Antistatic and antibacterial textile fabric and preparation method thereof

A textile fabric, antistatic technology, applied in conductive/antistatic filament manufacturing, textile and papermaking, biochemical fiber treatment, etc. Sol, low production efficiency of textile fabrics, etc., to achieve the effect of increasing antistatic effect, improving antibacterial effect, and efficient drying

Inactive Publication Date: 2021-04-13
陈快安
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The antistatic and antibacterial effects of the existing textile fabrics are not ideal. At the same time, in the preparation process of the existing textile fabrics, it is necessary to coat the textile fabrics with sol, or dip the textile fabrics in the sol. The coating of the sol cannot Ensure that the interior of the textile fabric can fully absorb the sol, while the exhaust dyeing of the textile fabric usually takes longer, resulting in low production efficiency of the textile fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic and antibacterial textile fabric and preparation method thereof
  • Antistatic and antibacterial textile fabric and preparation method thereof
  • Antistatic and antibacterial textile fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An antistatic and antibacterial textile fabric includes an inner layer fabric and an outer layer fabric, and the inner layer fabric is an antistatic fabric;

[0030] Wherein, this antistatic and antibacterial textile fabric is prepared by the following steps:

[0031] Step 1: Adhere the inner layer fabric and the outer layer fabric with an adhesive to obtain a basic fabric;

[0032] Step 2: Add the composite hydrosol into the dyeing tank 6 of the dyeing equipment, the pump 30 extracts the composite hydrosol through the rubber suction pipe 31, and transports the composite hydrosol to the upper sol through the first communication pipe 28 and the second communication pipe 29 respectively. In the tank 16 and the lower sol tank 18, put the basic fabric on the first belt conveyor 2, open the first cylinder 5, the piston rod of the first cylinder 5 pushes the lifting shell 4 downward, and the lifting shell 4 drives the second belt conveyor 3 descends, the belts on the first b...

Embodiment 2

[0036] The composite hydrosol in step 2 is prepared by the following steps: S1, by weight, weigh 15 parts of isopropanol, 6 parts of nano-zinc oxide, 11 parts of polyethylene glycol, and 150 parts of water, and weigh the isopropanol by weight. , nano-zinc oxide and polyethylene glycol are dissolved in water, and then mixed with glacial acetic acid in a volume ratio of 1:2.5 to obtain a composite acetic acid solution; S2, 10 parts by weight of cellulose are dissolved in the composite acetic acid solution to obtain cellulose acetate solution solution, and then 5 parts by weight of AgNO 3 Dissolving into the cellulose acetate solution to obtain a cellulose-silver composite antibacterial solution; S3, adding 90 parts by weight of ethyl orthosilicate to the cellulose-silver composite antibacterial solution under high-speed stirring, stirring with a magnetic stirrer for 3 hours at room temperature, A composite hydrosol is obtained. The antistatic fabric is prepared by the following...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses antistatic and antibacterial textile fabric and a preparation method thereof. The antistatic and antibacterial textile fabric has good antistatic and antibacterial effects through spinning of double-layer fabric, inner-layer fabric is antistatic fabric, and zinc oxide whiskers are added into the antistatic fabric, so that the antistatic effect of the prepared antistatic and antibacterial textile fabric is effectively improved; meanwhile, through dip dyeing and coating of composite hydrosol, the antibacterial effect of the antistatic and antibacterial textile fabric is effectively improved; and according to FZ/T01042-1996 measurement, the induction voltage of the antistatic and antibacterial textile fabric is 2388-2597 V. Meanwhile, the invention further discloses dip dyeing equipment. The dip dyeing equipment flattens the surface of basic fabric before the basic fabric is subjected to dip dyeing, wrinkles are prevented, and the composite hydrosol can be fully attached to the basic fabric through double processing of dip dyeing and coating.

Description

technical field [0001] The invention relates to the technical field of fabric preparation, in particular to an antistatic and antibacterial textile fabric and a preparation method thereof. Background technique [0002] The antistatic and antibacterial effects of the existing textile fabrics are not ideal. At the same time, in the preparation process of the existing textile fabrics, it is necessary to coat the sol on the textile fabric, or to dip the textile fabric in the sol, and the coating of the sol cannot. To ensure that the interior of the textile fabric can fully absorb the sol, and the dip dyeing of the textile fabric usually takes longer, resulting in low production efficiency of the textile fabric. SUMMARY OF THE INVENTION [0003] The object of the present invention is to provide an antistatic and antibacterial textile fabric and a preparation method thereof, and solve the following technical problems: (1) through the weaving of the double-layer fabric, the fabri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M17/00D06M11/44D06M11/65D06M11/79D06M15/07D06M15/53D01F8/16D01F8/14D01F8/08D01F8/06D01F1/09D06M101/04D06M101/06D06M101/20D06M101/28D06M101/30D06M101/32
CPCD01F1/09D01F8/06D01F8/08D01F8/14D01F8/16D06M11/44D06M11/65D06M11/79D06M15/07D06M15/53D06M16/00D06M17/00D06M2101/04D06M2101/06D06M2101/20D06M2101/28D06M2101/30D06M2101/32
Inventor 陈快安
Owner 陈快安
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap