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com