A kind of antistatic fabric and preparation method thereof

An antistatic and fabric technology, which is applied in the manufacture of conductive/antistatic filaments, rayon, and knitting. It can solve problems affecting product quality and fabric wearability, electrostatic interference, and affecting processing, so as to improve out-of-phase Effects of nucleation ability, increased compatibility, and accelerated crystallization rate

Active Publication Date: 2022-03-01
吴江嘉伦织造有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, electrostatic interference affects the smooth progress of processing, affects the quality of products and the wearability of fabrics, etc.
When the electrostatic phenomenon is serious, the static voltage is as high as several thousand volts, and sparks will be generated due to discharge, causing a fire and causing serious consequences.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antistatic fabric and preparation method thereof
  • A kind of antistatic fabric and preparation method thereof
  • A kind of antistatic fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A preparation method of antistatic fabric, comprising the following steps:

[0042] The preparation method of composite nanoparticles of silica airgel and titanium dioxide is as follows: adding silica airgel nanoparticles to deionized water and ultrasonicating for 5 minutes, removing the deionized water, and quick freezing to obtain silica airgel containing ice cubes Nanoparticles, then slowly drop titanium tetrachloride into the silica airgel nanoparticles containing ice cubes, dry them at 60 degrees for 20 minutes, then put them into a muffle furnace and heat them to 400 degrees, and put them into the muffle furnace The middle heating curve is to raise the temperature to 200 degrees at a heating rate of 5 degrees per minute, and then increase the temperature from 200 degrees to 400 degrees at a heating rate of 2 degrees per minute to prepare composite nanoparticles of silica airgel and titanium dioxide.

[0043] The preparation method of polyether surfactant is as fol...

Embodiment 2

[0048] A preparation method of antistatic fabric, comprising the following steps:

[0049] The preparation method of composite nanoparticles of silica airgel and titanium dioxide is as follows: adding silica airgel nanoparticles to deionized water and ultrasonicating for 10 minutes, removing the deionized water, and quick freezing to prepare silica airgel containing ice cubes Nanoparticles, and then slowly drop titanium tetrachloride into the silica airgel nanoparticles containing ice cubes, dry them at 70 degrees for 30 minutes, then put them into a muffle furnace and heat them to 400 degrees, and put them into the muffle furnace The middle heating curve is to raise the temperature to 200 degrees at a heating rate of 5 degrees per minute, and then increase the temperature from 200 degrees to 400 degrees at a heating rate of 2 degrees per minute to prepare composite nanoparticles of silica airgel and titanium dioxide.

[0050] The preparation method of polyether surfactant is ...

Embodiment 3

[0055] A preparation method of antistatic fabric, comprising the following steps:

[0056] The preparation method of composite nanoparticles of silica airgel and titanium dioxide is as follows: adding silica airgel nanoparticles to deionized water and ultrasonicating for 8 minutes, removing the deionized water, and quick freezing to obtain silica airgel containing ice cubes Nanoparticles, and then slowly drop titanium tetrachloride into the silica airgel nanoparticles containing ice cubes, dry them at 65 degrees for 28 minutes, then put them into a muffle furnace and heat them to 400 degrees, and put them into the muffle furnace The middle heating curve is to raise the temperature to 200 degrees at a heating rate of 5 degrees per minute, and then increase the temperature from 200 degrees to 400 degrees at a heating rate of 2 degrees per minute to prepare composite nanoparticles of silica airgel and titanium dioxide.

[0057] The preparation method of polyether surfactant is as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The object of the present invention is to provide an antistatic fabric and a preparation method thereof. Among them, the antistatic fabric is warp-knitted by antistatic yarn and nylon yarn, wherein the density of antistatic yarn is 80-100 / cm, and the density of nylon yarn is 50-90 / cm; It is made of antistatic polyester fiber, and the antistatic polyester fiber is made of polyester chip and antistatic polyester masterbatch by melt blending and spinning. The antistatic PET polyester fiber of the present invention is added with conductive filler carbon nanotubes, and the carbon nanotubes have the advantages of large specific surface area and small size, and have special macroscopic quantum tunneling effects, quantum size effects and surface effects, and the obtained PET Polyester fiber has excellent antistatic properties and good comprehensive properties. At the same time, the antistatic PET polyester fiber is made into yarn and woven with nylon to form a composite antistatic fabric. Combining the advantages of the two, the performance of the PET polyester material is further improved.

Description

technical field [0001] The invention belongs to the technical field of composite textile fabrics, and in particular relates to an antistatic fabric and a preparation method thereof. Background technique [0002] Textile materials are electrical insulator materials, and their specific resistance is generally high, especially synthetic fibers such as polyester, acrylic, and polyvinyl chloride with low hygroscopicity. Therefore, in the process of textile processing, due to the close contact and friction between fibers and fibers or between fibers and machine parts. Causes the transfer of charge on the surface of the object, resulting in static electricity. Fibers with the same charge repel each other, and fibers with different charges attract each other, resulting in hairy sliver, increased yarn hairiness, poor package formation, fiber sticking to machine parts, and increased yarn breakage. And form scattered stripes on the cloth surface, etc. After the clothing is electrifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B21/00D01F6/92D01F1/09D01F1/10
CPCD04B21/00D01F6/92D01F1/09D01F1/10D10B2331/04D10B2331/02
Inventor 韦贤福
Owner 吴江嘉伦织造有限公司