Preparation method of material for treating caries

A caries, equation technology, applied in the field of oral materials, can solve the problems of no refining process, dietary restrictions, crystallization, etc.

Active Publication Date: 2020-10-27
合华医疗器械(绍兴)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0019] 1) Excessive ammonium fluoride is added to the feed in this process, resulting in two disadvantages: one is that the solution system is unstable, and crystals will precipitate during storage
The second is the waste of raw materials
[0020] 2) This process directly adds silver oxide solids, and the raw materials may bring uncontrollable impurities, which makes it difficult to control the impurities in the final product
[0021] 3) There is no refining process in this process, and excess ammonium fluoride, excess ammonia and excess silver cannot be removed
[0026] 3) The heating conditions of this process are reflux reaction in a closed system at 60°C, 80°C, and 120°C for 2.0h, 1.0h, and 3.0h respectively. The reaction conditions are harsh and difficult to reproduce, and qualified products cannot be produced after repeated verifications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of material for treating caries
  • Preparation method of material for treating caries
  • Preparation method of material for treating caries

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0060] Implementation case 1:

[0061] 1. Preparation of silver oxide

[0062] name Mw(g / mol) m(g) or v(ml) n (mol) Equivalence ratio Remark AgNO 3

169.87 20.400g 0.12 1 Content≥99.9% NaOH 40.00 5.326g 0.132 1.1 Content 99.15% Ultra-pure water 18.01 92ml — — —

[0063] 2. Preparation of SDF solution

[0064] name Mw(g / mol) m(g) or v(ml) n (mol) Equivalence ratio Ag 2 o

231.73 13.90g 0.05998 1 NH 4 f

37.00 4.444g 0.11999 2 NH 3

17 9.652ml ammonia water 0.13797 2.3 Ultra-pure water 18.01 20ml — —

[0065] 3. The specific operation method is as follows:

[0066] 1) Preparation of silver oxide

[0067] Add 20.400 g of silver nitrate solid into a 250 ml three-necked flask, then add ultrapure water, and stir until dissolved. Slowly add sodium hydroxide solution dropwise to the solution, control the internal temperature ≤ 40°C, dropwise is completed in ...

Embodiment example 2

[0081] 1. Preparation of silver oxide

[0082] name Mw(g / mol) m(g) or v(ml) n (mol) Equivalence ratio Remark AgNO 3

169.87 20.400g 0.12 1 Content≥99.9% NaOH 40.00 5.326g 0.132 1.1 Content 99.15% Ultra-pure water 18.01 92ml — — —

[0083] 2. Preparation of SDF solution

[0084] name Mw(g / mol) m(g) or v(ml) n (mol) Equivalence ratio Ag 2 o

231.73 13.90g 0.05998 1 NH 4 f

37.00 4.882g 0.131956 2.2 NH 3

17 10.38ml ammonia water 0.14995 2.5 Ultra-pure water 18.01 20ml — —

[0085] 3. The specific operation method is as follows:

[0086] 1) Preparation of silver oxide

[0087] Add 20.400 g of silver nitrate solid into a 250 ml three-necked flask, then add ultrapure water, and stir until dissolved. Slowly add sodium hydroxide solution dropwise to the solution, control the internal temperature ≤ 40°C, dropwise is completed in 10 minutes, measure the pH of ...

Embodiment example 3

[0101] 1. Preparation of silver oxide

[0102] name Mw(g / mol) m(g) or v(ml) n (mol) Equivalence ratio Remark AgNO 3

169.87 20.400g 0.12 1 Content≥99.9% NaOH 40.00 5.326g 0.132 1.1 Content 99.15% Ultra-pure water 18.01 92ml — — —

[0103] 2. Preparation of SDF solution

[0104] name Mw(g / mol) m(g) or v(ml) n (mol) Equivalence ratio Ag 2 o

231.73 13.90g 0.05998 1 NH 4 f

37.00 4.444g 0.11999 2 NH 3

17 9.652ml ammonia water 0.13797 2.3 Ultra-pure water 18.01 20ml — —

[0105] 3. The specific operation method is as follows:

[0106] 3. The specific operation method is as follows:

[0107] 1) Preparation of silver oxide

[0108] Add 20.400 g of silver nitrate solid into a 250 ml three-necked flask, then add ultrapure water, and stir until dissolved. Slowly add sodium hydroxide solution dropwise to the solution, control the internal temperature ≤ 40°C, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of oral cavity materials, and particularly relates to a preparation method of a material for treating caries, namely a preparation method of ammonia silver fluoride.Silver nitrate, sodium hydroxide, ammonium fluoride and ammonia water are used as raw materials, a new thought is provided for preparing an ammonia silver fluoride solution, refining of the preparation process is achieved through gradient heating, excessive raw materials are removed, and generation and precipitation of by-products are avoided. The preparation process is economical, environment-friendly and stable, and can be used for preparing the ammonia silver fluoride solution with few impurities, few by-products and long-term placement stability.

Description

technical field [0001] The invention belongs to the field of oral materials, and in particular relates to a method for preparing a material for treating dental caries, that is, a method for preparing silver ammonium fluoride. Background technique [0002] Caries is a disease in which the hard tissue of the tooth body is chronically and progressively destroyed under the influence of various factors mainly including bacteria. [0003] Caries prevention generally adopts the following measures: [0004] (1) Strengthen oral health care and control dental plaque [0005] (2) Use of fluoride [0006] (3) Dietary restrictions [0007] Among them, fluoride is the most effective caries prevention material proved by scientific research and clinical practice. Its caries-inhibiting effect is mainly achieved by locally strengthening the tooth structure, inhibiting the demineralization process and enhancing remineralization. There are three ways to use fluoride for caries prevention: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G5/02A61K6/80
CPCA61K6/80C01G5/006C01G5/02
Inventor 洪亮张蕊路浩军邵荣郭旺明田力
Owner 合华医疗器械(绍兴)有限公司