Karst pipeline type ultrahigh-expansion grouting material for efficient blocking of gushing water, and preparation method, use method and application thereof

A kind of grouting material and karst technology, which is applied in the field of super-high expansion grouting material for high-efficiency plugging of karst pipeline-type water gushing, can solve the problems of cross-linking and curing of acrylic resin particles, and achieve the effect of low cost and simple operation

Active Publication Date: 2020-02-25
SHANDONG UNIV
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the inventor found in subsequent further research that although the water plugging of the expanded polymer grouting material relies on the rapid expansion of the acrylic resin particles when they encounter water, the volume of the particles increases rapidly, and the particles squeeze each other to form a plugging body to real...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Karst pipeline type ultrahigh-expansion grouting material for efficient blocking of gushing water, and preparation method, use method and application thereof
  • Karst pipeline type ultrahigh-expansion grouting material for efficient blocking of gushing water, and preparation method, use method and application thereof
  • Karst pipeline type ultrahigh-expansion grouting material for efficient blocking of gushing water, and preparation method, use method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] A preparation of super-high expansion grouting material for high-efficiency plugging of karst pipeline-type water gushing, comprising the following steps:

[0077] 1. Preparation of polymer granules A:

[0078] (1) Acrylic acid neutralization stage: first prepare 36 parts of 10% acrylic acid solution and 5 parts of 20% acrylamide interpolymer solution with ice water, add 12 parts of 10% lye to obtain neutralization degree 60% acrylic acid solution.

[0079] (2) Initiating polymerization reaction stage: 0.072 parts of crosslinking agent N, N-methylenebisacrylamide is configured into a solution with a mass fraction of 50%, added to the acrylic acid neutralizing solution configured in step (1), and Stir evenly for 1 hour, then add 50% initiator solution prepared by 0.025 parts of potassium persulfate, heat up to 80° C., and react for 23 minutes to form a colloidal polymer.

[0080] (3) Drying and crushing stage: Grinding the colloidal polymer obtained in step (3), drying...

Embodiment 2

[0103] A preparation of super-high expansion grouting material for high-efficiency plugging of karst pipeline-type water gushing, comprising the following steps:

[0104] 1. Preparation of polymer granules A:

[0105] (1) Acrylic acid neutralization stage: first prepare 36 parts of acrylic acid solution with a mass fraction of 80% and 5 parts of acrylamide interpolymer solution with a mass fraction of 80% with ice water, and add 24 parts of lye with a mass fraction of 60% to obtain the degree of neutralization Neutralizing liquid for 90% acrylic acid solution.

[0106] (2) The stage of initiating polymerization reaction: 0.09 parts of crosslinking agent N, N-methylenebisacrylamide is configured into a solution with a mass fraction of 50%, and 5 parts of the gelling catalyst (polyethylene bisacrylamide) of crosslinking solidification solution B Alcohol: p-di-o-chloroaniline methane: polyether polyol = 2:1:2) to prepare a solution with a mass fraction of 50%, add it to the acry...

Embodiment 3

[0121] A preparation of super-high expansion grouting material for high-efficiency plugging of karst pipeline-type water gushing, comprising the following steps:

[0122] 1. Preparation of polymer granules A:

[0123] (1) Acrylic acid neutralization stage: first prepare 36 parts of acrylic acid solution with a mass fraction of 40% and 5 parts of acrylamide interpolymer solution with a mass fraction of 40% with ice water, and add 12 parts of lye with a mass fraction of 50% to obtain the degree of neutralization It is 75% acrylic acid neutralizing solution.

[0124] (2) Initiating polymerization reaction stage: 0.05 part of crosslinking agent N,N-methylenebisacrylamide is configured into a solution with a mass fraction of 50%, and added to the acrylic acid neutralizing solution prepared in step (1), and uniformly Stir for 1h. Then add a 50% initiator solution prepared by 0.025 parts of ammonium persulfate, heat up to 80° C., and react for 88 minutes to form a colloidal polymer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of underground engineering blocking materials, and particularly relates to a karst pipeline type ultrahigh-expansion grouting material for efficient blocking of gushing water, and a preparation method, a use method and an application thereof. The grouting material comprises a high-molecular polymer particle A and a crosslinking curing liquid B, and thehigh-molecular polymer particle A is of an embedded core-shell structure, wherein primary high-molecular water-absorbent resin serves as the core, a part of a gelling catalyst is attached to the surface of the core to form the shell, and a part of the gelling catalyst permeates into the core to form an embedded structure. Before the grouting material is used, the high-molecular polymer particle Aand the crosslinking curing liquid B are stirred to achieve full mixing; and the obtained mixed solution is injected into cracks of a rock mass fracture zone as the grouting material. The grouting material can efficiently control high-pressure large-flow karst gushing water, improves the gushing water blocking efficiency, and further promotes the construction of major underground engineering in China.

Description

technical field [0001] The invention belongs to the technical field of plugging materials for underground engineering, and in particular relates to an ultra-high expansion grouting material for high-efficiency plugging of karst pipeline-type water gushing and its preparation, use and application. Background technique [0002] The information disclosed in the Background of the Invention is only intended to increase the understanding of the general background of the invention, and is not necessarily to be taken as an acknowledgment or any form of suggestion that the information constitutes the prior art that is already known to those skilled in the art. [0003] With the rapid development of society, traffic engineering is developing rapidly, the pace of infrastructure construction continues to accelerate, and projects such as railways, tunnels, highways, and mines are increasing. Especially with the vigorous implementation of the 21st Century Maritime Silk Road, the eastern c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L33/02C08L75/08C08J3/12C08F220/06C08F220/56C08F222/38
CPCC08L33/26C08L75/08C08J3/126C08F220/06C08J2333/26C08J2471/00C08J2471/02C08L2207/53C08L33/02C08F220/56C08F222/385C04B2111/70C04B2111/00663C04B26/06C04B2111/0075C04B2111/00698C04B24/06C04B24/2623C04B24/2652C04B24/38C04B2103/20C04B2103/0049C08F2800/20C08F2810/20C08J3/16C08J3/244C08J3/245C08J2333/02
Inventor 刘人太马晨阳陈孟军王振军白继文段少龙田嘉伟王晓晨张春雨李修浩
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap