A kind of activation method of proton exchange membrane fuel cell

A proton exchange membrane and activation method technology, which is applied in the activation field of proton exchange membrane fuel cells, can solve problems such as low output power density, unutilized fuel, unfavorable electrode reaction, etc., achieve shortened activation time, save fuel, and reduce dissolution Effect

Active Publication Date: 2021-12-03
FAW JIEFANG AUTOMOTIVE CO
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Existing activation methods usually use a single current density or a single voltage for activation. Although the activation time is shortened, the activation is not complete, which is not conducive to the thorough progress of the electrode reaction, resulting in low output power density, and at the same time, the fuel is not properly charged. use, waste resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of activation method of proton exchange membrane fuel cell
  • A kind of activation method of proton exchange membrane fuel cell
  • A kind of activation method of proton exchange membrane fuel cell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A kind of activation method of proton exchange membrane fuel cell is provided in the present embodiment, comprises the following steps:

[0044] 1) Make the active area 25cm 2 The CCM is assembled into a single cell, the anode is fed with hydrogen, the stoichiometric ratio is 1.1, and no humidification is used; the cathode is fed with 100% humidified nitrogen, and the stoichiometric ratio is 2.0. LSV test is carried out after 45 minutes, the voltage scanning range is 0.1-0.6V, the scanning speed is 2mV / s, and the preset value of the hydrogen permeation current in the LSV test curve is 2mA / cm 2 .

[0045] 2) When the tested hydrogen permeation current value is greater than the preset value of the current density, disconnect the gas source, switch the cathode gas to oxygen, the stoichiometric ratio is 2.0, and the stoichiometric ratio of pure hydrogen at the anode is 1.1.

[0046] 3) Set the gradient output voltage, the first step is 0.85V, the activation time is 3min, ...

Embodiment 2

[0050] A kind of activation method of proton exchange membrane fuel cell is provided in the present embodiment, comprises the following steps:

[0051] 1) Make the active area 25cm 2 The CCM is assembled into a single cell, the anode is fed with hydrogen, the stoichiometric ratio is 1.5, no humidification is used, the cathode is fed with 100% humidified nitrogen, and the stoichiometric ratio is 2.0. LSV test is carried out after 120 minutes, the voltage scanning range is 0.1-0.6V, the scanning speed is 10mV / s, and the preset value of the hydrogen permeation current in the LSV test curve is 5mA / cm 2 .

[0052] 2) The cathode gas is switched to air, the stoichiometric ratio of air is 2.0, and the stoichiometric ratio of pure hydrogen at the anode is 1.5.

[0053] 3) Set the gradient output voltage, the first step is 0.85V, the activation time is 5min, cycle 2 times, the second step is 0.6V, the activation time is 30min, cycle 4 times, the third step is 0.5V, the activation tim...

Embodiment 3

[0057] A kind of activation method of proton exchange membrane fuel cell is provided in the present embodiment, comprises the following steps:

[0058] 1) Make the active area 25cm 2 The CCM is assembled into a single cell, the anode is fed with hydrogen, the stoichiometric ratio is 1.5, and the cathode is fed with 100% humidified nitrogen, and the stoichiometric ratio is 2.0. When the battery operating temperature reaches 75 ° C, the cathode and anode gas are fed for 100 minutes before LSV Test, the voltage scanning range is 0.1-0.6V, the scanning speed is 5mV / s, and the preset value of the hydrogen permeation current in the LSV test curve is 4mA / cm 2 .

[0059] 2) The cathode gas is switched to oxygen, the stoichiometric ratio is 2.0, and the stoichiometric ratio of pure hydrogen at the anode is 1.5.

[0060] 3) Set the gradient output voltage, the first step is 0.85V, the activation time is 4min, cycle 3 times, the second step is 0.6V, the activation time is 25min, cycle ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an activation method of a proton exchange membrane fuel cell, the activation method comprising the following steps: (1) passing hydrogen gas into the anode of the assembled battery, nitrogen gas into the cathode, and then performing an LSV test, and the tested hydrogen permeation The current value is higher than the preset value of the current density, disconnect the gas source; (2) then switch the cathode gas to oxygen or air, and maintain the stoichiometric ratio of the cathode gas to 2 and the stoichiometric ratio of the anode gas hydrogen to 1.1-1.5 , carry out activation treatment, and then carry out polarization curve test, if two consecutive polarization curves overlap after activation, the activation is completed; wherein, the activation treatment includes 3 steps of constant voltage activation treatment performed sequentially. The method provided by the present invention, the introduction of the hydrogen permeation current test process can make the catalyst, electrolyte, and Nafion three interfaces in the battery reach the best equilibrium state, shorten the activation time, and can also greatly improve the chemical stability of the proton membrane in the battery. Extend battery life.

Description

technical field [0001] The invention relates to the field of fuel cells, in particular to an activation method for a proton exchange membrane fuel cell. Background technique [0002] Proton exchange membrane fuel cell (PEMFC) is considered to be one of the best green energy sources in the 20th century due to its advantages of high energy conversion efficiency, fast start-up at low temperature, no pollution, good durability, and high specific power. . The membrane electrode (Membrane Electrode Assembly, MEA) is the core component of the fuel cell. The membrane electrode includes an anode gas diffusion layer, an anode frame, an anode catalyst layer, a proton membrane, a cathode catalyst layer, a cathode frame, and a cathode gas diffusion layer. Membrane electrode is the site of heterogeneous material transport and electrochemical reaction, which determines the performance, life and cost of proton exchange membrane fuel cells. A high-performance battery should have smooth hyd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M8/04223H01M8/04537
CPCH01M8/04223H01M8/04582Y02E60/50
Inventor 于力娜朱雅男唐柳张克金杨帅
Owner FAW JIEFANG AUTOMOTIVE CO