Epoxy resin composition capable of being quickly thickened and fiber reinforced composite material semi-cured material thereof

A reinforced composite material and epoxy resin technology, applied in the field of fiber-reinforced thermosetting resin composite materials, can solve the problems of inability to meet the environmental protection requirements of composite parts, poor unsaturated SMC strength, low impact strength, etc., and achieve low production costs , high production efficiency, good mechanical effect

Inactive Publication Date: 2020-12-04
ADESSO ADVANCED MATERIALS WUXI CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

SMC is mostly obtained by glass fiber reinforced unsaturated resin, but glass fiber reinforced unsaturated SMC has poor strength and low impact strength, which cannot meet the requirements of light weight and high strength for material replacement, and unsaturated resin is made of styrene. Solvents cannot meet the environmental protection requirements for low VOC emissions of composite parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin composition capable of being quickly thickened and fiber reinforced composite material semi-cured material thereof
  • Epoxy resin composition capable of being quickly thickened and fiber reinforced composite material semi-cured material thereof
  • Epoxy resin composition capable of being quickly thickened and fiber reinforced composite material semi-cured material thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] The raw materials of the rapid thickening epoxy resin composition are added to the mixing device in order according to the weight and mixed evenly. First, 100 parts of the low-viscosity liquid bisphenol A epoxy resin, 0.75 parts of the defoamer, and 0.75 parts of the sizing agent are sequentially added , 6 parts of curing agent dicyandiamide 100S, 4 parts of organic urea accelerator UR500 are added to the mixing device and mixed evenly to obtain a fast-curing epoxy resin component; then 3 parts of epoxy thickener DETA are added to the mixing device and mixed evenly, That is, a rapidly thickening epoxy resin composition is obtained.

[0055] The quick-thickening epoxy resin composition is put into a drying room at 35°C for 20hrs, and the epoxy thickener amine-based active hydrogen cross-links with the epoxy functional group of the epoxy resin to increase the viscosity of the epoxy resin composition. Complete to obtain semi-solid semi-cured epoxy resin.

[0056] The thic...

Embodiment 2～10

[0061] The preparation method of the rapidly thickening epoxy resin composition, the preparation of the curing thickening, and the resin-cured casting body are the same as in Example 1, and the weight of each component of the rapidly thickening epoxy resin composition is shown in Table 1; The characteristics of the thickened epoxy resin composition, the properties of the resin-cured cast body and the Tg test are the same as in Example 1, and the test results are shown in Table 2.

[0062] As shown in Table 1 and Table 2, the initial viscosity at 25°C after mixing of the rapidly thickening epoxy resin composition of Examples 1-10 is 5-50 pa.s, and the epoxy resin composition can be controlled at 30-60°C Viscosity ≤ 1000mPa.s, low initial viscosity of epoxy resin is conducive to infiltration of reinforcing fibers; aging at 30-70°C for 1-200hrs reacts and thickens, so that the viscosity of the epoxy resin composition at 70°C increases to 10-5000Pa.s, The thickened semi-cured epox...

Embodiment 11

[0064] The rapidly thickening epoxy resin composition mixed in Example 3 is poured into the scraping groove of the SMC sheet machine, and the epoxy resin is evenly coated on the upper and lower carrier films with a scraper to form an epoxy resin paste film; Surface density is 300g / m 2 ELG recycled chopped carbon fiber felt is placed on the lower epoxy resin paste film, and then the upper epoxy resin film is covered on the surface of the carbon fiber felt. After extrusion and exhaust, the epoxy resin is fully infiltrated into the carbon fiber to form a chopped carbon fiber. Felt resin composite sheet, and then rolled and packaged; the chopped carbon fiber felt resin composite sheet that is rolled and packaged is cured in a drying room at 35°C for 20hrs, so that the epoxy resin composition is reacted and thickened to obtain a chopped carbon fiber felt prepreg . The epoxy chopped carbon fiber felt prepreg is prepared, the carbon fiber felt is infiltrated with epoxy resin, the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an epoxy resin composition capable of rapid thickening and a fiber reinforced composite material semi-cured material thereof, the epoxy resin composition is composed of rapid curing epoxy resin and an epoxy thickening agent containing active hydrogen, and the initial viscosity of the epoxy resin composition capable of rapid thickening at 25 DEG C is 5-100 Pa.s. The epoxy resin is low in viscosity and beneficial to infiltration of reinforced fibers, amino reactive hydrogen of an epoxy thickener and epoxy functional groups are subjected to a rapid cross-linking reaction at the temperature of 20-70 DEG C for thickening, the viscosity is 2,000-500,000 Pa.s at the temperature of 25 DEG C after thickening, and the epoxy resin fiber reinforced composite semi-cured materialstable in storage is formed. The invention also discloses a fiber reinforced composite material semi-cured material such as a chopped fiber sheet molding compound, a chopped fiber felt prepreg, a continuous fiber or fabric prepreg and the like, which is prepared by infiltrating a plurality of reinforced fibers into the epoxy resin composition and carrying out a thickening reaction at 20-70 DEG Cfor 1-200 hours.

Description

technical field [0001] The invention relates to the application field of fiber-reinforced thermosetting resin composite materials, in particular to a rapidly thickening epoxy resin composition and a fiber-reinforced composite material prepreg. Background technique [0002] Prepreg is a composition of resin matrix and reinforcement made by impregnating continuous fibers or fabrics with resin matrix under strictly controlled conditions. It is an intermediate material for manufacturing composite materials and can be directly used to manufacture various composite material components. Thermosetting resin matrix prepregs are currently mainly divided into two processes: solution impregnation method and hot melt method. The production process of prepreg prepared by solution impregnation method uses a large amount of organic solvents to dissolve resin, which is harmful to production personnel and the environment. The produced prepregs have residual organic solvents, and VOC emissions...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L71/00C08K5/17C08K7/14C08K7/06C08K7/10C08J5/04C08J5/24
CPCC08L63/00C08K5/17C08J5/043C08J5/042C08J5/24C08L2205/025C08L2205/03C08J2363/00C08J2463/00C08J2471/00C08K7/14C08K7/06C08K7/10C08J5/0405
Inventor 白灵阮长杰南江琨崔国新庞兴功
Owner ADESSO ADVANCED MATERIALS WUXI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap