LYOCELL fiber containing ginseng/ganoderma lucidum/poria cocos/aloe and preparation method thereof

A technology of Poria and ginseng, applied in the field of fiber, can solve the problem of difficult to meet the diversified needs of LYOCELL fiber, and achieve the effects of improving uniform stability, optimizing the preparation process and improving quality

Inactive Publication Date: 2021-02-02
BESTEE MATERIAL (TSINGTAO) CO LTD +2
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, with the widespread application of LYOCELL fiber and the enhancement of people's awareness of health care, the functions of the existing LYOCELL fiber are difficult to meet the diverse needs of the public for LYOCELL fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • LYOCELL fiber containing ginseng/ganoderma lucidum/poria cocos/aloe and preparation method thereof
  • LYOCELL fiber containing ginseng/ganoderma lucidum/poria cocos/aloe and preparation method thereof
  • LYOCELL fiber containing ginseng/ganoderma lucidum/poria cocos/aloe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0043] (1) Take 4 parts of ginseng, 2 parts of Ganoderma lucidum, 7 parts of Poria cocos, 5 parts of aloe, 2 parts of dopamine, and 30 parts of active protective agent according to the following parts by weight;

[0044] (2) The ginseng, ganoderma lucidum, poria cocos and aloe weighed in the step (1) were washed successively with clear water for 3 times, then dried at a temperature of 45°C for 20 minutes, then crushed and passed through a 40-mesh sieve to obtain mixed powder;

[0045] (3) The mixed powder obtained in step (2) is subjected to supercritical CO 2 The extraction method is used for extraction, the extraction conditions are extraction pressure 30MPa, temperature 40°C, flow rate 27L / h, time 120min, to obtain the extract;

[0046] (4) Add the extract and dopamine in the step (3) into the active protective agent, stir at a stirring rate of 100r / min for 20min, and stir evenly to obtain a modifier.

preparation example 2

[0048] (1) Take 4.5 parts of Ginseng, 2.5 parts of Ganoderma lucidum, 8.5 parts of Poria cocos, 6 parts of Aloe Vera, 2.5 parts of dopamine, and 33 parts of active protective agent according to the following parts by weight;

[0049] (2) The ginseng, ganoderma lucidum, poria cocos and aloe weighed in the step (1) were washed successively with clear water for 3 times, then dried at a temperature of 45°C for 25 minutes, then crushed and passed through a 40-mesh sieve to obtain mixed powder;

[0050] (3) The mixed powder obtained in step (2) is subjected to supercritical CO 2 The extraction method is used for extraction, the extraction conditions are extraction pressure 30MPa, temperature 40°C, flow rate 27L / h, time 140min, to obtain the extract;

[0051] (4) Add the extract and dopamine in the step (3) into the active protective agent, stir at a stirring rate of 100r / min for 25min, and stir evenly to obtain a modifier.

preparation example 3

[0053] (1) Take 5 parts of ginseng, 3 parts of Ganoderma lucidum, 10 parts of poria cocos, 7 parts of aloe, 3 parts of dopamine, and 36 parts of active protective agent according to the following parts by weight;

[0054] (2) The ginseng, ganoderma lucidum, poria cocos and aloe weighed in the step (1) were washed successively with clear water for 3 times, then dried at a temperature of 45°C for 30 minutes, then crushed and passed through a 40-mesh sieve to obtain mixed powder;

[0055] (3) The mixed powder obtained in step (2) is subjected to supercritical CO 2 The extraction method is used for extraction, the extraction conditions are extraction pressure 30MPa, temperature 40°C, flow rate 27L / h, time 160min, to obtain the extract;

[0056] (4) Add the extract and dopamine in the step (3) into the active protective agent, stir at a stirring rate of 100r / min for 30min, and stir evenly to obtain a modifier.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses LYOCELL fiber containing ginseng / ganoderma lucidum / poria cocos / aloe and a preparation method thereof, and relates to the technical field of fiber. According to the technical scheme, the LYOCELL fiber containing the ginseng / the ganoderma lucidum / the poria cocos / the aloe is prepared by spinning modifier and LYOCELL spinning solution according to the mass ratio of 1-2:8. The modifier is prepared from the following raw materials in parts by weight: 4-5 parts of the ginseng, 2-3 parts of the ganoderma lucidum, 7-10 parts of the poria cocos, 5-7 parts of the aloe, 2-3 parts of dopamine, and 30-36 parts of an active protective agent. The preparation method includes the steps of S1, preparing original fluid; S2, preparing the spinning solution; and S3, spinning. The LYOCELLfiber containing the ginseng / the ganoderma lucidum / the poria cocos / the aloe disclosed has the advantages of plant (natural) antibiosis, moistening, repairing and strong adhesiveness; and the preparation method disclosed has the advantage of endowing the LYOCELL fiber with functionality.

Description

technical field [0001] The invention relates to the fiber field, more specifically, it relates to a LYOCELL fiber containing ginseng / ganoderma lucidum / poria cocos / aloe vera and a preparation method thereof. Background technique [0002] LYOCELL fiber is made by dissolving wood (mainly eucalyptus) pulp in organic solvent N-methylmorpholine-N-oxide, and spinning through dry spraying and wet spinning; and the resulting cellulose fiber has dry strength and wet strength High uniformity, good washing stability, excellent hygroscopicity and soft hand feeling. Therefore, LYOCELL fiber is favored by consumers and widely used in various fields due to its advantages such as wide source of raw materials, simple spinning process, recyclable solvent, and excellent fiber performance. [0003] Existing reference can be made to the patent document that the authorized announcement number is CN103556248B, which discloses a kind of bamboo charcoal LYOCELL fiber, which is to carry out surface m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/02D01F1/10
CPCD01F1/10D01F1/103D01F2/02
Inventor 黄效华甄丽穆伟华
Owner BESTEE MATERIAL (TSINGTAO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap