Sewed rock wool and preparation method thereof

A technology for sewing and tying rock wool and sewing and tying is applied in the field of sewing and tying rock wool and its preparation, which can solve the problems of poor waterproof performance of rock wool insulation boards, and achieve the effects of preventing water leakage and easy diffusion.

Inactive Publication Date: 2020-08-28
普莱斯德节能科技有限责任公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention proposes a sutured rock wool and its preparation method, which solves the problem of poor waterproof performance of rock wool insulation boards in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of sewing rock wool, including rock wool board, the two sides of the rock wool board are stitched with alkali-resistant mesh cloth by basalt fiber thread, and the mesh cloth and the rock wool board are stitched and then compounded with a 5mm mortar layer on its six sides;

[0023] The mortar layer includes Portland cement, silica sand, calcium carbonate, water, tris hydrochloride, maleic anhydride, and silicic acid in a mass ratio of 110:50:5:35:1.1:1 2% sodium alginate by mass in salt cement, and 1.5% aminopropyltriethoxysilane by mass in portland cement.

[0024] The rock wool board includes 150 parts of basalt, 60 parts of dolomite, 40 parts of slag, 25 parts of coke, and 18 parts of phenolic resin.

[0025] The preparation method of the above-mentioned stitched rock wool comprises the following steps:

[0026] A. Prepare basalt, dolomite, slag, coke, and phenolic resin, mix them, melt them at 1800°C, extrude, stretch, press, cool and solidify, and then relea...

Embodiment 2

[0030] A kind of seamed rock wool, including rock wool board, the two sides of the rock wool board are stitched with alkali-resistant mesh cloth by alkali-resistant fiber thread, and the mesh cloth and the rock wool board are stitched and then compounded with a 5mm mortar layer on both sides ;

[0031] The mortar layer includes Portland cement, silica sand, calcium carbonate, water, tris hydrochloride and maleic anhydride in a mass ratio of 100:60:4:40:1.08:1.

[0032] The rock wool board includes 200 parts of basalt, 50 parts of dolomite, 80 parts of slag, 20 parts of coke, and 20 parts of phenolic resin.

[0033] The preparation method of the above-mentioned stitched rock wool comprises the following steps:

[0034] A. Prepare basalt, dolomite, slag, coke, and phenolic resin, mix them, melt them at 2000°C, extrude, stretch, press, cool and solidify, and then release the mold to prepare rock wool boards;

[0035] B. Cut the rock wool board into shape, compound mesh cloth on...

Embodiment 3

[0038] A kind of seamed rock wool, including rock wool board, the two sides of the rock wool board are stitched with alkali-resistant mesh cloth with alkali-resistant fiber thread, and the mesh cloth and the rock wool board are stitched and then compounded with a 5mm mortar layer on the six sides ;

[0039] The mortar layer includes Portland cement, silica sand, calcium carbonate, water, Tris hydrochloride, maleic anhydride, and silicic acid in a mass ratio of 120:45:8:28:1.16:1 1% sodium alginate by mass of salt cement, and 3% aminopropyltriethoxysilane by mass of Portland cement.

[0040] The rock wool board includes 100 parts of basalt, 80 parts of dolomite, 30 parts of slag, 30 parts of coke, and 15 parts of phenolic resin.

[0041] The preparation method of the above-mentioned stitched rock wool comprises the following steps:

[0042] A. Prepare basalt, dolomite, slag, coke, and phenolic resin, mix them, melt them at 1500°C, extrude, stretch, press, cool and solidify, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pressureaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of buildings, and provides seamed rock wool. The seamed rock wool comprises a rock wool board, gridding cloth is seamed on two sides of the rock wool boardthrough fiber threads, and a mortar layer is composited on at least one side of the seamed gridding cloth and the rock wool board, the mortar layer comprises Portland cement, silica sand, calcium carbonate and water according to the mass ratio of (100-120): (45-60): (4-8): (28-40). The rock wool board is cut and formed, gridding cloth is composited on the surface of the rock wool board, the gridding cloth is sewn through fiber lines, and a rock wool composite layer is obtained; portland cement, silica sand, calcium carbonate and water are mixed and stirred into mortar, and then the mortar issmeared on the rock wool composite layer in a batched mode to obtain the seam-bound rock wool. By means of the technical scheme, the problem that in the prior art, a rock wool insulation board is poorin waterproof performance is solved.

Description

technical field [0001] The invention belongs to the technical field of construction, and relates to a sutured rock wool and a preparation method thereof. Background technique [0002] Rock wool insulation board is made of natural basalt as the main raw material. After high-temperature melting, it is made into inorganic fibers through high-speed centrifugal equipment. Cotton insulation products. However, due to its loose layered structure, it has low strength and high water absorption, which restricts the application of this product to a certain extent. The external wall thermal insulation rock wool thin plastering system is to paste the rock wool insulation board to the wall foundation and then hang the plastering mortar on the surface of the rock wool insulation board, and embed the alkali-resistant mesh cloth in two-thirds of the mortar to make the rock wool The insulation board, mesh cloth and mortar layer are well consolidated, which improves the strength of the rock w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/80C04B28/18C04B26/12
CPCC04B26/122C04B28/186C04B2111/00612E04B1/80C04B7/02C04B14/06C04B14/28C04B22/002C04B24/123C04B24/04C04B24/38C04B24/12C04B14/14C04B14/26C04B18/141C04B14/022
Inventor 刘江洪郝志伦
Owner 普莱斯德节能科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com