A technology of non-woven fabrics and surgical gowns, which is applied in the field of wear-resistant non-woven materials for surgical gowns, can solve the problems of patient safety hazards, poor wear resistance of surgical gowns, and loss of protective ability of surgical gowns, etc., to achieve enhanced structural strength, The effect of increasing the degree of wear resistance

Inactive Publication Date: 2020-10-27
安庆德迪康医疗科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Surgical gowns should not easily produce dandruff or dust during wearing and use, because the fluff and particles falling off the surface of the surgical gown are easy to carry pathogens and cause harm to the safety of patients; at the same time, the surgical gown should have strong traction and wear resistance Performance, because the rupture and wear of the clothes will make the pathogens come into direct contact with the skin of the medical staff, making the surgical gowns lose their protective ability
However, the wear resistance of commonly used surgical gowns is poor and cannot meet the needs of full population

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A wear-resistant non-woven fabric material for surgical gowns, its raw materials include by weight: 50 parts of polyester fiber, 60 parts of polypropylene, 10 parts of wear-resistant agent, 1 part of antibacterial agent, 1 part of flame retardant, antistatic agent 0.5 parts, 5-parts of nano barium sulfate;

[0015] The wear-resistant agent is specifically molybdenum sulfide-free and wear-resistant resin;

[0016] The polyester fiber is PET or polyester;

[0017] The antibacterial agent is a nanometer metal antibacterial agent;

[0018] The flame retardant is diethyl ethyl phosphate efficient organophosphorus flame retardant;

[0019] The preparation method of a wear-resistant non-woven fabric material for surgical gowns is as follows: S1: Heat and melt raw materials: 50-60 parts of polyester fiber, 60-80 parts of polypropylene, 10-20 parts of wear-resistant agent, and 1 part of antibacterial agent are selected. -3 parts, 1-2 parts of flame retardant, 0.5-1.5 parts of...

Embodiment 2

[0021] A wear-resistant non-woven fabric material for surgical gowns, its raw materials include by weight: 55 parts of polyester fiber, 70 parts of polypropylene, 15 parts of wear-resistant agent, 2 parts of antibacterial agent, 1 part of flame retardant, antistatic agent 1 part, 7 parts of nano barium sulfate;

[0022] The wear-resistant agent is specifically molybdenum sulfide-free and wear-resistant resin;

[0023] The polyester fiber is PET or polyester;

[0024] The antibacterial agent is a nanometer metal antibacterial agent;

[0025] The flame retardant is diethyl ethyl phosphate efficient organophosphorus flame retardant;

[0026] The preparation method of a wear-resistant non-woven fabric material for surgical gowns is as follows: S1: Heat and melt raw materials: 50-60 parts of polyester fiber, 60-80 parts of polypropylene, 10-20 parts of wear-resistant agent, and 1 part of antibacterial agent are selected. -3 parts, 1-2 parts of flame retardant, 0.5-1.5 parts of a...

Embodiment 3

[0028] A wear-resistant non-woven fabric material for surgical gowns, its raw materials include by weight: 60 parts of polyester fiber, 80 parts of polypropylene, 20 parts of wear-resistant agent, 3 parts of antibacterial agent, 2 parts of flame retardant, antistatic agent 1.5 parts, 10 parts of nano barium sulfate;

[0029] The wear-resistant agent is specifically molybdenum sulfide-free and wear-resistant resin;

[0030] The polyester fiber is PET or polyester;

[0031] The antibacterial agent is a nanometer metal antibacterial agent;

[0032] The flame retardant is diethyl ethyl phosphate efficient organophosphorus flame retardant;

[0033] The preparation method of a wear-resistant non-woven fabric material for surgical gowns is as follows: S1: Heat and melt raw materials: 50-60 parts of polyester fiber, 60-80 parts of polypropylene, 10-20 parts of wear-resistant agent, and 1 part of antibacterial agent are selected. -3 parts, 1-2 parts of flame retardant, 0.5-1.5 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant non-woven fabric material for an operating coat. According to raw materials, the wear-resistant non-woven fabric material for the operating coat comprises, byweight, 50-60 parts of polyester fibers, 60-80 parts of polypropylene, 10-20 parts of wear-resistant agents, 1-3 parts of antibacterial agents, 1-2 parts of flame retardant, 0.5-1.5 parts of antistatic agents and 5-10 parts of nano barium sulfate. According to the wear-resistant non-woven fabric material for the operating coat, the wear-resistant agents are added into the preparation raw materialsof non-woven fabric, due to the addition of the wear-resistant agents, the wear resistance of the non-woven fabric is enhanced, the wear-resistant degree is increased, and the wear-resistant agents are molybdenum-sulfide-free and wear-resistant resin, have the effect of enhancing the structural strength and also have the effect of increasing the wear-resistant degree of the surface of the non-woven fabric. The flame retardant, the antibacterial agents, the antistatic agents and the barium sulfate are added to the raw materials, and therefore the prepared non-woven fabric material can have theeffects of anti-bacteria, flame retardance, static elasticity prevention, high glossiness and the like.

Description

technical field [0001] The invention belongs to the technical field of nonwoven fabrics, and in particular relates to a wear-resistant nonwoven fabric material for surgical gowns. Background technique [0002] The fabrics used in surgical gowns are medical shielding fabrics, which mainly focus on barrier properties, including the ability to prevent the penetration of liquids and microorganisms. Because medical staff will inevitably come into contact with the blood and body fluids of patients during medical rescue, the blood and body fluids of patients may often carry various pathogens. Surgical gowns should not easily produce dander or dust during wearing and use, because the fluff and particles falling off the surface of the surgical gown are easy to carry pathogens and cause harm to the safety of patients; at the same time, the surgical gown should have strong traction and wear resistance Performance, because the rupture and wear of the clothes will cause direct contact b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H3/005D04H3/147D01F8/06D01F8/14D01F1/10D01F1/07D01F1/09A41D31/08A41D31/26A41D31/30A41D31/04