Environment-friendly rubber and plastic product and preparation method thereof

A green and environmentally friendly technology for rubber and plastic products, applied in the rubber field, can solve the problems of excessive VOC emissions, large compression permanent deformation, and non-environmental protection, and achieve the effect of excellent mechanical properties

Pending Publication Date: 2020-08-25
HEBEI SHENZHOU THERMAL INSULATION BUILDING MATERIAL GRP CO LTD
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with single nitrile rubber, the tensile strength and tear resistance of blended rubber are improved, but the compression permanent deformation of blended rubber and plastic products is relatively large, which has become a technical bottleneck in the manufacture of rubber and plastic thermal insulation materials
By adding a large amount of phthalate plasticizers (DOP, DBP) to improve the resilience of rubber and plastic products, it is easy to lead to excessive VOC emissions, resulting in environmental impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly rubber and plastic product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0088] The second aspect of the present invention provides a method for preparing green environmental protection rubber and plastic products, the preparation method at least includes the following steps:

[0089] (1) Add nitrile rubber, polyvinyl chloride resin, protective wax, filler, flame retardant, foaming agent, active agent, chlorinated paraffin, and deodorant to the internal mixer and blend until the temperature of the blend reaches 140 -180℃ discharging;

[0090] (2) Put the intensive training materials into the training machine and cool down to resume training. When the temperature drops to 60-100 ° C, open the slices and store them for 20-26 hours after cooling;

[0091] (3) After the film is stored for 20-26 hours, continue to knead in the mill, add vulcanizing agent and accelerator, knead evenly, and then produce strips to obtain strips; extrude the strips through an extruder, and send them into an oven for drying For vulcanization and foaming, the oven temperatur...

Embodiment 1

[0097] Provided is a green and environment-friendly rubber and plastic product. In parts by weight, the preparation raw materials include: 14 parts of nitrile rubber, 5 parts of polyvinyl chloride resin, 4 parts of protective wax, 4.6 parts of filler, 4.7 parts of flame retardant, foaming agent 5 parts, 0.4 parts of active agent, 3 parts of accelerator, 0.2 parts of vulcanizing agent, 15 parts of chlorinated paraffin, 1.5 parts of deodorant.

[0098] The nitrile rubber can be obtained commercially, and the trade mark is JSRN230S.

[0099] The trade mark of described polyvinyl chloride is SG7.

[0100] The microcrystalline wax can be obtained commercially from manufacturers including but not limited to Shanghai Junpu Chemical Co., Ltd.

[0101] The filler is modified light calcium carbonate.

[0102] The modified light calcium carbonate is silane modified light calcium carbonate.

[0103] The silane is a combination of N-(6-aminohexyl)aminomethyltriethoxysilane and octadecyl...

Embodiment 2

[0117] Provided is a green and environment-friendly rubber and plastic product. The preparation raw materials include at least 10 parts by weight of nitrile rubber, 3 parts of polyvinyl chloride resin, 2 parts of protective wax, 1 part of filler, 4 parts of flame retardant, foaming 4 parts of agent, 0.2 part of active agent, 1 part of accelerator, 0.1 part of vulcanizing agent, 10 parts of chlorinated paraffin, and 0.3 part of deodorant.

[0118] The nitrile rubber can be obtained commercially, and the trade mark is JSRN230S.

[0119] The trade mark of described polyvinyl chloride is SG7.

[0120] The microcrystalline wax can be obtained commercially from manufacturers including but not limited to Shanghai Junpu Chemical Co., Ltd.

[0121] The filler is modified light calcium carbonate.

[0122] The modified light calcium carbonate is silane modified light calcium carbonate.

[0123] The silane is a combination of N-(6-aminohexyl)aminomethyltriethoxysilane and octadecyldime...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of rubber, in particular to an environment-friendly rubber and plastic product and a preparation method thereof. The preparation raw materials at least comprise, by weight: 10-18 parts of nitrile rubber, 3-9 parts of polyvinyl chloride resin, 2-6 parts of protective wax, 1-6 parts of a filler, 4-5 parts of a flame retardant, 4-7 parts of a foaming agent, 0.2-0.5 part of an active agent, 1-5 parts of an accelerant, 0.1-0.4 part of a vulcanizing agent, 10-20 parts of chlorinated paraffin and 0.3-2 parts of a deodorant. The preparation raw materials are selected preferentially, the proportion of the components is controlled and a deodorant is added, so that the rubber and plastic product has the characteristics of excellent mechanical properties, aging resistance and water resistance, is environment-friendly and safe, and can effectively protect the environment.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a green and environment-friendly rubber and plastic product and a preparation method thereof. Background technique [0002] Nitrile rubber (NBR) has good tear resistance, low compression deformation, excellent wear resistance and oil resistance. Its biggest use is to produce oil-resistant hoses, flame-retardant conveyor belts and oil-resistant rubber gasket materials. Has been widely used in automotive, aerospace, oil field chemical and other fields. At present, blending and modifying nitrile rubber to find a new reinforcement system and vulcanization system has become an important way to optimize the performance of nitrile rubber. [0003] At present, using technologies such as dynamic vulcanization technology, nitrile rubber / polyvinyl chloride, nitrile rubber / polypropylene, nitrile rubber / ethylene propylene rubber, nitrile rubber / polystyrene, nitrile rubber / chlorosulfonated Po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L27/06C08L91/06C08K13/06C08K9/06C08K3/26C08K3/22C08K5/09C08K5/39C08J9/10
CPCC08J9/103C08J9/0061C08J9/0023C08J9/0033C08J9/009C08J9/0066C08J9/0095C08J2203/04C08J2309/02C08J2427/06C08J2491/06C08K13/06C08K9/06C08K2003/265C08K2003/2224C08K5/09C08K5/39
Inventor 高铁强高铁彦高景岐
Owner HEBEI SHENZHOU THERMAL INSULATION BUILDING MATERIAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products