Production process of PC light-transmitting brick

A production process and technology of light-transmitting bricks, applied in the direction of manufacturing tools, metal processing equipment, grinding/polishing equipment, etc., can solve problems such as unsatisfactory use requirements, poor environmental comfort, dark concrete, etc., and achieve bright colors and clear outlines , pattern realistic effect

Inactive Publication Date: 2020-10-23
成都市东宇市政设施制造厂
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the production and preparation process of traditional cement products, its decorative patterns and patterns are generally prepared by concrete mixing plastic molding, etc. The impression of traditional concrete is always dull and poor in aesthetics, due to poor light transmission The comfort of the environment is poor and cannot meet the needs of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The production process of the PC transparent brick in the present embodiment comprises the following steps:

[0021] a. Prepare the mould;

[0022] b. Embed a 3mm rear sponge in the mold, fix the acrylic light-transmitting rod, and layout it into the required graphics;

[0023] c. C25 concrete is mixed with reinforcing agent and pigment powder and poured into the previously prepared mold after stirring and vibration forming process;

[0024] d. After vibration molding, put it into the steam curing workshop for 11 hours and then switch to natural curing for 14 days;

[0025] e. The cured brick embryo enters the grinding workshop, and is roughly ground with a 50-mesh abrasive disc until the surface is smooth without depressions, polished with a 500-mesh fine abrasive disc without obvious grinding marks, and polished with a polishing disc to a mirror effect.

[0026] Specifically, in a, the mold is made of steel plate resin, which is welded, polished and poured.

[0027...

Embodiment 2

[0032] The production process of the PC transparent brick in the present embodiment comprises the following steps:

[0033] a. Prepare the mould;

[0034] b. Embed a 3mm rear sponge in the mold, fix the acrylic light-transmitting rod, and layout it into the required graphics;

[0035] c. C25 concrete is mixed with reinforcing agent and pigment powder and poured into the previously prepared mold after stirring and vibration forming process;

[0036] d. After vibration molding, put it into the steam curing workshop for 12 hours and then switch to natural curing for 15 days;

[0037] e. The cured brick embryo enters the grinding workshop, and is roughly ground with a 50-mesh abrasive disc until the surface is smooth without depressions, polished with a 500-mesh fine abrasive disc without obvious grinding marks, and polished with a polishing disc to a mirror effect.

[0038] Specifically, in a, the mold is made of steel plate resin, which is welded, polished and poured.

[0039...

Embodiment 3

[0044] The production process of the PC transparent brick in the present embodiment comprises the following steps:

[0045] a. Prepare the mould;

[0046] b. Embed a 3mm rear sponge in the mold, fix the acrylic light-transmitting rod, and layout it into the required graphics;

[0047] c. C25 concrete is mixed with reinforcing agent and pigment powder and poured into the previously prepared mold after stirring and vibration forming process;

[0048] d. After vibration molding, put it into the steam curing workshop for steam curing for 14 hours and then switch to natural curing for 16 days;

[0049] e. The cured brick embryo enters the grinding workshop, and is roughly ground with a 50-mesh abrasive disc until the surface is smooth without depressions, polished with a 500-mesh fine abrasive disc without obvious grinding marks, and polished with a polishing disc to a mirror effect.

[0050] Specifically, in a, the mold is made of steel plate resin, which is welded, polished and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production process of a PC light-transmitting brick. The production process comprises the following steps of a, preparing a mold; b, embedding 3mm-thickness sponge into the mold, fixing an acrylic light-transmitting rod, and typesetting into a required pattern; c, mixing a reinforcing agent and pigment powder into c25 concrete, and pouring the mixture into a prepared moldthrough stirring and vibration molding processes; d, after vibration forming, putting into a steam curing workshop for steam curing for 12 hours, and then naturally curing for 15 days; e, the maintained green bricks entering a grinding workshop, conducting rough grinding through a 50-mesh grinding piece till the surfaces are flat and free of pits, conducting grinding through a 500-mesh fine grinding piece till no obvious grinding marks exist, and conducting polishing through a polishing piece till the mirror surface effect is achieved, specifically, in the step a, the mold is formed through welding, grinding and pouring with steel plate resin as a raw material, in the step b, the outer surface of the sponge is coated with bonding glue, and in the step c, the stirring speed of a reinforcing agent and pigment powder is 200r / min. According to the production process of the PC light-transmitting brick, a personalized solution is realized, and the production process of the PC light-transmitting brick has the advantages of bright color, vivid pattern, clear outline, good light-transmitting effect and the like.

Description

technical field [0001] The invention belongs to the technical field of cement products, and in particular relates to a production process of PC transparent bricks. Background technique [0002] Brick: Man-made small blocks for construction, divided into fired bricks (mainly clay bricks) and non-fired bricks (lime sand bricks, fly ash bricks, etc.), commonly known as bricks. Clay bricks are made of clay (including shale, coal gangue and other powders) as the main raw material, which is processed, shaped, dried and roasted with mud. [0003] In the production and preparation process of traditional cement products, its decorative patterns and patterns are generally prepared by concrete mixing plastic molding, etc. The impression of traditional concrete is always dull and poor in aesthetics, due to poor light transmission The comfort of the environment is poor and cannot meet the needs of use. Contents of the invention [0004] The object of the present invention is to provi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B28B1/087B28B11/24B24B7/22B24B9/06C04B28/00C04B111/80C04B111/82
CPCB24B7/22B24B9/06B28B1/087B28B11/245C04B28/00C04B2111/80C04B2111/82C04B16/04C04B16/12C04B2103/54
Inventor 龚小东
Owner 成都市东宇市政设施制造厂