Environment-friendly brick with good forming effect and preparation method thereof

An environmentally friendly brick and external admixture technology, which is applied in the field of environmentally friendly materials to achieve the effect of compact structure and high strength

Inactive Publication Date: 2020-11-20
安徽省希泰环保科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The molding effect and heat resistance of the environmental protection bricks in the prior art cannot meet the needs of actual use, so it is urgent to develop an environmental protection brick with a good molding effect to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An environmentally friendly brick with good molding effect, its raw materials include: 60 parts of fine iron tailings, 30 parts of coarse iron tailings, 20 parts of construction solid waste crushing powder, 8 parts of 325# cement, and liquid external admixture 2 parts, 2 parts water.

[0020] The liquid external admixture is prepared according to the following process: 10 parts by weight of carbamate, 3 parts of butyl acrylate and 3.5 parts of p-toluenesulfonic acid are evenly mixed, then the temperature is raised to 70 ° C, kept for 30 minutes, and then 4.5 parts are added Mix 1 part polypropylene, 6 parts silane coupling agent KH-550, 6 parts diatomaceous earth and 4 parts aluminum polyphosphate, stir at 750r / min for 20min, adjust the pH to 4, then raise the temperature to 70°C and keep it warm for 1h , after washing, dry in vacuum at 70°C to constant weight, cool to room temperature, then add 6 parts of sepiolite powder, 6 parts of nano-aluminum hydroxide, 3.5 parts ...

Embodiment 2

[0023] An environmentally friendly brick with good molding effect, its raw materials include by weight: 50 parts of fine iron tailings, 40 parts of coarse iron tailings, 15 parts of construction solid waste crushed powder, 10 parts of 325# cement, and liquid external admixture 1 part, 3 parts water.

[0024] The liquid external admixture is prepared according to the following process: 8 parts by weight of carbamate, 5 parts of butyl acrylate and 2 parts of p-toluenesulfonic acid are evenly mixed, and then the temperature is raised to 80 ° C, kept for 20 minutes, and then added with 6 1 part of polypropylene, 4 parts of silane coupling agent KH-550, 9 parts of diatomaceous earth and 2 parts of aluminum polyphosphate, mix well, stir at 850r / min for 10min, adjust the pH to 5.0, then raise the temperature to 65°C, keep warm for 1.5 h, after washing, dry in vacuum at 65°C to constant weight, cool to room temperature, then add 8 parts of sepiolite powder, 3 parts of nano-aluminum hy...

Embodiment 3

[0027] An environmentally friendly brick with good molding effect, its raw materials include by weight: 70 parts of fine iron tailings, 20 parts of coarse iron tailings, 25 parts of construction solid waste crushing powder, 6 parts of 325# cement, and liquid external admixture 3 parts, 1 part water.

[0028] The liquid external admixture is prepared according to the following process: 12 parts by weight of carbamate, 1 part of butyl acrylate and 5 parts of p-toluenesulfonic acid are uniformly mixed, and then the temperature is raised to 60 ° C, kept for 40 minutes, and then added with 3 1 part of polypropylene, 8 parts of silane coupling agent KH-550, 3 parts of diatomaceous earth and 6 parts of aluminum polyphosphate were mixed evenly, stirred at 650r / min for 30min, adjusted to pH 3.5, then heated to 75°C, and kept at 0.5 h, after washing, dry in vacuum at 75°C to constant weight, cool to room temperature, then add 4 parts of sepiolite powder, 9 parts of nano-aluminum hydroxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly brick with a good forming effect. The environment-friendly brick is prepared from the following raw materials in parts by weight: 50-70 parts of fine iron tailings, 20-40 parts of coarse iron tailings, 15-25 parts of building solid waste crushed powder, 6-10 parts of No.325 cement, 1-3 parts of a liquid additive and 1-3 parts of water. The inventionfurther provides a preparation method of the environment-friendly brick with the good forming effect. During preparation, the coarse iron tailings are hard in texture and high in strength and can replace aggregate. The preparation method comprises the following steps: proportionally adding the raw materials, stirring, adding the liquid admixture, stirring, and pressing. The formed product is compact in structure, free of surface cracks and free of dispersion phenomenon when being taken out of the mold, and the appearance meets the production standard. The compression resistance is 34.2 MP.

Description

technical field [0001] The invention belongs to the technical field of environment-friendly materials, and in particular relates to an environment-friendly brick with good molding effect and a preparation method thereof. Background technique [0002] Manufactured by using fly ash, coal slag, coal gangue, tailings slag, chemical slag or natural sand, sea mud, industrial waste, waste incineration slag, etc. (one or more of the above raw materials) as the main raw materials without high-temperature calcination A new type of wall material is called environmental protection brick. [0003] The molding effect and heat resistance of the environmental protection bricks in the prior art cannot meet the needs of actual use, so it is urgent to develop an environmental protection brick with a good molding effect to solve the problems in the prior art. Contents of the invention [0004] The object of the present invention is to provide an environmentally friendly brick with good moldi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B40/02
CPCC04B28/02C04B40/024C04B2111/00017C04B2201/50C04B18/12C04B18/16C04B24/12C04B24/045C04B24/20C04B24/2611C04B24/42C04B14/08C04B22/16C04B14/042C04B22/06C04B22/0013
Inventor 王炜
Owner 安徽省希泰环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap