Antibacterial and crease-resistant knitted fabric and preparation method thereof

A knitted fabric and anti-wrinkle technology, which is applied in the field of textile fabrics, can solve the problems that the fabric cannot be restored to flatness, bacteria breed, and the strength of knitted fabrics is reduced, and achieve excellent drape and hand feeling, enhanced antibacterial performance, and comfortable stretchability.

Pending Publication Date: 2021-07-27
石狮雍仓织造有限公司
View PDF24 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the improvement of people's living standards, people's requirements for knitted fabrics are getting higher and higher. When wearing pure cotton knitted fabrics, when the human body sweats a lot, the pure cotton knitted fabrics will absorb a lot of sweat and become wet. It becomes heavier, the speed of moisture conduction and dehumidification slows down, and sweat remains on the clothing and skin, which is prone to peculiar smell and even breeds bacteria, which will affect the health of the body
In addition, knitted fabrics also have deficiencies and defects in anti-wrinkle performance. After wearing for a long time, the fabric cannot return to smoothness.
Generally, for the wrinkle resistance of knitted fabrics, it is often treated by dipping anti-wrinkle and anti-shrinkage resin. After treatment, the anti-wrinkle performance of knitted fabrics is improved, but the treatment with antibacterial and anti-wrinkle resins will easily cause the strength of knitted fabrics to decrease and yellowing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of antibacterial anti-wrinkle knitted fabric and preparation method thereof

[0029] Antibacterial and anti-wrinkle knitted fabric, the anti-bacterial and anti-wrinkle fabric includes fabric base layer, anti-wrinkle layer and antibacterial layer; one side of the fabric base layer is connected with an anti-wrinkle layer through a knitted loop structure; the anti-wrinkle layer and the anti-bacterial layer are passed Knitting loops are connected.

[0030] The above-mentioned fabric base layer is woven by warm and breathable composite yarn; the above-mentioned warm and breathable composite yarn is made of warm and breathable single yarn with a twist of 47 twists / 10cm; the above-mentioned warm and breathable single yarn is made of cotton fiber, modal fiber, moisture-wicking fiber Alternately arranged in the order of 1:2:1, prepared by spinning process. Above-mentioned anti-wrinkle layer adopts elastic anti-wrinkle core-spun yarn; above-mentioned elastic anti-wrinkle ...

Embodiment 2

[0042] A kind of antibacterial anti-wrinkle knitted fabric and preparation method thereof

[0043] The difference with embodiment 1 is:

[0044] The above-mentioned antibacterial functional fiber is selected from the combination of apocynum fiber, chitosan fiber, and the like.

[0045] The preparation of above-mentioned antibacterial polyvinyl alcohol fiber comprises the following steps:

[0046] S1, preheat the silver nitrate solution with a concentration of 0.25mol / L to 35°C, and set aside; mix the carbon nanotubes with the preheated silver nitrate solution at a mass volume ratio of 1:1.6, and ultrasonically shake for 10 hours at a constant temperature , filtered, washed and dried to obtain silver-loaded carbon nanotubes;

[0047] S2, adding polyvinyl alcohol with a degree of polymerization of 1700 into hot water at 100°C to dissolve, then adding the silver-loaded carbon nanotubes prepared in step S1, mixing and stirring evenly, and preparing antibacterial polyvinyl alcoho...

Embodiment 3

[0055] A kind of antibacterial anti-wrinkle knitted fabric and preparation method thereof

[0056] The difference with embodiment 1 is:

[0057] The above-mentioned antibacterial functional fiber is selected from the combination of bamboo fiber and chitosan fiber.

[0058] The preparation of above-mentioned antibacterial polyvinyl alcohol fiber comprises the following steps:

[0059] S1, preheat the silver nitrate solution with a concentration of 0.26mol / L to 35°C for later use; mix the carbon nanotubes with the preheated silver nitrate solution at a mass volume ratio of 1:1.8, and ultrasonically oscillate at a constant temperature for 11 hours , filtered, washed and dried to obtain silver-loaded carbon nanotubes;

[0060] S2, adding polyvinyl alcohol with a degree of polymerization of 1800 into hot water at 100°C to dissolve, then adding the silver-loaded carbon nanotubes prepared in step S1, mixing and stirring evenly, and preparing antibacterial polyvinyl alcohol by solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial and crease-resistant knitted fabric and a preparation method thereof. The antibacterial and crease-resistant knitted fabric comprises a fabric base layer, a crease-resistant layer and an antibacterial layer; one side of the fabric base layer is connected with the crease-resistant layer through a knitted coil structure; the crease-resistant layer and the antibacterial layer are connected through a knitted coil; the fabric base layer is formed by weaving warm-keeping breathable composite yarns; the crease-resistant layer is made of elastic crease-resistant covering yarns; and the antibacterial layer is prepared by blending antibacterial functional fibers and antibacterial polyvinyl alcohol fibers according to a ratio of (1.8-2.3): (2-2.5) into yarns. The antibacterial and crease-resistant knitted fabric prepared by the invention has remarkable antibacterial and crease-resistant properties, good washing resistance and durability and excellent moisture absorption and air permeability, and can keep skin dry and prevent sweat from staying on the fabric and breeding bacteria when a human body sweats.

Description

technical field [0001] The invention relates to the technical field of textile fabrics, in particular to an antibacterial and anti-wrinkle knitted fabric and a preparation method thereof. Background technique [0002] Knitted fabrics are fabrics made by bending yarns into loops with knitting needles and interlocking them. The difference between knitted fabrics and woven fabrics is the shape of the yarn in the fabric. Knitting is divided into weft knitting and warp knitting. Weft knitting is to feed one or several yarns from the weft direction to the working needle of the knitting machine, so that the yarns are sequentially bent into loops, and are strung together to form weft knitting. things. Warp knitting is composed of one or several groups of parallel yarns arranged on the knitting needles and woven along the longitudinal direction at the same time. The structure and shape of the warp knitted fabric are more stable. Knitted fabric has the characteristics of soft text...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/06B32B5/08B32B9/02B32B9/04B32B9/00B32B27/02B32B27/40B32B27/32B32B27/12B32B27/30B32B23/02B32B23/10B32B33/00B32B37/00B32B38/16D02G3/04D02G3/44D02G3/32D04B1/14D04B1/16D04B1/18D01F6/50D01F1/10
CPCB32B5/06B32B5/08B32B5/26B32B5/026B32B33/00B32B37/00B32B38/162D02G3/04D02G3/449D02G3/44D02G3/328D04B1/14D04B1/18D04B1/16D01F6/50D01F1/103B32B2262/062B32B2262/065B32B2262/0292B32B2262/0253B32B2262/0223B32B2250/20B32B2307/7145B32B2307/304B32B2307/724B32B2307/51D10B2321/06D10B2201/22D10B2201/08D10B2201/01D10B2201/04D10B2201/02D10B2331/10
Inventor 王小民刘银彪
Owner 石狮雍仓织造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap