Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of low surface treatment and anti-corrosion coatings, applied in the direction of anti-corrosion coatings, epoxy resin coatings, anti-fouling/underwater coatings, etc. Efforts to reduce pollution
Inactive Publication Date: 2020-04-07
WUXI HUADONG ZINDN TECH
View PDF6 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The purpose of the present invention is to provide a new type of high-efficiency water-based epoxy low surface treatment anti-corrosion coating and its preparation for the problem that large-scale steel structures and equipment, such as bridges, pipelines, and complex equipment, cannot be thoroughly sandblasted and rust-removed during the maintenance process. Methods and uses, low surface treatment coatings (Surface-tolerant Coating) are mainly aimed at the situation where it is impossible to fully reach the sandblasting grade Sa2. The surface of St3 level and the surface of the old coating choose this type of coating, which has good permeability and substrate adhesion; there will be no compatibility problems on the old coating; it has certain corrosion inhibition performance; excellent outdoor construction, etc. features
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0047] A water-based epoxy anti-corrosion coating with low surface treatment. The coating is composed of components A and B and deionized water. Basalt flakes, wetting and dispersing agent, leveling agent, defoamer and deionized water are prepared; component B is curing agent; all parts are parts by weight; the specific coating formula is as follows:
[0077] A water-based epoxy anti-corrosion coating with low surface treatment. The coating is composed of components A and B and deionized water. Basalt flakes, wetting and dispersing agent, leveling agent, defoamer and deionized water are prepared; component B is curing agent; all parts are parts by weight; the specific coating formula is as follows:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a waterborne epoxy low-surface treatment anticorrosive paint, a preparation method and application thereof. The paint is composed of 80-85 weight parts of matrix coating, 10-12weight parts of a curing agent and 3-6 weight parts of deionized water. Specifically, the matrix coating is prepared from waterborne epoxy resin, a nano composite liquid, a rust conversion agent, titanium dioxide, an antirust pigment, micron basalt scales, a wetting dispersant, a leveling agent, a defoaming agent and deionized water. The matrix coating, the curing agent and the distilled water are added into a clean container according to a weight ratio of 80-85:10-12:3-6 and are mixed uniformly, and then curing is carried out for 5-10min, thus obtaining the paint applicable to coating. The paint disclosed by the invention can be applied to large steel structures like bridges, pipelines and complex equipment without thorough rust removal, and has excellent corrosion resistance.
Description
technical field [0001] The invention relates to a water-based epoxy anticorrosion coating with low surface treatment, a preparation method and application thereof, and belongs to the field of coatings. Background technique [0002] In recent years, a large number of steel structures such as offshore oil drilling platforms, power plants, built bridges and stadium facilities at home and abroad have entered the maintenance period, and the old coating needs to be repainted. However, it is very difficult to perform pre-sand blasting treatment on the basis of these built steel structures, involving environmental protection, construction difficulty and engineering maintenance cost. [0003] With the development of industry, the industrial paint market for metal protection and decoration also develops and grows accordingly. The protective coatings used in some outdoor metalengineering facilities are anti-corrosion coatings, which need to be completely derusted, but some large-scal...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 