A kind of high-strength tear-resistant nonwoven fabric for bag production and preparation method thereof

A high-strength, tear-resistant technology, used in non-woven fabrics, rayon manufacturing, textiles and papermaking, etc., can solve problems such as the inability to meet the requirements of high-performance guarantee materials, the inability to meet market demands, and the general tear resistance , to save manpower and equipment costs, improve mechanical properties such as strength, and easy operation.

Active Publication Date: 2022-08-05
厦门澳丽妃包袋有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] 1. The strength is low and the tear resistance is average, which cannot meet the requirements of some high-performance guarantee materials;
[0009] 2. If non-woven fabrics made of pure special fibers (or filaments, long fibers) are used, the cost is high and cannot meet market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength tear-resistant nonwoven fabric for bag production and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A high-strength tear-resistant non-woven fabric for bag production, the high-strength tear-resistant non-woven fabric for bag production is prepared from high-strength composite fibers through a spunlace process or a needle punch process;

[0058] The high-strength composite fibers are made from raw materials including the following parts by weight:

[0059] 30-37 parts of polybutylene adipamide,

[0060] 45-55 parts of polyhexamethylene adipamide,

[0061] 15-20 parts of polysaccharide diamine,

[0062] 10-14 parts of polyparaphenylene terephthalamide,

[0063] 3.5-5 parts of carboxylated carbon nanotubes,

[0064] 2.5~3.5 parts of graphene oxide,

[0065] 1.5~2.2 parts of cerium oxide,

[0066] 3 to 5 parts of nanofillers,

[0067] 5 to 10 parts of flow aid.

[0068] In this embodiment, the high-strength composite fibers are preferably made of raw materials including the following parts by weight:

[0069] 34 parts of polybutylene adipamide,

[0070] 50 parts...

Embodiment 2

[0088] A high-strength tear-resistant non-woven fabric for bag production, the high-strength tear-resistant non-woven fabric for bag production is prepared from high-strength composite fibers through a spunlace process or a needle punch process;

[0089] The high-strength composite fibers are made from raw materials including the following parts by weight:

[0090] 30 parts of polybutylene adipamide,

[0091] 45 parts of polyhexamethylene adipamide,

[0092] 15 parts of polysaccharide diamine,

[0093] 10 parts of polyparaphenylene terephthalamide,

[0094] 3.5 parts of carboxylated carbon nanotubes,

[0095] 2.5 parts of graphene oxide,

[0096] 1.5 parts of cerium oxide,

[0097] 3 parts of nanofillers,

[0098] 5 parts of flow aid.

[0099] In this embodiment, the carboxylated carbon nanotubes are carboxylated multi-walled carbon nanotubes, and the diameter of the carboxylated multi-walled carbon nanotubes is less than 3 nm and the length is 25-40 nm.

[0100] In th...

Embodiment 3

[0109] A high-strength tear-resistant non-woven fabric for bag production, the high-strength tear-resistant non-woven fabric for bag production is prepared from high-strength composite fibers through a spunlace process or a needle punch process;

[0110] The high-strength composite fibers are made from raw materials including the following parts by weight:

[0111] 37 parts of polybutylene adipamide,

[0112] 55 parts of polyhexamethylene adipamide,

[0113] 20 parts of polysaccharide diamine,

[0114] 14 parts of polyparaphenylene terephthalamide,

[0115] 5 parts of carboxylated carbon nanotubes,

[0116] 3.5 parts of graphene oxide,

[0117] 2.2 parts of cerium oxide,

[0118] 5 parts of nanofillers,

[0119] 10 parts of flow aid.

[0120] In this embodiment, the carboxylated carbon nanotubes are carboxylated multi-walled carbon nanotubes, and the diameter of the carboxylated multi-walled carbon nanotubes is less than 3 nm and the length is 25-40 nm.

[0121] In thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength tear-resistant nonwoven fabric for bag production and a preparation method thereof. The high-strength composite fibers are made from the following raw materials in parts by weight: 30-37 parts of polybutylene adipamide, 45-55 parts of polyhexamethylene adipamide, and 15-55 parts of polysebamide 20 parts, 10-14 parts of poly(p-phenylene terephthalamide), 3.5-5 parts of carboxylated carbon nanotubes, 2.5-3.5 parts of graphene oxide, 1.5-2.2 parts of cerium oxide, 3-5 parts of nano-fillers, 5 to 10 parts of flow aid. Under the condition of the same thickness, the high-strength tear-resistant non-woven fabric for bag production of the present invention has large bursting strength and breaking strength, which are obviously better than ordinary nylon non-woven fabrics, and has high strength and high tear resistance. Excellent performance.

Description

technical field [0001] The invention relates to the technical field of non-woven fabrics, in particular to a high-strength tear-resistant non-woven fabric for bag production and a preparation method thereof. Background technique [0002] Non-woven fabrics, also known as non-woven fabrics, are composed of oriented or random fibers. It is called cloth because of its appearance and certain properties. The non-woven fabric has no warp and weft threads, so it is very convenient to cut and sew, and it is light and easy to shape. [0003] Because it is a fabric that does not require spinning and weaving, it just orients or randomly arranges textile staple fibers or filaments to form a web structure, which is then reinforced by mechanical, thermal bonding or chemical methods. [0004] It is not interwoven and braided by yarns one by one, but the fibers are directly bonded together by physical methods, so when you get the sticky scale in your clothes, you will find that, You can't...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/12D01F1/10D04H3/005D04H3/105D04H3/11
CPCD01F8/12D01F1/10D04H3/005D04H3/105D04H3/11
Inventor 赖广州
Owner 厦门澳丽妃包袋有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap