Preparation method for producing deep-drawn cold-formed medicinal aluminum foil with cast-rolling billet in short process
A short process, cold forming technology, applied in metal rolling and other directions, can solve the problems of strength and toughness to be improved, long production process, etc., to ensure the uniformity of grain structure, excellent deep drawing cold forming performance, resistance to cold forming. The effect of high breaking strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0051] This embodiment discloses a preparation method for producing deep-drawing cold-formed medicinal aluminum foil from a short-flow cast-rolled billet, which specifically includes the following steps:
[0052] (1) Melting and casting-rolling process: 8021 aluminum alloy is used for smelting, casting and rolling into billets with a certain thickness; the smelting and casting-rolling process must be cleaned of slag and degassing to ensure uniform composition, and the melting temperature is 700-770℃ , The temperature of the guide furnace is 730-770℃;
[0053] (2) Cold rolling and homogeneous high temperature treatment: the billet in step (1) is billeted and rolled. The billet is rolled through 1-3 passes to form a billet with a thickness of 2.0-6.5mm. The outer ring is welded and used The straps are tightened, and the annealing furnace enters the furnace for production; rolling oil is used for lubrication and cooling to obtain aluminum alloy coils;
[0054] (3) Intermediate rolling,...
Example Embodiment
[0078] Example one:
[0079] The specific steps of this embodiment are as follows:
[0080] (1) Melting, casting and rolling process: The smelting, smelting and casting process of 8021 aluminum alloy must be cleaned of slag and gas, and ensure uniform composition. The melting temperature is 755℃, and the temperature of the pilot furnace is 740℃.
[0081] In this embodiment, the mass percentages of the components in the 8021 alloy material are: a. Add the aluminum ingot and the AL-Fe master alloy to the smelting furnace according to the above proportions. The mass content of Fe is 20%, or the mass content of Fe is 75. % Of additives to control the proportion of each element in the aluminum alloy as Si=0.08%, Fe=1.35%, Cu=0.015%, Mn<0.05%, Mg<0.05%, Cr<0.05%, Zn<0.05%, Ti= 0.028%, the rest is Al; add modifier Sr: 0.018%; then smelt at 755℃, smelt for 5 hours and then refining, use 99.99% high-purity argon inert gas and refining agent for refining for 20 minutes, and remove the melt af...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Surface hardness value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap