Preparation method of far-infrared health-care textile

A far-infrared health care and textile technology, applied in the field of textiles, can solve the problems of poor fabric style and durability, and achieve the effect of simple method and easy-to-obtain raw materials

Inactive Publication Date: 2021-03-12
无锡瑞升纺织服饰有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its fabric style and durability are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method of far-infrared health care textiles, said preparation method comprising the following steps:

[0021] Step 1. Take ferromagnesia tourmaline and prepare tourmaline powder by wet grinding method in a planetary ball mill. The wet grinding process parameters are as follows: the ratio of ball to material is 1:3, absolute ethanol is used as the grinding solvent, and agate balls are used as the ball milling medium , the filling rate is 80%;

[0022] Step 2. The prepared tourmaline powder is dried and passed through a 300 mesh sieve;

[0023] Step 3. Get 2 parts by mass of tourmaline powder and 0.1 parts by mass of nano powder TiO after sieving in step 2 2 , 0.3 parts by mass of nano-powder SnO 2 , 0.2 parts by mass La(NO 3 ) 3 ·6H 2 O, 0.5 parts by mass of tea seed oil, 0.3 parts by mass of zinc borate and 20 parts by mass of deionized water were stirred at a temperature of 30° C. for 30 min at a speed of 300 r / min to obtain a mixed solution;

[002...

Embodiment 2

[0027] A preparation method of far-infrared health care textiles, said preparation method comprising the following steps:

[0028] Step 1. Take ferromagnesia tourmaline and prepare tourmaline powder by wet grinding method in a planetary ball mill. The wet grinding process parameters are as follows: the ratio of ball to material is 1:4, absolute ethanol is used as the grinding solvent, and agate balls are used as the ball milling medium , the filling rate is 80%;

[0029] Step 2. The prepared tourmaline powder is dried and passed through a 500 mesh sieve;

[0030] Step 3. Get 4 parts by mass of tourmaline powder, 0.5 parts by mass of nano-powder TiO after sieving in step 2 2 , 0.5 parts by mass of nano-powder SnO 2 , 0.4 parts by mass La(NO 3 ) 3 ·6H 2 O, 0.7 parts by mass of tea seed oil, 0.6 parts by mass of zinc borate and 30 parts by mass of deionized water were stirred at a temperature of 40° C. for 60 min at a speed of 400 r / min to obtain a mixed solution;

[0031] ...

Embodiment 3

[0034] A preparation method of far-infrared health care textiles, said preparation method comprising the following steps:

[0035] Step 1. Take ferromagnesia tourmaline and prepare tourmaline powder by wet grinding method in a planetary ball mill. The wet grinding process parameters are as follows: the ratio of ball to material is 1:4, absolute ethanol is used as the grinding solvent, and agate balls are used as the ball milling medium , the filling rate is 80%;

[0036] Step 2. The prepared tourmaline powder is dried and passed through a 400 mesh sieve;

[0037] Step 3. Get 3 parts by mass of tourmaline powder, 0.4 parts by mass of nano-powder TiO after step 2 sieves 2 , 0.3 parts by mass of nano-powder SnO 2 , 0.3 parts by mass La(NO 3 ) 3 ·6H 2 O, 0.6 parts by mass of tea seed oil, 0.5 parts by mass of zinc borate and 25 parts by mass of deionized water were stirred at a temperature of 35° C. for 45 min at a speed of 400 r / min to obtain a mixed solution;

[0038] Step...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a far-infrared health-care textile, and belongs to the technical field of textiles. The preparation process comprises the following steps of grinding iron-magnesium tourmaline into powder; drying the tourmaline powder; taking the tourmaline powder, nano powder TiO2, nano powder SnO2, La (NO3) 3.6 H2O, tea seed oil, zinc borate and deionized water andperforming stirring to obtain a mixed solution; enabling PA slices to be dried in a vacuum drying oven, and carrying out melt spinning through a double-screw extrusion injection molding machine; andimmersing the spun yarns obtained in the step 4 into the mixed solution prepared in the step 3, drying, and spinning the spun yarns into a spinning product. The method is simple, raw materials are easy to obtain, PA is subjected to injection molding spinning and then immersed into the mixed solution of tourmaline powder and La (NO3) 3.6 H2O, the tourmaline powder and La (NO3) 3.6 H2O are combinedto achieve the combined synergistic effect, then drying treatment is conducted, finally spinning is conducted on the spun yarns to form the spinning product, and the finally prepared product has the far infrared health care function.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of far-infrared health-care textiles. Background technique [0002] The human body emits infrared rays all the time, and absorbs infrared rays at the same time. Infrared rays belong to the category of electromagnetic waves and are radiations with strong thermal effects. The wavelengths are before red light and microwaves. They are generally divided into three bands: near-infrared light, mid-infrared light and far-infrared light. Usually, the wavelength range of 4~400 μm in infrared is defined as far infrared, and 90% of the wavelengths are between 8~14 μm. Far-infrared can activate human cells, excrete old and dead cells or endow regeneration ability, enhance cell energy, enhance cell function and vitality, etc. [0003] The far-infrared health-care fabric belongs to a kind of functional textile, which has the functions of keeping warm and ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/80D06M11/46D06M11/65D06M13/224D06M13/203D06M101/34
CPCD06M11/46D06M11/65D06M11/80D06M13/203D06M13/2246D06M2101/34
Inventor 乔拂晓
Owner 无锡瑞升纺织服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com