Organic silicon modified acrylic pressure-sensitive adhesive and preparation method thereof

A technology of acrylic pressure-sensitive adhesive and silicone, which is applied in the field of pressure-sensitive adhesives, can solve the problems of affecting the performance of acrylic pressure-sensitive adhesives, poor emulsification effect, and bursting, and achieves improved temperature resistance, no bursting, and Effect of gel, performance improvement

Inactive Publication Date: 2020-12-29
安徽富印新材料股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the process of producing water-based acrylic pressure-sensitive adhesives, poor emulsification effect, bursting and gelation often occur, which affect the performance of acrylic pressure-sensitive adhesives.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A silicone-modified acrylic pressure-sensitive adhesive prepared from the following raw materials in parts by weight: 8 parts of acrylic acid, 160 parts of butyl acrylate, 160 parts of isobutyl acrylate, 19 parts of styrene, and 4 parts of hydroxyethyl acrylate , 0.8 parts of benzoyl peroxide, 4 parts of dilauroyl peroxide, 22 parts of hydroxyethyl methacrylate, 4 parts of vinyl silicone oil, 0.75 parts of hydrogen-containing silicone oil, 0.02 parts of Custer platinum catalyst, 15 parts of ammonia water, 220 parts of deionized water.

[0019] A preparation method of silicone-modified acrylic pressure-sensitive adhesive, the steps are as follows:

[0020] (1) Weigh acrylic acid, butyl acrylate, isobutyl acrylate, styrene, hydroxyethyl acrylate, benzoyl peroxide, dilauroyl peroxide, hydroxyethyl methacrylate, vinyl silicone oil in parts by weight , Hydrogen-containing silicone oil, platinum catalyst, ammonia water, deionized water;

[0021] (2) Put one-third of the wei...

Embodiment 2

[0025] A silicone-modified acrylic pressure-sensitive adhesive prepared from the following raw materials in parts by weight: 7 parts of acrylic acid, 170 parts of butyl acrylate, 170 parts of isobutyl acrylate, 18 parts of styrene, and 5 parts of hydroxyethyl acrylate , 0.7 parts of benzoyl peroxide, 5 parts of dilauroyl peroxide, 12 parts of hydroxyethyl methacrylate, 5 parts of vinyl silicone oil, 0.5 parts of hydrogen-containing silicone oil, 0.03 parts of Custer platinum catalyst, 14 parts of ammonia water, 250 parts of deionized water.

[0026] A preparation method of silicone-modified acrylic pressure-sensitive adhesive, the steps are as follows:

[0027] (1) Weigh acrylic acid, butyl acrylate, isobutyl acrylate, styrene, hydroxyethyl acrylate, benzoyl peroxide, dilauroyl peroxide, hydroxyethyl methacrylate, vinyl silicone oil in parts by weight , Hydrogen-containing silicone oil, platinum catalyst, ammonia water, deionized water;

[0028] (2) Put one-third of the weig...

Embodiment 3

[0032] A silicone-modified acrylic pressure-sensitive adhesive prepared from the following raw materials in parts by weight: 9 parts of acrylic acid, 150 parts of butyl acrylate, 150 parts of isobutyl acrylate, 20 parts of styrene, and 3 parts of hydroxyethyl acrylate , 1.0 parts of benzoyl peroxide, 3 parts of dilauroyl peroxide, 25 parts of hydroxyethyl methacrylate, 3 parts of vinyl silicone oil, 1.5 parts of hydrogen-containing silicone oil, 0.01 parts of Custer platinum catalyst, 17 parts of ammonia water, 200 parts of deionized water.

[0033] A preparation method of silicone-modified acrylic pressure-sensitive adhesive, the steps are as follows:

[0034] (1) Acrylic acid, butyl acrylate, isobutyl acrylate, styrene, hydroxyethyl acrylate, benzoyl peroxide, dilauroyl peroxide, hydroxyethyl methacrylate, vinyl silicone oil are weighed in parts by weight , Hydrogen-containing silicone oil, platinum catalyst, ammonia water, deionized water;

[0035] (2) Put one-third of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an organic silicon modified acrylic pressure-sensitive adhesive and a preparation method thereof. The adhesive is prepared from the following raw materials in parts by weight: 7-9 parts of acrylic acid, 150-170 parts of butyl acrylate, 150-170 parts of isobutyl acrylate, 18-20 parts of styrene, 3-5 parts of hydroxyethyl acrylate, 0.7-1.0 part of benzoyl peroxide, 3-5 parts of dilauroyl peroxide, 12-25 parts of hydroxyethyl methylacrylate, 3-5 parts of vinyl silicone oil, 0.5-1.5 parts of hydrogen-containing silicone oil, 0.01-0.03 part of platinum catalyst, 14-17 parts of ammonia water, and 200-250 parts of deionized water. The preparation method disclosed by the invention is good in emulsifying effect, free of implosion and gel phenomena, and capable of ensuring that the prepared acrylic pressure-sensitive adhesive is good in comprehensive performance. The acrylic pressure-sensitive adhesive has high temperature resistance and aging resistance, meanwhile, the phenomena of implosion and gel are avoided in the preparation process, and it can be guaranteed that the prepared acrylic pressure-sensitive adhesive is good in comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of pressure-sensitive adhesives, in particular to an organosilicon-modified acrylic pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] At present, the materials used for surface protection film include acrylic, epoxy resin, polyurethane, silicone materials and hybrid materials, etc. Among them, acrylic and silicone have their own advantages, and acrylic pressure-sensitive adhesive has moderate performance and low price; silicone pressure-sensitive adhesive Sensitive glue has good temperature resistance and aging resistance, but it is more expensive. [0003] At present, it is known that the important factors affecting the performance of acrylic pressure-sensitive adhesives include the influence of glass transition temperature, the influence of polymer molecular weight and its molecular weight distribution, the influence of polar groups, the influence of cross-linking,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J11/08C08F220/18C08F220/06C08F212/08C08F220/20C08G77/44
CPCC08G77/44C08L2201/08C09J11/08C09J133/066C08F220/1804C08L83/10C08F220/06C08F212/08C08F220/20
Inventor 陈会杰
Owner 安徽富印新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap