A kind of high wear-resisting and high shock-absorbing sports shoe sole material and preparation method thereof

A technology for sole materials and sports shoes, applied in the field of sports shoes, can solve the problems of not meeting the requirements of lightness, general tear strength, general rebound rate, etc., and achieve good compression resistance and recovery, good comprehensive physical properties, and excellent flexibility. sexual effect

Active Publication Date: 2022-07-15
福建省中伟体育用品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Chinese invention patent CN201210408660.4 discloses a rubber material for the sole of sports shoes with wide temperature range and high shock absorption and its preparation method. agent, petroleum resin, which maintain good shock absorption performance in a wide temperature range, and have good wear resistance, but its tear strength is average, the density is high, and the sole is heavy, which does not meet the modern people's light and light shoes. need
Chinese invention patent CN201010248174.1 discloses a high-shock-absorbing, wear-resistant sports shoe sole material and its manufacturing method. On the basis of rubber, softening oil and reinforcing It is made by the screening of active agents and reasonable control of the process. It has excellent shock absorption, wear resistance and wet skid resistance, but its density is relatively high, the rebound rate is average, and the comfort is average.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high wear-resisting and high shock-absorbing sports shoe sole material and preparation method thereof
  • A kind of high wear-resisting and high shock-absorbing sports shoe sole material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A high-wear-resisting and high-shock-absorbing sole material for sports shoes, the sole material is composed of the following raw materials by weight: 40 parts of ethylene-vinyl acetate copolymer, 2 parts of modified nano-zinc oxide, 20 parts of PBSs, 40 parts of PBS Polyester thermoplastic polyurethane elastomer, 8 parts of waste rubber powder, 8 parts of modified diatomaceous earth, 3 parts of ligand type titanate coupling agent, 3 parts of foaming agent, 1 part of crosslinking agent, 3 parts of vulcanizing agent and 0.8 parts antioxidant. According to the preparation method of the sole material composed of the above-mentioned materials, it specifically comprises the following steps:

[0033] (1) EVA / PBSs copolymer: add EVA to the double-roll mill, heat up to 100°C, add PBSs after the EVA is completely melted, mix for 30min, then raise the temperature to 160°C, add modified nano-oxidation Zinc and cross-linking agent were mixed for 1 hour, and the tablet was removed ...

Embodiment 2

[0041] A high-wear-resistance and high-shock-absorbing sole material for sports shoes, the sole material is composed of the following raw materials by weight: 60 parts of ethylene-vinyl acetate copolymer, 5 parts of modified nano-zinc oxide, 10 parts of PBSs, 25 parts of PBS Polyester thermoplastic polyurethane elastomer, 10 parts of waste rubber powder, 12 parts of modified diatomaceous earth, 1 part of ligand type titanate coupling agent, 5 parts of azodicarboxylate, 2 parts of diisopropyl peroxide Benzene, 1 part benzoyl peroxide and 0.3 part antioxidant AW. The preparation method of the sole material composed of this material is the same as that in Example 1, and the specific reference is made to Example 1.

[0042] The VA content in the above-mentioned EVA ethylene-vinyl acetate copolymer is 22-36%, and the polyester thermoplastic polyurethane elastomer is Elastollan C64D from BASF, Germany.

[0043] The preparation method of the above-mentioned modified nano-zinc oxide ...

Embodiment 3

[0047] A high-wear-resistance and high-shock-absorbing sole material for sports shoes, the sole material is composed of the following raw materials by weight: 50 parts of ethylene-vinyl acetate copolymer, 3 parts of modified nano-zinc oxide, 15 parts of PBSs, 34 parts of PBS Polyester thermoplastic polyurethane elastomer, 8 parts of waste rubber powder, 10 parts of modified diatomaceous earth, 2 parts of ligand type titanate coupling agent, 4 parts of azodicarboxylate, 1.5 parts of diisopropyl peroxide Benzene, 2 parts benzoyl peroxide and 0.5 part antioxidant AW. The preparation method of the sole material composed of this material is the same as that in Example 1, and the specific reference is made to Example 1.

[0048] The VA content in the above-mentioned EVA ethylene-vinyl acetate copolymer is 22-36%, and the polyester thermoplastic polyurethane elastomer is Elastollan C64D from BASF, Germany.

[0049] The preparation method of the above-mentioned modified nano-zinc oxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sports shoe sole material with high wear resistance and high shock absorption and a preparation method thereof, and relates to the technical field of sports shoes. The high-wear-resisting and high-shock-absorbing sports shoe sole material disclosed in the present invention, under the action of a cross-linking agent and modified nano-zinc oxide, utilizes PBSs to modify EVA to cross-link and blend to form an EVA / PBSs copolymer, which is then mixed with polymer It is prepared by blending raw materials such as ester thermoplastic polyurethane elastomer, waste rubber powder and modified diatomite, and molding and foaming. The sports shoe sole material with high wear resistance and high shock absorption provided by the invention has the advantages of simple preparation process and easy operation, low density, high elasticity, excellent wear resistance, shock absorption, weather resistance and corrosion resistance, and improves the The comfort of sports shoes, prolong the service life of sports shoes.

Description

technical field [0001] The invention belongs to the technical field of sports shoes, in particular to a sole material for sports shoes with high wear resistance and high shock absorption and a preparation method thereof. Background technique [0002] With the rapid development of modern society, people's concept of wearing shoes has undergone great changes. From the protection and heat preservation of the last century to the pursuit of lightness, comfort, beauty, shock absorption, wear resistance and other functions. As the world's largest producer and consumer of sports shoes, China's research and development of sports shoes is also changing with each passing day. Existing sports soles are divided into three categories: vulcanized rubber soles, air-cushion filled soles and foam soles. With the continuous development of science and technology, foam soles have the advantages of both excellent performance and low cost, occupying a relatively high place in sports soles. large ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L75/06C08L83/14C08L19/00C08K9/06C08K9/04C08K3/22C08K7/26C08K5/10C08J9/10A43B13/04A43B13/18
CPCC08J9/102C08J9/0061C08J9/009C08J9/0066C08J9/0023A43B13/04A43B13/187C08J2323/08C08J2375/06C08J2483/14C08J2423/08C08J2475/06C08J2419/00
Inventor 王建治
Owner 福建省中伟体育用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com