A composite film, high-speed technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, lamination, etc., can solve the problems of poor structural characteristics, high-frequency transmission loss, large hygroscopicity, etc., to improve the strength and modulus , excellent insulation performance, and the effect of improving the bonding strength

Active Publication Date: 2021-07-13
宁波聚嘉新材料科技有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the mainstream antenna base material is mainly polyimide (Polyimide, PI), but due to the large dielectric constant and loss factor of the PI base material, high moisture absorption, and poor reliability, the high-frequency transmission loss is serious, The structural characteristics are poor, and it is difficult to meet the needs of 5G high-fre

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • LCP composite film suitable for high frequency and high speed and preparation method thereof
  • LCP composite film suitable for high frequency and high speed and preparation method thereof
  • LCP composite film suitable for high frequency and high speed and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] DETAILED DESCRIPTION One: Combination figure 1 The present embodiment is an LCP composite film suitable for high frequency high speed, characterized in that the LCP composite film suitable for high frequency high speed includes the top to bottom, including TLCP layers (1), TLCP-plastic composite layer (2) and Grassroots (3);

[0019] The TLCP layer (1) contains TLCP and polytetrafluoroethylene, and the mass fraction of polytetrafluoroethylene is 15 to 30%, and the margin is TLCP;

[0020] The TLCP-plastic composite layer (2) contains TLCP fibers, PET and polytetrafluoroethylene, and the mass fraction of TLCP fibers is 10 to 20%, and the mass fraction of PET is 20 to 30%, and the margin is polytetrafluoro. Ethylene.

[0021] The tensile strength of the TLCP fibers exceeds 18CN / DTEX, which can greatly improve the tensile strength of the plastic article as the skeleton as the skeleton.

[0022] In this embodiment, PET is a polyethylene terephthalate which has good electrical...

Example Embodiment

[0023] DETAILED DESCRIPTION 2: Combination figure 1 The difference between the present embodiment and the specific embodiment is: the TLCP fiber is one or two layers in the TLCP-plastic composite layer (2); when the TLCP fiber is one layer, the TLCP-plastic composite layer (2) The mass fraction of TLCP fibers is 10 to 15%, and the TLCP fiber is provided in longitudinal direction; when the TLCP fiber is two layers, the mass fraction of TLCP fibers in the TLCP-plastic composite layer (2) is 15 to 20%, and the same The TLCP fibers are set together, and the adjacent two-layer TLCP fibers are intersected. Others are the same as those of the specific embodiments.

Example Embodiment

[0024] Detailed Embodiment 3: Combination figure 1 This embodiment differs from the specific embodiment of the other or two: the TLCP is a copolyester to hydroxybenzoic acid and 2-hydroxy-6-naphthoic acid. Others are the same as those of the specific embodiments.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an LCP composite film suitable for high frequency and high speed and a preparation method thereof. The composite film sequentially comprises a TLCP layer, a TLCP-plastic composite layer and a base layer from top to bottom. The method comprises the following steps: 1, preparing a TLCP single-layer film; 2, preparing a TLCP-plastic composite layer; and 3, preparing a base layer to obtain the LCP composite film suitable for high frequency and high speed. The composite film has low dielectric constant and dielectric loss, greatly reduces high-frequency and high-speed signal transmission loss, and has wide 5G application market space.

Description

technical field [0001] The invention relates to an LCP composite film suitable for high frequency and high speed and a preparation method thereof. Background technique [0002] With the advent of the 5G era, optoelectronics, aerospace, national defense and mobile communications have put forward higher requirements for high-frequency and high-speed transmission, as well as materials for hardware carriers such as application-side mobile phones, base stations, Internet of Things, and automobiles, as well as new chemical materials. stricter requirements. Antennas are an indispensable part of wireless communication. Under the trend of 5G high frequency, high speed and miniaturization, antenna technology has more stringent requirements on materials. On the one hand, it needs to meet the special requirements of millimeter waves for antenna materials. Minimize the space occupied by the antenna. At present, the mainstream antenna base material is mainly polyimide (Polyimide, PI), b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B33/00B32B27/32B32B27/06B32B27/12B32B5/02B32B27/36B32B27/20B32B37/06B32B37/10C08L27/18C08L67/04C08L67/02C08K7/28
CPCB32B33/00B32B27/322B32B27/06B32B27/12B32B5/02B32B27/36B32B27/20B32B37/06B32B37/10C08L27/18C08L67/04B32B2307/206C08L2205/03C08L2205/16C08L2205/02C08L67/02C08K7/28
Inventor 王阳任忠平孙志忠
Owner 宁波聚嘉新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap