Flame-retardant UV-LED coating gloss oil and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A UV-LED, lighting technology, applied in coatings, fire-retardant coatings, polyester coatings, etc., can solve the problems of poor flame-retardant effect and inability to flame-retardant of UV-LED coating varnish
Active Publication Date: 2021-07-06
中山市中益油墨涂料有限公司
View PDF8 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In order to solve the technical problem of poor flame retardant effect of the existing UV-LED coating varnish, the present invention provides a flame retardant UV-LED coating varnish, which has a good flame retardant effect and has excellent flexibility and Adhesion, as well as good printing adaptability and other properties, will solve the technical problem of non-flame retardancy encountered by the same type of coating varnish in China at present
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] A preparation method for flame retardant UV-LED coated varnish, comprising the following steps:
[0026] S1: Prepare the materials according to the parts by weight in Table 1, put the polyester acrylic resin, epoxy acrylic resin, reactive diluent and photoinitiator into the container, and stir at 48°C at a stirring rate of 900 rpm for 20 minutes;
[0027] S2: Slowly add tannic acid-modified nano-graphene, fillers and additives, and stir for 5 minutes at a stirring rate of 900 rpm under normal temperature and pressure;
[0028] S3: Filtered with 300-mesh mesh, it can be packed after passing the test.
Embodiment 2
[0030] A preparation method for flame retardant UV-LED coated varnish, comprising the following steps:
[0031] S1: Prepare the materials according to the parts by weight in Table 1, put the polyester acrylic resin, epoxy acrylic resin, reactive diluent and photoinitiator into the container, and stir for 10 minutes at a stirring rate of 900 rpm at 50°C;
[0032] S2: Slowly add tannic acid-modified nano-graphene, fillers and additives, and stir for 8 minutes at a stirring rate of 900 rpm under normal temperature and pressure;
[0033] S3: Filtered with 300-mesh mesh, it can be packed after passing the test.
Embodiment 3
[0035] A preparation method for flame retardant UV-LED coated varnish, comprising the following steps:
[0036] S1: Prepare the materials according to the parts by weight in Table 1, put the polyester acrylic resin, epoxy acrylic resin, reactive diluent and photoinitiator into the container, and stir at 45°C at a stirring rate of 1000 rpm for 20 minutes;
[0037] S2: Slowly add tannic acid-modified nano-graphene, fillers and additives, and stir for 5 minutes at a stirring rate of 1000 rpm under normal temperature and pressure;
[0038] S3: Filtered with 300-mesh mesh, it can be packed after passing the test.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides flame-retardant UV-LED coating gloss oil and a preparation method thereof. The flame-retardant UV-LED coating gloss oil comprises 20-25 parts of polyesteracrylic resin, 10-15 parts of epoxyacrylic resin, 40-45 parts of a reactive diluent, 5-10 parts of a photoinitiator, 5-10 parts of tannic acid modified nano graphene, 3-4 parts of a filler and 1-2 parts of an auxiliary agent. Polyesteracrylic resin and epoxy acrylic resin are blended to serve as a gloss oil prepolymer, tannic acid modified nano graphene is added as a modifier, the modifier is mixed with a monomer and the prepolymer in gloss oil, then polymerization is conducted to obtain a nano composite material, a synergistic flame-retardant composite filler is provided, the flame retardant property of the composite filler can be greatly improved, the prepared UV-LED coating gloss oil has good flame retardant effect, excellent flexibility and adhesive force, good printing adaptability and the like, and the technical problem that the same type of coating gloss oil in China at present cannot resist flame is solved.
Description
technical field [0001] The invention belongs to the technical field of UV-LED inks, and in particular relates to a flame-retardant UV-LED coating varnish and a preparation method thereof. Background technique [0002] In order to improve the quality of the current building materials and furniture products, it is often necessary to apply or print a layer of protective coating or varnish after preparation, which can not only prevent water and dust, but also improve the grade of the product. [0003] However, the current UV-LED coating varnish components contain a large amount of organic compounds, which will accelerate the combustion of the flame and release a large amount of harmful gases when a fire occurs. These existing problems are completely inconsistent with the environmental protection and safety required by the furniture and building materials industry, which greatly limits its application in furniture and building materials products. Therefore urgently need further ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 