Halogen-free flame-retardant scratch-resistant antibacterial polypropylene material as well as preparation method and application thereof

An antibacterial polypropylene and scratch-resistant technology, applied in the field of modified polypropylene materials and their preparation, can solve the problems of adding a large amount of flame retardant, harmful to human body, and adding a large amount of halogen-free flame retardant, so as to improve the resistance to Scratch effect, lower flame retardant dosage, effect of excellent antibacterial properties

Active Publication Date: 2021-03-26
WANHUA CHEM GRP CO LTD +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Halogen-based flame retardants are usually added to traditional flame-retardant polypropylene materials, but the gas produced during the combustion process is harmful to the human body and causes serious environmental pollution, which does not meet environmental protection requirements
Therefore, the requirements for halogen-free flame-retardant polypropylene materials are increasing day by day. However, the amount of halogen-free flame retardants added to polypropylene materials is large, which has a great impact on the overall performance of the product. It is difficult to meet the flame-retardant requirements. Performance conditions, while maintaining the rigidity and toughness of the product at an optimal level
[0004] With the aging of China's population and people's high-end demand for bathrooms, smart toilets, as a growing daily necessities, are increasingly appearing in people's daily lives. Non-toxic polypropylene, which requires polypropylene materials to have excellent flame retardancy and scratch resistance, while ordinary flame retardant formulations generally cannot achieve excellent scratch resistance; at the same time, based on hygiene requirements, the antibacterial properties of toilet seats are becoming more and more popular. Pay attention to
[0005] The existing technology for the modification of polypropylene has made some progress in flame retardancy, scratch resistance, and antibacterial properties, but all of them are mainly researched and developed in a single technical field, and at the same time solve the flame retardancy, scratch resistance, and antibacterial properties. still have difficulties
[0006] CN109575430A discloses a halogen-free flame-retardant polypropylene material, which adds zirconium phosphate and expanded graphite to the formula to achieve a synergistic flame-retardant effect, but the expansion-type flame retardant added in the formula reaches 10-20 parts, and the flame retardant The overall addition is still more

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame-retardant scratch-resistant antibacterial polypropylene material as well as preparation method and application thereof
  • Halogen-free flame-retardant scratch-resistant antibacterial polypropylene material as well as preparation method and application thereof
  • Halogen-free flame-retardant scratch-resistant antibacterial polypropylene material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0053] Preparation of Zirconium Phosphonate 1#

[0054] Accurately weigh 20.3g of zirconium oxychloride and dissolve it in 200mL of deionized water to make an aqueous solution of zirconium oxychloride, and accurately weigh 21g of glyphosate and dissolve it in 3000mL of deionized water to make an aqueous solution of glyphosate. Add 40 g of hydrofluoric acid with a concentration of 40% to the zirconium oxychloride aqueous solution, stir and mix the zirconium oxychloride aqueous solution and the glyphosate aqueous solution in a flask, keep stirring, heat the reaction in a water bath at 80° C. for 6 hours, centrifuge the product, and use Wash with deionized water until the supernatant is neutral, dry at 90°C, and grind the sample into powder to obtain 28.7 g of zirconium glyphosate phosphonate, which is denoted as ZrGP1, and its X-ray diffraction (XRD) spectrum is shown in figure 1 , the scanning electron microscope (SEM) photo see figure 2 .

[0055] Preparation of Silver Ammo...

Embodiment 1

[0062] 7 parts of intumescent flame retardant, 7 parts of silver ammonium phosphomolybdate intercalated zirconium phosphate, 4 parts of ceramic fiber powder, 2 parts of silicone masterbatch MB50-001 (Dow Corning), 0.8 parts of antioxidant 1010, 36 parts of white oil #0.5 parts and 78.5 parts of polypropylene 6012 (Sinopec) were weighed and mixed uniformly in proportion, then added to a twin-screw extruder with a length-to-diameter ratio of 38:1, melted, extruded and granulated to obtain the product. The product performance is shown in Table 2.

Embodiment 2

[0064] 9 parts of intumescent flame retardant, 3 parts of silver ammonium phosphomolybdate intercalated zirconium phosphate, 2 parts of ceramic fiber powder, 3 parts of silicone masterbatch MB50-001 (Dow Corning), 0.5 parts of antioxidant 1010, 36 parts of white oil #0.5 parts and 82 parts of polypropylene 6012 (Sinopec) were weighed and mixed uniformly in proportion, then added to a twin-screw extruder with a length-to-diameter ratio of 38:1, melted, extruded and granulated to obtain the product. Product properties are shown in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a halogen-free flame-retardant scratch-resistant antibacterial polypropylene material as well as a preparation method and application thereof. The halogen-free flame-retardantscratch-resistant antibacterial polypropylene material is prepared from the following raw materials in parts by weight: 76-89 parts of polypropylene; 4-10 parts of an intumescent flame retardant; 2-12parts of silver ammonium phosphomolybdate intercalation modified zirconium phosphonate; 1-5 parts of ceramic fiber powder; 0.5-4 parts of silicone master batch; 0.3-1 part of an antioxidant; and 0.2-1 part of white oil. The silver ammonium phosphomolybdate intercalation modified zirconium phosphonate, the ceramic fiber powder and the silicone master batch are added at the same time, so that the compatibility with polypropylene can be greatly improved, the flame retardant property of the material is improved, the addition amount of a flame retardant is greatly reduced, the scratch resistance of the material can be improved, the material has excellent antibacterial property, and the material has excellent comprehensive performance when applied to the field of intelligent toilet lids.

Description

technical field [0001] The invention relates to a modified polypropylene material and a preparation method thereof, in particular to a halogen-free flame-retardant, scratch-resistant, antibacterial polypropylene material and a preparation method thereof. Background technique [0002] Polypropylene material is one of the four general-purpose plastics. It can be modified by toughening, strengthening, filling, blending and other modification methods to obtain modified materials with excellent comprehensive properties. It has been widely used in the fields of automobiles, home appliances, and building materials. Among them, the filling modification of polypropylene, on the one hand, can reduce the cost, and on the other hand, it can improve the performance of polypropylene composite materials. [0003] Halogen-based flame retardants are usually added to traditional flame-retardant polypropylene materials, but the gases produced during the combustion process are harmful to the hu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L83/04C08L91/06C08K13/04C08K3/32C08K5/5317C08K7/04
CPCC08L23/12C08L2205/03C08L2201/02C08K2201/003C08K2201/004C08L83/04C08L91/06C08K13/04C08K3/32C08K5/5317C08K7/04
Inventor 李静易光铨张红涂永鑫徐卓言苗春萌古亮亮
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com