Composite-layer pavement brick and preparation method thereof

A composite layer and pavement brick technology, which is applied to roads, roads, pavement details, etc., can solve the problems of poor bearing capacity, short service life, and easy wear and tear of composite pavement bricks, and achieve good anti-skid performance, low overall cost, Not easy to fall off effect

Inactive Publication Date: 2021-02-05
GUANGDONG GAITEQI NEW MATERIAL TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this application is to provide a composite layer pavement brick and its preparation method, aiming to solve the problem that the composite layer pavement bricks in the prior art are all prepared in one piece, resulting in poor bearing capacity of the composite pavement brick and easy wear and tear on the surface. The problem of short life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite-layer pavement brick and preparation method thereof
  • Composite-layer pavement brick and preparation method thereof
  • Composite-layer pavement brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The first aspect of the embodiment of the present application provides a method for preparing a composite layer pavement brick, comprising the following steps:

[0026] S01. Provide the surface layer raw material mixture and the bottom raw material mixture of the composite layer pavement bricks respectively;

[0027] S02. Provide a mold, and spray concrete additives on the inner surface of the bottom of the mold to obtain an additive layer;

[0028] S03. Place the surface layer raw material mixture on the surface of the auxiliary agent layer, and perform vacuum pressing to obtain a pre-surface layer;

[0029] S04. Opening grooves on the surface of the pre-surface layer away from the auxiliary agent layer, placing gravel in the mold and performing pressing treatment to obtain the pre-connection layer;

[0030] S05. Lay the bottom layer raw material mixture on the surface of the pre-connection layer and carry out vacuum exhaust treatment to form a pre-bottom layer, and o...

Embodiment 1

[0087] Composite layer pavement brick and its preparation method

[0088] Composite ply brick

[0089] The composite ply pavement brick comprises a surface layer and a bottom layer, wherein the surface layer raw material mixture includes the following raw materials in parts by weight:

[0090]

[0091] Control the mass ratio of the added water to the cement of the surface layer to be 0.28:1; and / or,

[0092] The bottom raw material mixture comprises the raw materials of following parts by weight:

[0093]

[0094] Control the mass ratio of the added water to the bottom cement to be 0.16:1;

[0095] Among them, the cement is selected from Portland cement with a strength > 42.5MPa; the average particle size of the admixture is 5-30 μm; the average particle size of the fine aggregate is 2-4.75mm; the average particle size of the coarse aggregate is 4.75- 25mm; the diameter of the steel fiber is 0.1-0.25mm, and the length is 10-20mm.

[0096] A kind of preparation me...

Embodiment 2

[0106] Composite layer pavement brick and its preparation method

[0107] Composite ply brick

[0108] The composite ply pavement brick comprises a surface layer and a bottom layer, wherein the surface layer raw material mixture includes the following raw materials in parts by weight:

[0109]

[0110] Control the mass ratio of the added water to the cement of the surface layer to be 0.32:1;

[0111] The bottom raw material mixture comprises the raw materials of following parts by weight:

[0112]

[0113] Control the mass ratio of added water to bottom cement to be 0.2:1;

[0114] Among them, the cement is selected from Portland cement with a strength > 42.5MPa; the average particle size of the admixture is 5-30 μm; the average particle size of the fine aggregate is 2-4.75mm; the average particle size of the coarse aggregate is 4.75- 25mm; the diameter of the steel fiber is 0.1-0.25mm, and the length is 10-20mm.

[0115] A kind of preparation method of composite...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of pavement bricks, and provides a preparation method of a composite layer pavement brick, which comprises the following steps: preparing an assistant layer on the inner surface of a mold, and sequentially preparing a surface layer, a connecting layer and a bottom layer; wherein an auxiliary agent layer is formed, a hydration reaction of the concrete incontact with the mold surface is delayed, and the setting time of the concrete in contact with the mold surface is prolonged, so that cement paste on the surface of the concrete in contact with the mold surface is flushed away in the subsequent flushing treatment, and the composite-layer pavement brick with the rough surface is obtained. then the surface abrasion resistance of the composite-layerpavement brick is provided, meanwhile, the surface layer and the bottom layer are connected through the connecting layer containing the gravels, the interface bonding force of the surface layer and the bottom layer can be increased, and the bearing capacity of the composite-layer pavement brick is improved; the preparation method is simple, the combination degree of the surface layer and the stratum can be improved, it is guaranteed that the surface layer and the bottom layer are not prone to falling off, meanwhile, the contractility of the material is reduced, and the composite-layer pavement brick material is high in bearing capacity, good in anti-skid performance, good in durability and suitable for wide application.

Description

technical field [0001] The application belongs to the technical field of pavement bricks, and in particular relates to a composite layer pavement brick and a preparation method thereof. Background technique [0002] Pavement bricks are a common type of brick in my country, also known as pavement bricks, which are usually widely used in sidewalks, residential areas, and squares. It is made of cement, gravel, and sand as raw materials. It is shaped by vibration, and the surface is cut into stripes or squares. It looks like granite. Some are elegant and rough, and some are romantic and soft. [0003] The production of concrete pavement bricks also has a certain history. The early concrete pavement bricks were relatively thin, and their strength, wear resistance and flexural resistance were relatively low, so their service life was short. The concrete pavement bricks used in some cities in our country are poured with plastic molds. Although this kind of pavement bricks are brig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B40/06C04B41/72B28B13/02B28B3/00E01C11/24E01C5/04C04B111/20
CPCB28B3/006B28B13/02B28B13/0295C04B28/04C04B40/06C04B41/5323C04B41/72C04B2111/00362C04B2111/00612C04B2111/2038C04B2201/50C04B2201/52E01C5/04E01C11/24C04B14/14C04B18/08C04B18/141C04B14/00C04B2103/54C04B2103/302C04B2103/304C04B2103/0068C04B2103/12C04B2103/65C04B2103/601C04B14/48
Inventor 刘福财崔海波肖敏张信祯李斌黄贺明黎浩胡翔
Owner GUANGDONG GAITEQI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap