Modified PP synthetic paper as well as preparation method and application thereof
A synthetic paper and modification technology, applied in chemical instruments and methods, synthetic resin layered products, paper/cardboard layered products, etc., can solve the problems of reduced bonding effect, polarity difference, etc., to improve the bonding force , The effect of improving the mounting performance and improving the affinity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] According to the weight of the mass number, 10 parts of POE 20 parts, 1 maleic anhydride, 20 nanocium carbonate and 0.85% hydrogen-containing amount of 0.85%, mixed, mixed, mixed, mixed and uniform The extruder extruded granulation to obtain modified PP masterbatch, and then prepared a PP masterpiece into the extrusion method to obtain a PP synthetic paper. The prepared PP synthetic paper was taken between corona tempered to a corona value of 40 dacc, and the surface of the PP synthesis paper surface was frictionally treated with a 300 mesh. Finally, the obtained PP synthetic paper surface was sprayed with 10 wt% ethylene glycol and the toluene solution of three (pentafluorophenyl) borane, and after holding at 30 ° C for a certain 30 min, the excess organic solvent was cleaned and dried to obtain one. A modified PP synthetic paper having a hydroxyl group in the side surface.
Embodiment 2
[0035] According to the weight of the weight parts, PP 100 parts, POE 30 parts, and 10 parts of methacrylate, 50 parts of nanocium carbonate and a hydrogen-containing amount of 1.58%, and mix each raw material, After mixing is uniform, the granulation is extruded by the extruder to obtain a modified PP masterbatch, and then the PP master can be prepared by a cast film to obtain a PP synthetic paper. The prepared PP synthetic paper was injected between corona to 50 dacco, and was frictionally friction with 400 mesh roller, so that the surface of the PP synthesis paper has a pattern. Finally, a toluene solution containing 15 wt% propylene glycol and a catalytic amount of three (pentafluorobenzene) borane was sprayed on the surface of the obtained PP synthesis paper, and after holding at 50 ° C for a certain 30 min, the surface excess organic solvent was cleaned, and the surface surface surface was dried. Chemical modified PP synthetic paper grafted.
Embodiment 3
[0037]According to the weight of the weight parts, PP 100 parts, POE 25 parts, PP-G-MAH 5 parts, and 40 parts of nanocium carbonate and a hydrogen-containing amount of 1.32%, and mixed, mixed, mixed After uniform, the granulation is extruded by the extruder to obtain a modified PP master, and then the PP master particles are prepared by the casting method to obtain a PP synthetic paper. The prepared PP synthetic paper was treated by corona until the corona value of 45 dacc, and the surface of the PP synthesis paper surface was frictionally treated with a 350 mesh. Finally, the obtained PP synthetic paper surface is sprayed with 12 wt% butetaniol and a toluene solution of three (pentafluorobenzene) borane, at 40 ° C for 20 minutes, washing excess organic solvents, drying A modified PP synthetic paper having a hydroxyl group in the side surface.