Pearl white ceramic product and preparation method thereof

A technology of ceramic products and pearl white, applied in clay products, other household utensils, applications, etc., can solve the problems of ceramics not beautiful enough, poor antibacterial performance, etc., to achieve the purification of air, better texture, and beneficial to the human body the healthy effect of

Inactive Publication Date: 2021-01-01
福建省德化县晖德陶瓷有限公司
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides pearl white ceramic products and a preparation method thereof, mainly to solve the problems that the ceramics produced by the existing technology are not beautiful enough, and the antibacterial properties are not good enough to meet people’s requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pearl white ceramic product and preparation method thereof
  • Pearl white ceramic product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] refer to Figure 1-2 , a pearl white ceramic product, including a green body and a glaze layer, and the glaze layer is coated on the outer surface of the green body, wherein the green body includes the following components in parts by mass: 4 parts of titanium dioxide, 15 parts of kaolin, 7 parts of neodymium ore, dysprosium 8 parts of ore, 18 parts of rare earth, 20 parts of alumina, 14 parts of zirconia, 13 parts of bentonite, 25 parts of quartz, 18 parts of feldspar; the glaze layer includes: 70 parts of kaolin, 20 parts of frit, 11 parts of lithium fluoride, pearl 40 parts of powder, 16 parts of talc powder, 10 parts of zinc oxide, 14 parts of zirconium silicate, 15 parts of barium carbonate, 15 parts of quartz, and 20 parts of nano-platinum powder, which can be released by adding titanium dioxide, neodymium ore, dysprosium ore and rare earth ore. Far-infrared rays release heat, and then eliminate the pathological process of inflammation through the response of neur...

Embodiment 2

[0047] refer to Figure 1-2 , a pearl white ceramic product, including a green body and a glaze layer, and the glaze layer is coated on the outer surface of the green body, wherein the green body includes the following components in parts by mass: 5 parts of titanium dioxide, 18 parts of kaolin, 9 parts of neodymium ore, dysprosium 10 parts of ore, 20 parts of rare earth, 24 parts of alumina, 17 parts of zirconia, 15 parts of bentonite, 20 parts of quartz, 16 parts of feldspar; the glaze layer includes: 60 parts of kaolin, 16 parts of frit, 8 parts of lithium fluoride, pearl 35 parts of powder, 14 parts of talc powder, 8 parts of zinc oxide, 12 parts of zirconium silicate, 13 parts of barium carbonate, 13 parts of quartz, and 18 parts of nano-platinum powder, which can be released by adding titanium dioxide, neodymium ore, dysprosium ore and rare earth ore. Far-infrared rays release heat, and then eliminate the pathological process of inflammation through the response of neuro...

Embodiment 3

[0060] refer to Figure 1-2 , a pearl white ceramic product, including a green body and a glaze layer, and the glaze layer is coated on the outer surface of the green body, wherein the green body includes the following components in parts by mass: 8 parts of titanium dioxide, 20 parts of kaolin, 11 parts of neodymium ore, dysprosium 14 parts of ore, 22 parts of rare earth, 26 parts of alumina, 18 parts of zirconia, 16 parts of bentonite, 18 parts of quartz, 13 parts of feldspar; the glaze layer includes: 50 parts of kaolin, 20 parts of frit, 11 parts of lithium fluoride, pearl 40 parts of powder, 16 parts of talc powder, 10 parts of zinc oxide, 10 parts of zirconium silicate, 15 parts of barium carbonate, 15 parts of quartz, and 15 parts of nano-platinum powder, which can be released by adding titanium dioxide, neodymium ore, dysprosium ore and rare earth ore. Far-infrared rays release heat, and then eliminate the pathological process of inflammation through the response of ne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramic production, and discloses a pearl white ceramic product, which comprises a green body and a glaze layer, the glaze layer is coated on the outersurface of the green body, the green body comprises, by mass, 3-12 parts of titanium dioxide, 10-30 parts of kaolin, 5-15 parts of neodymium ore, 8-16 parts of dysprosium ore, 10-30 parts of rare earth, 10-30 parts of aluminum oxide, 10-18 parts of zirconium oxide, 12-18 parts of bentonite, 15-25 parts of quartz and 12-18 parts of feldspar. The invention also provides a preparation method of the pearl white ceramic product. The preparation method comprises the following steps: S1, ball-milling, and weighing the raw materials; and S2, stirring and mixing. The whiteness and the semitransparent degree of the pearl ceramic prepared in the invention are greatly improved, the pearls are added into the raw materials, the ceramic prepared by calcining is better in texture and strong in antibacterial ability, subsequent ligands can be prevented from chapping during drying, and refined mud cakes are convenient to transport and store.

Description

technical field [0001] The invention relates to the technical field of ceramic production, in particular to pearl white ceramic products and a preparation method thereof. Background technique [0002] Due to the continuous development of ceramic science and technology. And the market's increasing demand for new ceramic products forces ceramic companies to continuously develop new products, and must consider the problems and impacts of product changes on the rational organization of the production process. In order to enhance adaptability, ceramic enterprises not only need to vigorously improve the application level of science and technology and the research ability of new products, and constantly update products, but also must adopt advanced production organization methods such as plan review method, group technology and multi-variety mixed flow production. [0003] Pearl white porcelain is one of the relatively rare varieties of Dehua white porcelain. The whiteness of pear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/13C04B33/04C04B33/34C03C8/02C03C8/18C03C8/20C04B41/86
CPCC04B33/16C04B33/13C04B33/04C04B33/34C03C8/02C03C8/20C03C8/18C04B41/86C04B41/5022C04B2235/3232C04B2235/3224C04B2235/3217C04B2235/3244C04B2235/3463C04B2235/661
Inventor 曾宪城王建国
Owner 福建省德化县晖德陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com