Water-based alkyd acrylic hybrid resin and preparation method thereof
An alkyd acrylic and hybrid resin technology, applied in the direction of coating, can solve the problems of low performance such as water resistance, and achieve the effect of improving hardness and improving heat storage capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example 1
[0040] The present invention provides a method for preparing an aqueous alkyme-acrylic acid hybrid resin, comprising the steps of:
[0041] (1) Preparation of the base alkyd resin, the composition of the feedstock, such as Table 1.
[0042] The preparation method is: the raw material is added to the clean reaction kettle, and the temperature is warmed to 180 ° C, constant temperature 1 h, and the condensed water is collected from the xylene. Continue to warm to 225 ° C, constant temperature to the raw material to continue to heat up to 245 ° C, to less than 10 mgkOH / g, cool down, dilute, and obtain the base alkyd resin.
[0043] Table 1 Composition and ratio of the feedstock of the base alkyd resin
[0044]
[0045] (2) Preparation of fatty acid modified acrylic acid prepolymer, the composition of the feedstock, such as shown in Table 2.
[0046] The preparation method is: the total mass of each raw material is 18% by weight of xylene as a cubicle, and the r...
Example Embodiment
[0054] Example 2
[0055] The present invention provides a method for preparing an aqueous alkyme-acrylic acid hybrid resin, comprising the steps of:
[0056] (1) Preparation of the base alkyd resin, the preparation method is the same as in Example 1.
[0057] (2) Preparation of fatty acid modified acrylic prepolymers, the composition of its feedstock, such as Table 4.
[0058] The preparation method is: the total mass of each raw material is 18% by weight of xylene as a cubicle, and the raw material is mixed and uniform, and the droplets are added to the reaction kettle at 140 ° C, and the drop-off time is 6 h. After the dropwise addition, thermostated reaction was 2 h at 140 ° C, and the fatty acid modified acrylic prepolymer was obtained.
[0059] Table 4 Composition and ratio of raw materials for fatty acid modified acrylic prepolymers
[0060]
[0061]
[0062] (3) Preparation of an aqueous alkyd acrylic acid hybrid resin, the composition of the raw material, such as Tabl...
Example Embodiment
[0066] Example 3
[0067] The present invention provides a method for preparing an aqueous alkyme-acrylic acid hybrid resin, comprising the steps of:
[0068] (1) Preparation of the base alkyd resin, the composition of the feedstock, such as Table 6.
[0069] The preparation method is: the raw material is added to the clean reaction kettle, and the temperature is warmed to 180 ° C, constant temperature 1 h, and the condensed water is collected from the xylene. Continue to warm to 225 ° C, constant temperature to the raw material to continue to heat up to 245 ° C, and the alkyd resin is lowered to less than 10 mgKOH / g, cool down, dilute, to obtain a base alkyd resin polymer.
[0070] Table 6 Foundation composition and ratio of baseline glycolic resin
[0071]
[0072]
[0073] (2) Preparation of fatty acid modified acrylic prepolymers, the composition of the feedstock, such as shown in Table 7.
[0074] The preparation method is: the total mass of each raw material is 18% by ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap