A technology of high-grade cement and preparation process, applied in the field of cement production, can solve the problems of uneven raw meal composition, high power consumption, low heat consumption, etc., and achieve the effect of improving the utilization rate of energy and time and improving the quality.

Active Publication Date: 2020-12-18
福建三明南方水泥有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dry method refers to the method of drying and grinding the raw materials at the same time, or first drying and grinding the raw material powder and then feeding it into the dry kiln to calcinate the clinker. The main advantage of the dry method is low heat consumption, and the disadvantage is The composition of the raw material is not easy to be uniform, and the power consumption is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of high-grade cement based on modified fluorgypsum
  • Preparation process of high-grade cement based on modified fluorgypsum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Below in conjunction with accompanying drawing and embodiment the present invention will be further described:

[0023] like figure 1 , figure 2 Shown, in the present invention, provide a kind of high grade cement preparation technology based on modified fluorogypsum, comprising:

[0024] Step S1, crushing and grinding the cement raw materials, and blending them into a mixture in proportion;

[0025] Step S2, drying the mixture and adding it to a raw material mill, starting the raw material mill to grind the mixture into cement raw meal powder;

[0026] Step S3, pour the cement raw meal powder into a mixer for mixing; the mixer includes: a feed port 1, a tank body 2, a discharge port 3, a first screw shaft 4, a second screw shaft 5, paddles 6. The first reducer 7, the second reducer 8, the first motor 9, the second motor 10, the first photoelectric encoder 11 and the second photoelectric encoder 12, the feed port 1 is set in the tank 2 directly above the rear end, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of high-grade cement based on modified fluorgypsum, which relates to the technical field of cement production, and comprises the following steps: crushingand grinding cement raw materials, and proportionally mixing into a mixture; starting a raw material mill to grind into cement raw material powder; pouring the cement raw material powder into the stirrer for stirring; collecting angular velocity data of two motors of the stirrer, and solving a difference value according to the angular velocity data of the two motors when the fluctuation values ofthe angular velocities of the two motors are both smaller than a first preset value; when the difference value is smaller than a second preset value, judging that the raw material powder is calcinedinto cement clinker after being uniformly stirred; and grinding the cement clinker, the modified fluorgypsum and the admixture to preset fineness to obtain cement. According to the method, the mixinguniformity degree of the cement raw material powder is represented by solving the angular speed difference of the two motors after the stability of the angular speed is solved, calcination in the following steps is facilitated, the utilization rate of energy and time can be effectively increased, and the quality of produced cement is improved.

Description

technical field [0001] The invention relates to the technical field of cement production, in particular to a process for preparing high-grade cement based on modified fluorogypsum. Background technique [0002] Cement is a powdery hydraulic inorganic gelling material. It can be mixed with water to form a slurry. It can be hardened in the air or better hardened in water, and can firmly bind sand, stone and other materials together. Early lime and The mixture of volcanic ash is very similar to the modern lime pozzolanic cement. It is used to bond the concrete made of crushed stone. After hardening, it not only has high strength, but also can resist the erosion of fresh water or salt water. It has been used as an important glue for a long time. Concrete material, widely used in civil construction, water conservancy, national defense and other projects. [0003] Cement production can be divided into dry method (including semi-dry method) and wet method (including semi-wet metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/04
CPCC04B7/04
Inventor 付道阔俞小飞罗华民肖俊生周建中杨文锦李星煌
Owner 福建三明南方水泥有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap