A kind of magnetic sheet toy and preparation method thereof

A magnetic sheet and toy technology, applied in the field of plastic products, can solve the problems of poor air circulation, adverse physical and mental health of children, and decreased air quality, and achieve the effects of good water absorption, improved antibacterial washability, and prevention of infection with bacteria

Active Publication Date: 2021-12-28
HANGZHOU STRONG MAGNET & ASSEMBLY CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] When the magnetic sheet toys are used for teaching, because the teaching environment of children is indoors, the air circulation is poor, and a large number of children gather together in the teaching environment, resulting in a decrease in air quality, which is not conducive to the physical and mental health of children

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnetic sheet toy and preparation method thereof
  • A kind of magnetic sheet toy and preparation method thereof
  • A kind of magnetic sheet toy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1-3

[0042] In the preparation example 1-3, the PVC paste resin is selected from the PVC paste resin whose article number is P450 sold by Rongbei (Shanghai) Chemical Technology Co., Ltd., and the kelp powder is selected from the kelp powder whose article number is 094 sold by Jiangsu Jinjie Food Co., Ltd., seaweed The powder is selected from the seaweed powder sold by Shenzhen Hengsheng Biotechnology Co., Ltd. with item number 002.

preparation example 1

[0043] Preparation example 1: (1) Dry the loofah and opal at 70°C for 2 hours, pulverize, add the opal powder into the triethanolamine solution, stir for 1 hour, take it out, dry it at 80°C, put the loofah powder in three In the methylpropanethiol solution, heat at 180°C for 2h, the mass ratio of loofah powder, opal powder and trimethylpropanethiol solution is 1:0.8:1.2, and the mass ratio of opal powder and triethanolamine solution is 1 :1;

[0044] (2) Mix PVC paste resin with kelp powder and seaweed powder evenly, heat up to 160°C, stir for 2 hours, then cool down to 100°C, add opal powder and loofah powder while stirring, continue stirring for 20 minutes, vacuumize and degas, Cool to room temperature, the preparation of PVC paste resin, seaweed part and seaweed powder is 1:0.5:0.3, the mass ratio of PVC paste resin, opal powder and loofah powder is 1:1.2:2, the particle size of seaweed powder and seaweed powder 200nm.

preparation example 2

[0045] Preparation Example 2: (1) Dry the loofah and opal at 75°C for 1.5h, pulverize, add the opal powder into the triethanolamine solution, stir for 1.5h, take it out, dry it at 85°C, put the loofah powder in In trimethylpropanethiol solution, heated at 190°C for 1.8h, the mass ratio of loofah powder, opal powder and trimethylpropanethiol solution is 1:0.9:1.3, the mass of opal powder and triethanolamine solution The ratio is 1:1.2;

[0046] (2) Mix PVC paste resin with kelp powder and seaweed powder evenly, heat up to 170°C, stir for 1.5 hours, then cool down to 150°C, add opal powder and loofah powder while stirring, continue stirring for 40 minutes, vacuumize and degas , cooled to room temperature, the preparation of PVC paste resin, seaweed part and seaweed powder is 1:0.7:0.4, the mass ratio of PVC paste resin, opal powder and loofah powder is 1:1.3:2.5, the grain size of seaweed powder and seaweed powder The diameter is 200nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a magnetic sheet toy and a preparation method thereof. The magnetic sheet toy includes a shell, a magnet and a pad in the shell, and the shell includes the following raw materials in parts by weight: 30-50 parts of resin base material, 15-20 parts of anion-modified polyester fiber, 10-20 parts PVC paste resin / opal composite material, 15-20 parts of negative ion viscose fiber, 7-13 parts of compatibilizer, 2-5 parts of antioxidant, 5-10 parts of silane coupling agent, 6-12 parts of organic antibacterial agent, 5‑15 parts flame retardant. The magnetic sheet toy of the present invention has the ability to purify the air, improve the air quality of the teaching environment for children, and has good antibacterial rate, good antibacterial effect, and good washability. After repeated washing, it still has a relatively high negative ion release and antibacterial rate. The advantages.

Description

technical field [0001] The invention relates to the technical field of plastic products, more specifically, it relates to a magnetic sheet toy and a preparation method thereof. Background technique [0002] In recent years, with the continuous improvement of people's living standards, the requirements for the quality of life have become higher and higher, and the cultivation of young children has also paid more and more attention. Most families first consider the development of the intelligence of young children. For the development of children's intelligence, the market is flooded with various kinds of educational toys, such as magnetic sheet toys. Magnetic sheet toys are assembled into different shapes by assembling various magnetic sheets. Children can use their potential imagination to assemble them into their favorite models according to the shapes of different magnetic sheets, such as houses and cars. [0003] A piece of magnetic sheet is composed of three parts: 1. S...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A63H33/26A63H33/04A63H33/08C08L23/08C08L69/00C08L55/02C08L25/12C08L51/06C08L67/02C08L1/24C08L27/06C08L79/00C08L77/00C08K13/02C08K5/13C08K5/134C08K3/36C08K3/08C08K3/22C08K3/04C08K3/38C08K5/00D01F6/92D01F1/10
CPCA63H33/26A63H33/08A63H33/046C08L23/0815C08L55/02D01F6/92D01F1/103C08L2205/16C08L2205/035C08L2205/08C08K2201/011C08K2003/2296C08K2003/085C08K2003/2213C08K2003/387C08L69/00C08L25/12C08L51/06C08L67/02C08L1/24C08L27/06C08L79/00C08L77/00C08K13/02C08K5/13C08K5/1345C08K3/36C08K3/08C08K3/22C08K3/042C08K3/38C08K5/00
Inventor 徐江洋卢海卫
Owner HANGZHOU STRONG MAGNET & ASSEMBLY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap