Preparation method of mica plate with electromagnetic wave absorption function
A technology for absorbing electromagnetic waves and mica boards, applied in the field of preparation of mica boards, can solve the problems of volatilization and release of toxic and harmful substances, pyrolysis of organic matter, etc., and achieve the effect of improving insulation performance, excellent high temperature resistance and wave absorption performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] Add 15 parts of mica powder, 12 parts of barium ferrite powder, 8 parts of flaky sendust powder and 1.4 parts of sodium silicate solution into the mixer in parts by weight, stir for 75 minutes to make it evenly mixed, then continue to stir and Dry at a temperature of 110°C, and obtain a primary composite powder after lowering to normal temperature; add another 85 parts of mica powder and 8 parts of silica sol to the primary composite powder in order by weight, stir for 75 minutes to make it evenly mixed, and then continue Stir and dry at a temperature of 80°C, and obtain secondary composite powder after lowering to normal temperature; place the secondary composite powder in a press mold, and press it into a slab under a pressure of 45MPa; place the slab in a nitrogen furnace, Insulate at 700°C for 15 minutes to make it completely solidified, and obtain a mica board with a wave-absorbing function. After testing in the range of 1GHz~8GHz, the absorption performance of the...
Embodiment 2
[0016] Add 20 parts of mica powder, 10 parts of barium ferrite powder, 7 parts of flaky sendust powder and 1.5 parts of sodium silicate solution into the mixer in parts by weight, stir for 60 minutes to make it evenly mixed, then continue to stir and Dry at a temperature of 110°C, and obtain a primary composite powder after lowering to normal temperature; add another 80 parts of mica powder and 8 parts of silica sol to the primary composite powder in order by weight, stir for 60 minutes to make it evenly mixed, and then continue Stir and dry at a temperature of 80°C, and obtain secondary composite powder after lowering to normal temperature; place the secondary composite powder in a press mold, and press it into a slab under a pressure of 45MPa; place the slab in a nitrogen furnace, Insulate at 400° C. for 45 minutes to make it completely solidified to obtain a mica board with a wave-absorbing function. After testing in the range of 1GHz~8GHz, the absorption performance of the...
Embodiment 3
[0018] Add 18 parts of mica powder, 15 parts of barium ferrite powder, 10 parts of flaky sendust powder and 1.8 parts of sodium silicate solution into the mixer in parts by weight, stir for 90 minutes to make it evenly mixed, then continue to stir and Dry at a temperature of 90°C, and get a primary composite powder after lowering to normal temperature; add another 82 parts of mica powder and 6 parts of silica sol to the primary composite powder in order by weight, stir for 90 minutes to make it evenly mixed, and then continue Stir and dry at a temperature of 60°C, and obtain a secondary composite powder after cooling down to normal temperature; place the secondary composite powder in a press mold, and press it into a slab under a pressure of 50MPa; place the slab in a nitrogen furnace, Keep it warm at 600°C for 30 minutes to make it completely solidified, and obtain a mica board with a wave-absorbing function. After testing in the range of 1GHz~8GHz, the absorption performance...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap