Polymer gel, monodisperse polymer microsphere with particle size distribution and its preparation and application
A particle size distribution and polymer technology, which is applied in drilling compositions, chemical instruments and methods, etc., can solve the problems of unsatisfactory on-site implementation effect, increased cost of polymer microspheres, unsatisfactory and other problems, and achieves low cost, The effect of improved dispersion and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0055]This embodiment provides a monodisperse polymer microsphere with particle size distribution for control and drive, wherein the preparation method of the monodisperse polymer microsphere with particle size distribution for control and drive comprises the following steps:
[0056] (1) Preparation of polymer gel:
[0057] Add successively the tap water of 99 parts by weight, the salt-resistant polymer (molecular weight is 8,000,000, degree of hydrolysis is 12%), the salicylaldehyde of 0.3 part by weight and the ammonium sulfate of 0.1 part by weight in tool plugged jar , after high-speed stirring to make it mix and dissolve, the resulting mixture was placed in a drying oven whose temperature was adjusted to 80° C., and the polymer gel was prepared after gelling, and its viscoelastic modulus G” was 8500 mPa·s.
[0058] (2) Preparation of monodisperse polymer microspheres with particle size distribution for adjusting and driving:
[0059] In the colloid mill, add 20 parts by...
Embodiment 2
[0061] This embodiment provides a monodisperse polymer microsphere with particle size distribution for control and drive, wherein the preparation method of the monodisperse polymer microsphere with particle size distribution for control and drive comprises the following steps:
[0062] (1) Preparation of polymer gel:
[0063] Add successively the tap water of 99 parts by weight, the salt-resistant polymer (molecular weight is 8,000,000, degree of hydrolysis is 12%), the salicylaldehyde of 0.3 part by weight and the ammonium sulfate of 0.1 part by weight in tool plugged jar , after high-speed stirring to make it mix and dissolve, the resulting mixture was placed in a drying oven whose temperature was adjusted to 80° C., and the polymer gel was prepared after gelling, and its viscoelastic modulus G” was 8500 mPa·s.
[0064] (2) Preparation of monodisperse polymer microspheres with particle size distribution for adjusting and driving:
[0065] In the colloid mill, add 20 parts b...
Embodiment 3
[0068] This embodiment provides a monodisperse polymer microsphere with particle size distribution for control and drive, wherein the preparation method of the monodisperse polymer microsphere with particle size distribution for control and drive comprises the following steps:
[0069] (1) Preparation of polymer gel:
[0070] Add successively the tap water of 99 parts by weight, the salt-resistant polymer (molecular weight is 8,000,000, degree of hydrolysis is 12%), the salicylaldehyde of 0.3 part by weight and the ammonium sulfate of 0.1 part by weight in tool plugged jar , after high-speed stirring to make it mix and dissolve, the resulting mixture was placed in a drying oven whose temperature was adjusted to 80° C., and the polymer gel was prepared after gelling, and its viscoelastic modulus G” was 8500 mPa·s.
[0071] (2) Preparation of monodisperse polymer microspheres with particle size distribution for adjusting and driving:
[0072] Add 30 parts by weight of the polym...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com