A super-hydrophobic, ceramic tile technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of poor antifouling effect of silicone antifouling agents, and achieve good antifouling effect and hardness High, low impact effect

Inactive Publication Date: 2021-02-05
HUNAN CHENLI NEW MATERIAL CO LTD
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for matte bricks with more pores on the brick surface, the antifouling effect of silicone antifouling agent is relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A superhydrophobic fluorosilicone ceramic antifouling agent, which uses perfluorinated hydrogen-containing polymethylhydrogensiloxane as a base resin, amino-substituted cage polysilsesquioxane and polyisocyanate as a crosslinking catalyst , Nano-alumina is the reinforcing filler, superhydrophobic fluorosilicone resin cured at room temperature, its specific formula is composed of perfluorinated hydrogen-containing polymethylhydrosiloxane (hydrogen content 1.2%, viscosity 60mPa· s) 15.0%, octaaminophenyl POSS 6.0%, 4,4'-dicyclohexylmethane diisocyanate 1.0%, nano-alumina 6.0% (particle size 13nm, specific surface area 200±20m 2 / g), polyhydroxypolysiloxane (viscosity 100mPa·s, hydroxyl content 3.6%) 4.0%, 3-fluorophenylboronic acid 3.0%, petroleum ether (boiling range 90-120°C).

[0022] The preparation method of the superhydrophobic fluorosilicone resin ceramic antifouling agent described in the present embodiment is as follows:

[0023] At room temperature, add perfluo...

Embodiment 2

[0025] A superhydrophobic fluorosilicone ceramic antifouling agent, which uses perfluorinated hydrogen-containing polymethylhydrogensiloxane as a base resin, amino-substituted cage polysilsesquioxane and polyisocyanate as a crosslinking catalyst , Nano-alumina is used as a reinforcing filler, a superhydrophobic fluorosilicone resin cured at room temperature, its specific formula by mass is: perfluorinated hydrogen-containing polymethylhydrogen siloxane (viscosity 20mPa·s, hydrogen content 1.63 %) 20.0%, octa-3-aminopropyl POSS 3.0%, hexamethylene diisocyanate 2.0%, nano-alumina (particle size 10nm, specific surface area 230±20m 2 / g) 3.0%, polyhydroxy polysiloxane (viscosity 200 mPa·s, hydroxyl content 2.1%) 8.0%, 4-n-propylphenylboronic acid 1.0%, D40 solvent 63.0%.

[0026] The preparation method of the superhydrophobic fluorosilicone resin ceramic antifouling agent described in the present embodiment is as follows:

[0027] At room temperature, add perfluorinated hydrogen-...

Embodiment 3

[0029] A superhydrophobic fluorosilicone ceramic antifouling agent, which uses perfluorinated hydrogen-containing polymethylhydrogensiloxane as a base resin, amino-substituted cage polysilsesquioxane and polyisocyanate as a crosslinking catalyst , Nano-alumina is used as a reinforcing filler, superhydrophobic fluorosilicone resin cured at room temperature, and its specific formula is composed of perfluorinated hydrogen-containing polymethylhydrogen siloxane (viscosity 30mPa·s, hydrogen content 1.48 %) 17.0%, octa-3-aminopropyl POSS 4.0%, isophorone diisocyanate 1.5%, nano-alumina (18nm, specific surface area 170±20m 2 / g) 3.5%, polyhydroxypolysiloxane (viscosity 80mPa·s, hydroxyl content 3.9%) 6.0%, 3-methoxyphenylboronic acid 2.0%, D40 solvent 36.0%, kerosene 15.0%, n-heptane 15.0% %.

[0030] The preparation method of the superhydrophobic fluorosilicone resin ceramic antifouling agent described in the present embodiment is as follows:

[0031] At room temperature, add perf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a super-hydrophobic antifouling ceramic tile which is characterized in that the surface of the ceramic tile is coated with a super-hydrophobic fluorosilicone resin ceramic antifouling agent by about 1-2g / cm < 2 >, and the super-hydrophobic antifouling ceramic tile is obtained. According to the super-hydrophobic fluorosilicone resin ceramic antifouling agent, perfluoro hydrogen-containing polymethylhydrosiloxane is used as matrix resin, amino-substituted polyhedral oligomeric silsesquioxane and polyisocyanate are used as cross-linking catalysts, and nano aluminum oxideis used as reinforcing filler so that the super-hydrophobic fluorosilicone resin antifouling agent which is cured at normal temperature is generated. The super-hydrophobic antifouling ceramic tile issmall in glossiness influence, excellent in hydrophobicity and good in antifouling effect.

Description

technical field [0001] The invention relates to a ceramic brick, in particular to a super-hydrophobic antifouling brick, and belongs to the technical field of hydrophobic and antifouling bricks. [0002] technical background [0003] During the firing process, the ceramic tiles will absorb pollutants due to the pores and tiny cracks remaining on the brick or glazed surface. The current ultra-clean and bright ceramic tiles can solve the above problems by adding antifouling agents to fill the holes during polishing. At present, the best anti-fouling for ultra-clean and bright tiles at home and abroad is nano-anti-fouling, that is, a layer of nano-scale protective layer with special protective function and stable structure is formed on the edge of polished tiles and glazed tiles. It is mainly used to upgrade ceramics. The anti-fouling performance of polished tiles is known as a revolutionary breakthrough in anti-fouling technology in the building ceramics industry, and it also g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/08C09D183/04C09D175/04C09D5/16C09D7/61C09D7/63
CPCC08K2003/2227C08K2201/011C08L2205/025C08L2205/03C08L2312/00C09D5/1675C09D5/1687C09D5/34C09D183/08C08L83/08C08L83/04C08K5/29C08K3/22C08K5/55
Inventor 朱佳媚
Owner HUNAN CHENLI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap