1,2,4-triazole nitrate-coated boron-magnesium composite metal powder fuel and preparation method thereof

A composite metal and nitrate technology, which is used in explosive composite components, offensive equipment, explosive processing equipment, etc., can solve the problems of high calorific value, high oxygen consumption of boron, and more residues, etc., to improve combustion efficiency, increase The effect of improving combustion temperature and heat release

Active Publication Date: 2021-09-17
HUZHOU TEACHERS COLLEGE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (2) Boron consumes a lot of oxygen and produces a lot of residues, which cannot give full play to its high calorific value.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 1,2,4-triazole nitrate-coated boron-magnesium composite metal powder fuel and preparation method thereof
  • 1,2,4-triazole nitrate-coated boron-magnesium composite metal powder fuel and preparation method thereof
  • 1,2,4-triazole nitrate-coated boron-magnesium composite metal powder fuel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation process of 1,2,4-triazole nitrate is as follows: in a nitrogen-filled drying oven, add 1.0458g, 15.1mmol of 1,2,4-triazole to a Schlenk flask, under nitrogen flow, under stirring conditions Add 13ml of anhydrous methanol, then carefully add 1.3925g, 15.2mmol of concentrated nitric acid, react at room temperature for 1h, transfer to a vacuum drying oven after the reaction is completed, and dry at room temperature for 24h, the white crystal product is the prepared 1,2,4-triazole nitrates.

[0036] In order to test the application performance of the boron-magnesium composite metal powder fuel coated with the energetic ion salt 1,2,4-triazole nitrate of this patent, the physical and chemical properties of the fuel were firstly characterized, and secondly, the fuel particles were added to the boron-rich Fuel propellants and boron-based ignition powders are prepared to test their combustion properties.

[0037] The boron-containing fuel-rich propellant formul...

Embodiment 1

[0044] Taking the target product quality of 100g as an example, the amount and type of various raw materials required are: boron-magnesium composite metal powder (particle size 4.5 μm, boron content 93%) 78g, 1,2,4-triazole nitrate (purity 99 %) 21.2g, silane coupling agent KH5600.8g, methanol 1060ml. Accurately weigh quantitative 1,2,4-triazole nitric acid and KH560, dissolve in methanol, add boron-magnesium composite metal powder to the above solution under room temperature stirring conditions, fully stir, and evenly disperse to form a mixed suspension; The mixed suspension was evacuated in a four-neck flask under stirring at 45° C. until the surface was dry and semi-slurry. Take it out and move it to a vacuum oven for drying at 50°C until the boron-magnesium composite metal powder is in a relatively dry state. The above-mentioned boron-magnesium composite metal powder is sieved, classified and screened to form boron-magnesium composite metal powder fuel coated with energet...

Embodiment 2

[0046]Taking the target product quality of 100g as an example, the amount and type of various raw materials required are: boron-magnesium composite metal powder (particle size 4.5 μm, boron content 95%) 78g, 1,2,4-triazole nitrate (purity 99 %) 21.2g, silane coupling agent KH5600.8g, methanol 1060ml. Accurately weigh quantitative 1,2,4-triazole nitric acid and KH560, dissolve in methanol, add boron-magnesium composite metal powder to the above solution under room temperature stirring conditions, fully stir, and evenly disperse to form a mixed suspension; The mixed suspension was evacuated in a four-neck flask under stirring at 45° C. until the surface was dry and semi-slurry. Take it out and move it to a vacuum oven for drying at 50°C until the boron-magnesium composite metal powder is in a relatively dry state. The above-mentioned boron-magnesium composite metal powder is sieved, classified and screened to form boron-magnesium composite metal powder fuel coated with energeti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a boron-magnesium composite metal powder fuel coated with 1,2,4-triazole nitrate and a preparation method thereof. The fuel of the present invention comprises the following composition in parts by weight: 70-80 parts of boron-magnesium composite metal powder; 20-30 parts of 1,2,4-triazole nitrate; and 0.5-1 part of silane coupling agent. The invention also discloses a preparation method of boron-magnesium composite metal powder fuel coated with 1,2,4-triazole nitrate, including the steps of raw material metering, preparation of raw material solution, adding boron-magnesium composite metal powder, vacuum drying, sieving, etc. . Adding the fuel of the invention to the boron-rich fuel-rich propellant or ignition powder can reduce the ignition temperature, improve the combustion efficiency, and fully utilize the characteristics of high calorific value of the boron powder.

Description

technical field [0001] The invention belongs to the technical field of solid propellants and ignition powder high-energy fuels, in particular to boron-magnesium composite metal powder fuel coated with 1,2,4-triazole nitrate and a preparation method thereof. Background technique [0002] Among various metal fuels that can be used in the fields of solid propellants and explosives, boron-magnesium composite metal powder has many advantages such as high mass calorific value, high volume calorific value, non-toxicity, non-toxic combustion products, and abundant resources. Research hotspots in the field of boron-rich fuel propellants and explosives. In the field of solid propellant and propellant and explosives, a large amount of addition can improve the volumetric specific impulse. Although the theoretical calorific value of boron-magnesium composite metal powder is very high, its actual test calorific value is very low. the reason is: [0003] (1) There is a layer of B on the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C06B33/08C06B21/00
CPCC06B21/0008C06B33/08
Inventor 郝利峰曹枫
Owner HUZHOU TEACHERS COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap