Preparation method of polyethylene modified high-strength composite alloy material

A polyethylene modification and composite alloy technology, which is applied in the field of polyethylene modified high-strength composite alloy material preparation, can solve problems such as poor effect of polyethylene materials, prevent the decline of physical and mechanical properties, improve molecular weight and relative viscosity, reduce The effect of density

Inactive Publication Date: 2021-01-22
深圳中轩生态环境科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for preparing a polyethylene-modified high-strength composite alloy material to solve the problem of poor effect of current polyethylene materials in the above-mentioned background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyethylene modified high-strength composite alloy material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for preparing a polyethylene-modified high-strength composite alloy material, comprising the following raw materials in parts by weight: 130 parts of modified polyethylene masterbatch, 55 parts of grafted polyethylene resin, 35 parts of inorganic filler, and 4 parts of chain extender , 6 parts of coupling agent, 4 parts of compatibilizer and 2 parts of antioxidant 1076.

[0022] In this embodiment, the modified polyethylene masterbatch includes the following raw materials in parts by weight: 45 parts of polyethylene, 2 parts of quartz powder, 15 parts of polyvinyl chloride, and 5 parts of polycarbonate. The specific steps for making the modified polyethylene masterbatch The method is as follows: weighing each raw material in parts by weight for later use, melting and blending each raw material, extruding and granulating to obtain a modified polyethylene masterbatch.

[0023] Specifically, the nylon 6 resin is a resin with a melting point of 225°C.

[0024] It ...

Embodiment 2

[0033] A method for preparing a polyethylene-modified high-strength composite alloy material, comprising the following raw materials in parts by weight: 120 parts of modified polyethylene masterbatch, 60 parts of grafted polyethylene resin, 30 parts of inorganic filler, and 3 parts of chain extender , 5 parts of coupling agent, 3 parts of compatibilizer and 2 parts of antioxidant 1076.

[0034] In this embodiment, the modified polyethylene masterbatch includes the following raw materials in parts by weight: 40 parts of polyethylene, 2 parts of quartz powder, 20 parts of polyvinyl chloride, and 10 parts of polycarbonate. The specific steps for making the modified polyethylene masterbatch The method is as follows: weighing each raw material in parts by weight for later use, melting and blending each raw material, extruding and granulating to obtain a modified polyethylene masterbatch.

[0035] Specifically, the nylon 6 resin is a resin with a melting point of 225°C.

[0036] It...

Embodiment 3

[0045] A method for preparing a polyethylene-modified high-strength composite alloy material, comprising the following raw materials in parts by weight: 150 parts of modified polyethylene masterbatch, 50 parts of grafted polyethylene resin, 30 parts of inorganic filler, and 5 parts of chain extender , 8 parts of coupling agent, 5 parts of compatibilizer and 3 parts of antioxidant 1076.

[0046]In this embodiment, the modified polyethylene masterbatch includes the following raw materials in parts by weight: 50 parts of polyethylene, 1 part of quartz powder, 20 parts of polyvinyl chloride, and 3 parts of polycarbonate. The specific steps for making the modified polyethylene masterbatch The method is as follows: weighing each raw material in parts by weight for later use, melting and blending each raw material, extruding and granulating to obtain a modified polyethylene masterbatch.

[0047] Specifically, the nylon 6 resin is a resin with a melting point of 225°C.

[0048] It is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of environment-friendly materials, in particular to a preparation method of a polyethylene modified high-strength composite alloy material, which comprisesthe following raw materials: modified polyethylene master batch, nylon 6 resin, inorganic filler, a chain extender, a coupling agent, a compatilizer and an antioxidant 1076. The polyethylene modifiedhigh-strength composite alloy material disclosed by the invention is high in shore A hardness, high in maximum bearing strength and high in elongation at break, so that the polyethylene modified high-strength composite alloy material has relatively high elongation at break and relatively high tensile strength at the same time, and the requirements of processing technologies such as injection molding, extrusion and wiredrawing are met; the impact toughness of the composite material is improved by the nylon 6 resin, so that the composite material has balanced physical and mechanical properties,and the molecular weight and relative viscosity of nylon can be effectively improved by adopting the chain extender, so that the defect that the physical and mechanical properties are reduced due tomolecular chain breakage in the nylon regeneration process can be effectively prevented.

Description

technical field [0001] The invention relates to the technical field of environmental protection materials, in particular to a method for preparing a polyethylene-modified high-strength composite alloy material. Background technique [0002] Polyethylene has incomparable wear resistance, impact resistance, chemical resistance, and self-lubricating properties compared to other engineering plastics. It is widely used in various fields of the national economy, especially in wear-resistant transportation, equipment linings, and various mechanical parts. With unique advantages, the development and application of its products have broad prospects, and the development of new application fields is attracting people's attention. However, ordinary polyethylene materials have weak maximum compressive strength, poor impact and compression resistance, thick wall thickness, many consumables, and high cost. Contents of the invention [0003] The purpose of the present invention is to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L27/06C08L69/00C08L51/06C08K3/36C08K3/26C08K3/34C08K5/134C08K13/02C08K7/08C08K13/04C08K7/14
CPCC08L23/06C08K2201/014C08K2003/265C08L2205/035C08L2205/025C08L27/06C08L69/00C08L51/06C08K3/36C08K3/26C08K3/34C08K5/1345C08K13/02C08K7/08C08K13/04C08K7/14
Inventor 李玉顺潘新宇杨文
Owner 深圳中轩生态环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap