Ultrathin graphite composite bipolar plate base material capable of being quickly cold-pressed and molded and preparation method thereof
A technology of cold forming and bipolar plates, which is applied in the direction of fuel cells, battery electrodes, electrochemical generators, etc., can solve the problems of short service life, failure to meet the requirements of large quantities, low strength, etc., and achieve excellent product performance, Efficient production efficiency and the effect of improving electrical conductivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] The present invention provides a thin graphite composite bipolar plate base material A rapid cold forming, the material composition and weight percentage:
[0024] 150 mesh to 200 mesh natural flake graphite powder 40%
[0025] 100 mesh to 150 mesh graphite worms 20%
[0026] 200 mesh to 300 mesh graphite worms 15%
[0027] 23% of a synthetic resin
[0028] Surfactant 2%
[0029] In this embodiment, the graphite material is added to the dry mixer according to the composition and mixed, and the like graphite material mixed surfactant further added after mixing, the mixer is started and dried in vacuo apparatus, evacuated with stirring to ensure mixing after the powder was dried powder was completely removed, the dried mixed powder of 300 mesh was added milled granulator, the material through a 300 mesh screen, the operation is repeated until all the powder through a 300 mesh sieve. The three-dimensional mesh good graphite powder mixer, then added with a f...
Example Embodiment
[0031] Example 2
[0032] The present invention provides a thin graphite composite bipolar plate materials A preparation yl rapid cold forming, the material composition and weight percentage:
[0033] 150 mesh to 200 mesh natural flake graphite powder 50%
[0034] 100 mesh to 150 mesh graphite worms 15%
[0035] 200 mesh to 300 mesh graphite worms 10%
[0036] 23% of a synthetic resin
[0037] Surfactant 2%.
[0038] In this embodiment, the graphite material is added to the dry mixer according to the composition and mixed, and the like graphite material mixed surfactant further added after mixing, the mixer is started and dried in vacuo apparatus, evacuated with stirring to ensure mixing after the powder was dried powder was completely removed, the dried mixed powder of 300 mesh was added milled granulator, the material through a 300 mesh screen, the operation is repeated until all the powder through a 300 mesh sieve. The three-dimensional mesh good graphite powder mixer, then ad...
Example Embodiment
[0040] Example 3
[0041] The present invention provides a thin graphite composite bipolar plate materials A preparation yl rapid cold forming, the material composition and weight percentage:
[0042] 150 mesh to 200 mesh natural flake graphite powder 60%
[0043] 100 mesh to 150 mesh graphite worms 10%
[0044] 200 mesh to 300 mesh graphite worms 10%
[0045] 19% of a synthetic resin
[0046] Surfactant 1%.
[0047] In this embodiment, the graphite material is added to the dry mixer according to the composition and mixed, and the like graphite material mixed surfactant further added after mixing, the mixer is started and dried in vacuo apparatus, evacuated with stirring to ensure mixing after the powder was dried powder was completely removed, the dried mixed powder of 300 mesh was added milled granulator, the material through a 300 mesh screen, the operation is repeated until all the powder through a 300 mesh sieve. The three-dimensional mesh good graphite powder mixer, then ad...
PUM
Property | Measurement | Unit |
---|---|---|
Conductivity | aaaaa | aaaaa |
Resistance | aaaaa | aaaaa |
Flatness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap